By using the melt spinning techniques, the Fe63Co32Gd5 alloy ribbons with 15-50 m in thickness and 3-7 mm in width were prepared at the wheel speeds of 15, 20, 25 and 35 m/s. The rapid solidification microstructures w...By using the melt spinning techniques, the Fe63Co32Gd5 alloy ribbons with 15-50 m in thickness and 3-7 mm in width were prepared at the wheel speeds of 15, 20, 25 and 35 m/s. The rapid solidification microstructures were characterized by three layers, the middle layer of which reaches 80% thickness and forms the column grain of(Fe,Co) solid with Gd solution. Grain refinement takes place with the increase of the wheel speed. And after 0.5 h heat treatment at 823 K, the ribbon thickness becomes larger and the middle layer of column grain is very orderly perpendicular to the ribbon plane. The coercivity of quenched and annealed Fe63Co32Gd5 ribbons both have the inflection point at the wheel speed of 20 m/s, and the tendency is declining. The heat treatment processing makes the coercivity become lower by improving the order of(Fe,Co)17Gd2 compound. The saturation magnetization of quenched ribbons increases with the enhancement of wheel speed, whereas that of annealed ones decreases firstly and then increases. The minimum coercivity is 5.30×103 A/m and the maximum saturation magnetization is 163.62 A·m2/kg, which is obtained in the conditions of the wheel speed of 35 m/s and 0.5 h heat treatment at the temperature of 823 K.展开更多
The n-type semiconducting titanium oxide thin films are well-known as electron transporting interlayer in photovoltaic cells. The favorable characteristics of interlayers in photovoltaics are high optical transmittan...The n-type semiconducting titanium oxide thin films are well-known as electron transporting interlayer in photovoltaic cells. The favorable characteristics of interlayers in photovoltaics are high optical transmittance （T%）, wide band gap energy （Eg） and high electrical conductivity （σ）. Modifying titanium oxide films with metal nanoparticles would increase electrical conductivity but reduce optical band gap energy. We developed the sol-gel derived titanium suboxide （TiOx） films modified with silver （Ag） or gold （Au） or copper （Cu） nanoparticles （NPs）. This study explores a tradeoff between narrowing optical band gap and enhancing electrical conductivity of nanostructured TiOx films by controlling the Au- or Ag- or Cu-NPs loading concentrations （mol%） in titania. The Au- and Cu-NPs loading concentration of 4 mol% should meet a tradeoff which yields the higher T%, wider Eg and higher compared to those of pure TiOx films. In addition, since the pure Cu is not thermodynamically stable in ambience as compared to Au and Ag, the stability of as-obtained colloidal CuNPs is also examined. A careful examination of the time evolution of surface plasmon resonance （SPR） bands of CuNPs indicates that their stability is only up to 4 h.展开更多
One polythiophene derivative PT3T and two low band gap copolymers,PBTT-T3T and PBTT,with different ratios of 5,6-dini-trobenzothiadiazole as the acceptor unit in the polymer backbone have been synthesized by Pd-cataly...One polythiophene derivative PT3T and two low band gap copolymers,PBTT-T3T and PBTT,with different ratios of 5,6-dini-trobenzothiadiazole as the acceptor unit in the polymer backbone have been synthesized by Pd-catalyzed Stille-coupling polymerizations.Thermal stability,X-ray diffraction analyses,UV-vis absorption spectra,photoluminescence spectra and electrochemical properties of the copolymers were investigated.The band gap estimated from UV-vis-NIR spectra of the copolymers films varied from 1.39 to 1.94 eV.Among these copolymers,the films of PBTT-T3T and PBTT,which contain the 5,6-dinitrobenzothiadiazole unit,cover a broad wavelength range in the visible and near-infrared region from 400 to 1000 nm with the maximal peak absorption around 700 nm,which is exactly matched with the maximum in the photon flux of the sun.展开更多
Indium oxide(In_2O_3) films were prepared on Al_2O_3(0001) substrates at 700 °C by metal-organic chemical vapor deposition(MOCVD).Then the samples were annealed at 800 °C,900 °C and 1 000 °C,respec...Indium oxide(In_2O_3) films were prepared on Al_2O_3(0001) substrates at 700 °C by metal-organic chemical vapor deposition(MOCVD).Then the samples were annealed at 800 °C,900 °C and 1 000 °C,respectively.The X-ray diffraction(XRD) analysis reveals that the samples were polycrystalline films before and after annealing treatment.Triangle or quadrangle grains can be observed,and the corner angle of the grains becomes smooth after annealing.The highest Hall mobility is obtained for the sample annealed at 900 °C with the value about 24.74 cm^2·V^(-1)·s^(-1).The average transmittance for the films in the visible range is over 90%.The optical band gaps of the samples are about 3.73 e V,3.71 e V,3.70 eV and 3.69 eV corresponding to the In_2O_3 films deposited at 700 °C and annealed at 800 °C,900 °C and 1 000 °C,respectively.展开更多
