Based on the analysis of the structure and properties of gardenia, the gardenia was extracted in neutral bath. The mordant dyeing of cotton, including pre-mordant, one-bath and post-mordant were studied, and the dyein...Based on the analysis of the structure and properties of gardenia, the gardenia was extracted in neutral bath. The mordant dyeing of cotton, including pre-mordant, one-bath and post-mordant were studied, and the dyeing properties such as dye K/S value and color fastness were investigated. According to the structure and property of mordants including alum, copper sulfate, iron sulfate and rare earth, the interaction mechanisms among gardenia, mordant and cotton fibers were analyzed and the processing factors affecting the mordant dyeing were discussed. As a result, gardenia showed favorable dyeing performance on cotton. The soaping color fastness and crocking fastness were improved by 0.5-1 grade after fixation process with the selected dye-fixing agent and optimized process conditions. The dyeing process and fixation process were optimized.展开更多
To expand the past and present colour concept and reinvent fabric design methods, happening colour is used as a kind of new colour concept and form to design and analyse the resource of colour. With the aid of sophist...To expand the past and present colour concept and reinvent fabric design methods, happening colour is used as a kind of new colour concept and form to design and analyse the resource of colour. With the aid of sophisticated computer software and advanced digital printing machines, happening colour allows images of considerable complication and intricacy to be designed and produced in modern fabric design by various arrangement of printing colours, which also allows further shifts of colour emphasis of the different visual and psychogenic recept.展开更多
Prediction of the formula for matching a given color standard by blending pro-dyed fibers is of considerable importance to the textile industry. This kind of formulation suffers from a lack of computer-aided tool to a...Prediction of the formula for matching a given color standard by blending pro-dyed fibers is of considerable importance to the textile industry. This kind of formulation suffers from a lack of computer-aided tool to assist the colorist attempting to find a good recipe to reproduce a target color. In this article a tristimulus color matching algorithm based on Stcarns-Noechel model is proposed. This algorithm was run to predict recipes for 36 viscose blends. The maximum color difference is 0.97 CIELAB units. It is demonstrated that the algorithm can be used in color matching of fiber blends.展开更多
In acid medium, rhodamine B（RhB）, rhodamine S（RhS）, rhodamine 6G（RhG） and butyl rhodamine B（b-RhB） have a fluorescence peak at 580, 549, 553 and 580nm, respectively. BrO^-3 oxidizes excess I^- into I^-3 Rhodam...In acid medium, rhodamine B（RhB）, rhodamine S（RhS）, rhodamine 6G（RhG） and butyl rhodamine B（b-RhB） have a fluorescence peak at 580, 549, 553 and 580nm, respectively. BrO^-3 oxidizes excess I^- into I^-3 Rhodamine dyes combine I^-3 to form ion association nanoparticles, resulting in fluorescence quenching at 580, 549, 553 and 580 rim, respectively. The fluorescence quenching intensity is proportional to the concentration of BrO^-3 in the range of 0.020 4 - 0.710 μg/mL for RhB, 0.025 - 0. 512μg/mL for RhS, 0.025 - 0.260 μg/mL for RhG, 0.025 - 1.28μg/mL for b-RhB, respectively. In the four systems, RhB system has good stability and high sensitivity. Thus, a simple, sensitive fluorescence method was proposed for the determination of BrO^-3 in commercial bread additives and flours, with satisfactory results. The results of the fluorescence spectra and scan electron microscopy show that the formation of about 60 ran （RhB - I^-3） n association nanoparticles and the interface between the nanoparticles and solution are main factors that cause the fluorescence quenching.展开更多
A new class of novel polymeric crosslinging agent （NPCA）, which contained silane coupling group and the epoxy groups, was designed and synthesized in our laboratory. NPCA was a non-formaldehyde multifunctional cross...A new class of novel polymeric crosslinging agent （NPCA）, which contained silane coupling group and the epoxy groups, was designed and synthesized in our laboratory. NPCA was a non-formaldehyde multifunctional crosslinking polymer. The cotton fabrics dyed with 8.0% （owf） Vinylsulpone-type dyes were treated with 3.0%- 4.0% NPCA, 0.5 mol/L potassium thiocyanate as a catalyst, then padded through two dips and two nips to reach a wet pickup of 80%- 85%, then dried at 80℃ for 2 minutes and cured in oven at 140- 150℃ for 3 minutes. Crocking fastness and fixation （%） were improved with up to 1.0 -1. 5 units, 35%- 50%, respectively. And there was little difference between the color yield of dyed fabrics before and after the treatment at certain conditions. The possible crosslinking mechanism of NPCA was also investigated. It was concluded that NPCA can improve colorfastness of cotton fabric by means of the three-dimensional network, covalent bonding and other molecular forces.展开更多
The soybean fiber was treated with low temperature plasma and the dyeing performance of the treated soybean fiber was also researched. The results show that the speed of dyeing and the percentages of balance dyeing ha...The soybean fiber was treated with low temperature plasma and the dyeing performance of the treated soybean fiber was also researched. The results show that the speed of dyeing and the percentages of balance dyeing have a sharp increase after being treated. So the dyeing temperature and the dosage of acid can be reduced without damaging the bulk fiber structure.展开更多
Pearlitic ductile irons(PDIs)are used in transportation and nuclear energy industries.In heavy loading situation,the service life of PDI is affected by numerous tribo aspects.In this study,surface of the PDI is alloye...Pearlitic ductile irons(PDIs)are used in transportation and nuclear energy industries.In heavy loading situation,the service life of PDI is affected by numerous tribo aspects.In this study,surface of the PDI is alloyed with WC-12%Co powder using a high power fibre laser.The wear properties of the base material and laser alloying samples were investigated by tribometer with various parameters,i.e.,temperature,load and sliding speed.Based on experimental test,the load has maximum percentage of contribution and followed by sliding speed and working temperature.The optimized tribological parameters by Grey relational analysis(GRA)were established and those values are closely matched with predicted values.Besides,base material and laser alloying surfaces were examined through Vickers hardness machine,scanning electron microscopy(SEM)and roughness tester.The laser altered specimen shows no defects and improves the wear properties than substrates.The identified optimal tribological parameters are load of 30 N,speed of 0.5 m/s and working temperature of 300℃,and load of 30 N,speed of 0.5 m/s and working temperature of 200℃ for base metal and laser alloying samples,respectively.展开更多
文摘Based on the analysis of the structure and properties of gardenia, the gardenia was extracted in neutral bath. The mordant dyeing of cotton, including pre-mordant, one-bath and post-mordant were studied, and the dyeing properties such as dye K/S value and color fastness were investigated. According to the structure and property of mordants including alum, copper sulfate, iron sulfate and rare earth, the interaction mechanisms among gardenia, mordant and cotton fibers were analyzed and the processing factors affecting the mordant dyeing were discussed. As a result, gardenia showed favorable dyeing performance on cotton. The soaping color fastness and crocking fastness were improved by 0.5-1 grade after fixation process with the selected dye-fixing agent and optimized process conditions. The dyeing process and fixation process were optimized.
