Thickness effects of thin La0.7Sr0.3MnO3 (LSMO) films on (LaAlOa)0.3(Sr2AlTaO6)0.7 substrates were examined by a slow positron beam technique. Doppler-broadening line shape parameter S was measured as a function...Thickness effects of thin La0.7Sr0.3MnO3 (LSMO) films on (LaAlOa)0.3(Sr2AlTaO6)0.7 substrates were examined by a slow positron beam technique. Doppler-broadening line shape parameter S was measured as a function of thickness and differnt annealing conditions. Results reveal there could be more than one mechanism to induce vacancy-like defects. It was found that strain-induced defects mainly influence the S value of the in situ oxygenambience annealing LSMO thin films and the strain could vanish still faster along with the increase of thickness, and the oxygen-deficient induced defects mainly affect the S value of post-annealing LSMO films.展开更多
To achieve a better understanding of the effects of the colossal magnetoresistivity in the mixed valence manganites,the model of a negative magnetoresistivity scaling proposed by Wagner et al is explored in both mat...To achieve a better understanding of the effects of the colossal magnetoresistivity in the mixed valence manganites,the model of a negative magnetoresistivity scaling proposed by Wagner et al is explored in both mathematical and physical analyses.The inconsistency in Wagners model is discussed and corrected. The behaviors of the large spin polarons in Nd 0.52 Sr 0.48 MnO 3 film at T c are studied and analyzed.The results show that only through necessary corrections can Wagners model become self consistent. A further exploration of the nature of the magnetically aligned clusters will make the model more convincing.展开更多
文摘Thickness effects of thin La0.7Sr0.3MnO3 (LSMO) films on (LaAlOa)0.3(Sr2AlTaO6)0.7 substrates were examined by a slow positron beam technique. Doppler-broadening line shape parameter S was measured as a function of thickness and differnt annealing conditions. Results reveal there could be more than one mechanism to induce vacancy-like defects. It was found that strain-induced defects mainly influence the S value of the in situ oxygenambience annealing LSMO thin films and the strain could vanish still faster along with the increase of thickness, and the oxygen-deficient induced defects mainly affect the S value of post-annealing LSMO films.
基金National Natural Science Foundation of China(No.50 0 72 0 1 5) Key Teacher Supporting Project (G0 0 0 32 ) +1 种基金StartingFoundation for Returned ResearchersKey Projectof Science andTechnology Research of National Education Committee
文摘To achieve a better understanding of the effects of the colossal magnetoresistivity in the mixed valence manganites,the model of a negative magnetoresistivity scaling proposed by Wagner et al is explored in both mathematical and physical analyses.The inconsistency in Wagners model is discussed and corrected. The behaviors of the large spin polarons in Nd 0.52 Sr 0.48 MnO 3 film at T c are studied and analyzed.The results show that only through necessary corrections can Wagners model become self consistent. A further exploration of the nature of the magnetically aligned clusters will make the model more convincing.