基金Projects(51271149,50901060)supported by the National Natural Science Foundation of ChinaProject(NPU-310201401007JCY01007)supported by the Nothwestern Polytechnical University(NPU)Foundations for Fundamental Research,ChinaProject(2012-0009451)supported by the National Research Foundation of Korea
文摘By using the melt spinning techniques, the Fe63Co32Gd5 alloy ribbons with 15-50 m in thickness and 3-7 mm in width were prepared at the wheel speeds of 15, 20, 25 and 35 m/s. The rapid solidification microstructures were characterized by three layers, the middle layer of which reaches 80% thickness and forms the column grain of(Fe,Co) solid with Gd solution. Grain refinement takes place with the increase of the wheel speed. And after 0.5 h heat treatment at 823 K, the ribbon thickness becomes larger and the middle layer of column grain is very orderly perpendicular to the ribbon plane. The coercivity of quenched and annealed Fe63Co32Gd5 ribbons both have the inflection point at the wheel speed of 20 m/s, and the tendency is declining. The heat treatment processing makes the coercivity become lower by improving the order of(Fe,Co)17Gd2 compound. The saturation magnetization of quenched ribbons increases with the enhancement of wheel speed, whereas that of annealed ones decreases firstly and then increases. The minimum coercivity is 5.30×103 A/m and the maximum saturation magnetization is 163.62 A·m2/kg, which is obtained in the conditions of the wheel speed of 35 m/s and 0.5 h heat treatment at the temperature of 823 K.
文摘The n-type semiconducting titanium oxide thin films are well-known as electron transporting interlayer in photovoltaic cells. The favorable characteristics of interlayers in photovoltaics are high optical transmittance （T%）, wide band gap energy （Eg） and high electrical conductivity （σ）. Modifying titanium oxide films with metal nanoparticles would increase electrical conductivity but reduce optical band gap energy. We developed the sol-gel derived titanium suboxide （TiOx） films modified with silver （Ag） or gold （Au） or copper （Cu） nanoparticles （NPs）. This study explores a tradeoff between narrowing optical band gap and enhancing electrical conductivity of nanostructured TiOx films by controlling the Au- or Ag- or Cu-NPs loading concentrations （mol%） in titania. The Au- and Cu-NPs loading concentration of 4 mol% should meet a tradeoff which yields the higher T%, wider Eg and higher compared to those of pure TiOx films. In addition, since the pure Cu is not thermodynamically stable in ambience as compared to Au and Ag, the stability of as-obtained colloidal CuNPs is also examined. A careful examination of the time evolution of surface plasmon resonance （SPR） bands of CuNPs indicates that their stability is only up to 4 h.
基金support from the National Natural Science Foundation of China (50933003 & 50903044)MOST of China (2009AA032304)
文摘One polythiophene derivative PT3T and two low band gap copolymers,PBTT-T3T and PBTT,with different ratios of 5,6-dini-trobenzothiadiazole as the acceptor unit in the polymer backbone have been synthesized by Pd-catalyzed Stille-coupling polymerizations.Thermal stability,X-ray diffraction analyses,UV-vis absorption spectra,photoluminescence spectra and electrochemical properties of the copolymers were investigated.The band gap estimated from UV-vis-NIR spectra of the copolymers films varied from 1.39 to 1.94 eV.Among these copolymers,the films of PBTT-T3T and PBTT,which contain the 5,6-dinitrobenzothiadiazole unit,cover a broad wavelength range in the visible and near-infrared region from 400 to 1000 nm with the maximal peak absorption around 700 nm,which is exactly matched with the maximum in the photon flux of the sun.
基金supported by the National Natural Science Foundation of China(Nos.6127411311204212 and 61404091)+5 种基金the Program for New Century Excellent Talents in University(No.NCET-11-1064)the Tianjin Natural Science Foundation(Nos.13JCYBJC1570013JCZDJC2610014JCZDJC31500 and 14JCQNJC00800)the Tianjin Science and Technology Developmental Funds of Universities and Colleges(Nos.2010070320130701 and 20130702)
文摘Indium oxide(In_2O_3) films were prepared on Al_2O_3(0001) substrates at 700 °C by metal-organic chemical vapor deposition(MOCVD).Then the samples were annealed at 800 °C,900 °C and 1 000 °C,respectively.The X-ray diffraction(XRD) analysis reveals that the samples were polycrystalline films before and after annealing treatment.Triangle or quadrangle grains can be observed,and the corner angle of the grains becomes smooth after annealing.The highest Hall mobility is obtained for the sample annealed at 900 °C with the value about 24.74 cm^2·V^(-1)·s^(-1).The average transmittance for the films in the visible range is over 90%.The optical band gaps of the samples are about 3.73 e V,3.71 e V,3.70 eV and 3.69 eV corresponding to the In_2O_3 films deposited at 700 °C and annealed at 800 °C,900 °C and 1 000 °C,respectively.