文摘To expand the past and present colour concept and reinvent fabric design methods, happening colour is used as a kind of new colour concept and form to design and analyse the resource of colour. With the aid of sophisticated computer software and advanced digital printing machines, happening colour allows images of considerable complication and intricacy to be designed and produced in modern fabric design by various arrangement of printing colours, which also allows further shifts of colour emphasis of the different visual and psychogenic recept.
文摘Prediction of the formula for matching a given color standard by blending pro-dyed fibers is of considerable importance to the textile industry. This kind of formulation suffers from a lack of computer-aided tool to assist the colorist attempting to find a good recipe to reproduce a target color. In this article a tristimulus color matching algorithm based on Stcarns-Noechel model is proposed. This algorithm was run to predict recipes for 36 viscose blends. The maximum color difference is 0.97 CIELAB units. It is demonstrated that the algorithm can be used in color matching of fiber blends.
文摘In acid medium, rhodamine B（RhB）, rhodamine S（RhS）, rhodamine 6G（RhG） and butyl rhodamine B（b-RhB） have a fluorescence peak at 580, 549, 553 and 580nm, respectively. BrO^-3 oxidizes excess I^- into I^-3 Rhodamine dyes combine I^-3 to form ion association nanoparticles, resulting in fluorescence quenching at 580, 549, 553 and 580 rim, respectively. The fluorescence quenching intensity is proportional to the concentration of BrO^-3 in the range of 0.020 4 - 0.710 μg/mL for RhB, 0.025 - 0. 512μg/mL for RhS, 0.025 - 0.260 μg/mL for RhG, 0.025 - 1.28μg/mL for b-RhB, respectively. In the four systems, RhB system has good stability and high sensitivity. Thus, a simple, sensitive fluorescence method was proposed for the determination of BrO^-3 in commercial bread additives and flours, with satisfactory results. The results of the fluorescence spectra and scan electron microscopy show that the formation of about 60 ran （RhB - I^-3） n association nanoparticles and the interface between the nanoparticles and solution are main factors that cause the fluorescence quenching.
基金Supported by the Nation Nature Science Foundation of China (No.20325210)
文摘A new class of novel polymeric crosslinging agent （NPCA）, which contained silane coupling group and the epoxy groups, was designed and synthesized in our laboratory. NPCA was a non-formaldehyde multifunctional crosslinking polymer. The cotton fabrics dyed with 8.0% （owf） Vinylsulpone-type dyes were treated with 3.0%- 4.0% NPCA, 0.5 mol/L potassium thiocyanate as a catalyst, then padded through two dips and two nips to reach a wet pickup of 80%- 85%, then dried at 80℃ for 2 minutes and cured in oven at 140- 150℃ for 3 minutes. Crocking fastness and fixation （%） were improved with up to 1.0 -1. 5 units, 35%- 50%, respectively. And there was little difference between the color yield of dyed fabrics before and after the treatment at certain conditions. The possible crosslinking mechanism of NPCA was also investigated. It was concluded that NPCA can improve colorfastness of cotton fabric by means of the three-dimensional network, covalent bonding and other molecular forces.
基金Supported by Shanghai Leading Academic Discipline Project (No.P1404)
文摘The soybean fiber was treated with low temperature plasma and the dyeing performance of the treated soybean fiber was also researched. The results show that the speed of dyeing and the percentages of balance dyeing have a sharp increase after being treated. So the dyeing temperature and the dosage of acid can be reduced without damaging the bulk fiber structure.
文摘Pearlitic ductile irons(PDIs)are used in transportation and nuclear energy industries.In heavy loading situation,the service life of PDI is affected by numerous tribo aspects.In this study,surface of the PDI is alloyed with WC-12%Co powder using a high power fibre laser.The wear properties of the base material and laser alloying samples were investigated by tribometer with various parameters,i.e.,temperature,load and sliding speed.Based on experimental test,the load has maximum percentage of contribution and followed by sliding speed and working temperature.The optimized tribological parameters by Grey relational analysis(GRA)were established and those values are closely matched with predicted values.Besides,base material and laser alloying surfaces were examined through Vickers hardness machine,scanning electron microscopy(SEM)and roughness tester.The laser altered specimen shows no defects and improves the wear properties than substrates.The identified optimal tribological parameters are load of 30 N,speed of 0.5 m/s and working temperature of 300℃,and load of 30 N,speed of 0.5 m/s and working temperature of 200℃ for base metal and laser alloying samples,respectively.