The lanthanum aluminum mesoporous materials were synthesized using sodium dodecyl sulfate as a template agent by ultrasonic hydrothermal method.The resulting samples were characterized by low angle X-ray diffraction（...The lanthanum aluminum mesoporous materials were synthesized using sodium dodecyl sulfate as a template agent by ultrasonic hydrothermal method.The resulting samples were characterized by low angle X-ray diffraction（XRD）,N2 adsorption-desorption studies,transmission electron microscopy（TEM）and surface morphology analysis（SEM）,surface acid（NH3-TPD）,reducibility properties（TPR）,X-ray energy dispersive spectrometer（EDS）and thermogravimetric analysis（TG/DTG）.A l/La composite mesoporous material were synthesized with n（Al）︰n（La）=70︰1.0,80°C of reaction temperature,20 h of reaction time,12 h of crystallization time,650°C of calcination temperature.The specific surface area of the sample is 273.90 m 2 ·g ？1 ,with the average diameter 5.642 nm and pore volume 0.2354 cm 3 ·g ？1 .The samples have mesoporous structure and its particles are similar to a worm-shaped tubular structure.The influence of calcination temperature on the surface physical and chemical properties of Al/La composited mesoporous materials was examined,and the results showed that the acid strength was increased but the amount of acidic sites is decreased as the calcination temperature increased.It was found that the sample calcined at 650°C had appropriate acid content,acid strength and better reducibility.展开更多
A metal-ligand coordinated surfactant system formed by calcium dodecylsulfate(Ca(DS)2)/tetradecyldimethylamine oxide (C14DMAO)/H2O was studied in terms of surface tension,conductivity,negative-staining TEM,phase behav...A metal-ligand coordinated surfactant system formed by calcium dodecylsulfate(Ca(DS)2)/tetradecyldimethylamine oxide (C14DMAO)/H2O was studied in terms of surface tension,conductivity,negative-staining TEM,phase behavior and rheological operation.In C14DMAO solution,when Ca(DS)2 is added,metal-ligand complexes form between the Ca 2+and N→O group of C14DMAO.Under this metal-ligand driving force,different phases can be obtained at different concentrations and different ratios of Ca(DS)2 and C14DMAO.At the fixed C14DMAO concentration,L1-phase consisting of spherical micelles forms at first.With the addition of Ca(DS)2,the spherical micelles elongate to be wormlike micelles and then after an L1/L-two phase region,the birefringent vesicle-phase(Lv-phase)region is observed.When Ca(DS)2 concentration continues to increase,a gel-phase region is found after the Lv-phase region and then precipitates of undissolved Ca(DS)2 appear.The transition between different phases is affected by temperature remarkably.The wormlike micellar solutions and vesicle solutions were checked by rheological measurements and showed apparent viscoelasticity at high surfactant concentrations.展开更多
文摘The lanthanum aluminum mesoporous materials were synthesized using sodium dodecyl sulfate as a template agent by ultrasonic hydrothermal method.The resulting samples were characterized by low angle X-ray diffraction（XRD）,N2 adsorption-desorption studies,transmission electron microscopy（TEM）and surface morphology analysis（SEM）,surface acid（NH3-TPD）,reducibility properties（TPR）,X-ray energy dispersive spectrometer（EDS）and thermogravimetric analysis（TG/DTG）.A l/La composite mesoporous material were synthesized with n（Al）︰n（La）=70︰1.0,80°C of reaction temperature,20 h of reaction time,12 h of crystallization time,650°C of calcination temperature.The specific surface area of the sample is 273.90 m 2 ·g ？1 ,with the average diameter 5.642 nm and pore volume 0.2354 cm 3 ·g ？1 .The samples have mesoporous structure and its particles are similar to a worm-shaped tubular structure.The influence of calcination temperature on the surface physical and chemical properties of Al/La composited mesoporous materials was examined,and the results showed that the acid strength was increased but the amount of acidic sites is decreased as the calcination temperature increased.It was found that the sample calcined at 650°C had appropriate acid content,acid strength and better reducibility.
基金supported by the National Natural Science Foundation of China (20833010 and 20803045)the Foundation of Ministry of Education of China for New Teachers (200804221008)
文摘A metal-ligand coordinated surfactant system formed by calcium dodecylsulfate(Ca(DS)2)/tetradecyldimethylamine oxide (C14DMAO)/H2O was studied in terms of surface tension,conductivity,negative-staining TEM,phase behavior and rheological operation.In C14DMAO solution,when Ca(DS)2 is added,metal-ligand complexes form between the Ca 2+and N→O group of C14DMAO.Under this metal-ligand driving force,different phases can be obtained at different concentrations and different ratios of Ca(DS)2 and C14DMAO.At the fixed C14DMAO concentration,L1-phase consisting of spherical micelles forms at first.With the addition of Ca(DS)2,the spherical micelles elongate to be wormlike micelles and then after an L1/L-two phase region,the birefringent vesicle-phase(Lv-phase)region is observed.When Ca(DS)2 concentration continues to increase,a gel-phase region is found after the Lv-phase region and then precipitates of undissolved Ca(DS)2 appear.The transition between different phases is affected by temperature remarkably.The wormlike micellar solutions and vesicle solutions were checked by rheological measurements and showed apparent viscoelasticity at high surfactant concentrations.