α‐,β‐,δ‐,andγ‐MnO2nanocrystals are successfully prepared.We then evaluated the NH3selective catalytic reduction(SCR)performance of the MnO2catalysts with different phases.The NOx conversion efficiency decrease...α‐,β‐,δ‐,andγ‐MnO2nanocrystals are successfully prepared.We then evaluated the NH3selective catalytic reduction(SCR)performance of the MnO2catalysts with different phases.The NOx conversion efficiency decreased in the order:γ‐MnO2>α‐MnO2>δ‐MnO2>β‐MnO2.The NOx conversion with the use ofγ‐MnO2andα‐MnO2catalysts reached90%in the temperature range of140–200°C,while that based onβ‐MnO2reached only40%at200°C.Theγ‐MnO2andα‐MnO2nanowire crystal morphologies enabled good dispersion of the catalysts and resulted in a relatively high specific surface area.We found thatγ‐MnO2andα‐MnO2possessed stronger reducing abilities and more and stronger acidic sites than the other catalysts.In addition,more chemisorbed oxygen existed on the surface of theγ‐MnO2andα‐MnO2catalysts.Theγ‐MnO2andα‐MnO2catalysts showed excellent performance in the low‐temperature SCR of NO to N2with NH3.展开更多
Pd-only three-way catalyst （TWC）, Pd supported on washcoating （the mixture of alumina and Ce-Zr solid solution）/cordierite, was prepared and its catalytic performance and the operation window （2-value） at 450 ℃...Pd-only three-way catalyst （TWC）, Pd supported on washcoating （the mixture of alumina and Ce-Zr solid solution）/cordierite, was prepared and its catalytic performance and the operation window （2-value） at 450 ℃ were evaluated with the simulated automotive exhaust feed gas. Surfactants such as Tween-80 and Span-20 were added in the process of preparing the catalyst in order to improve the thermal stability and catalytic performance of Pd-only TWC. The fresh and aged catalysts at 1000 ℃ for 4 h were characterized by low-temperature N2 adsorption, XRD, XPS, and H2-TPR techniques. The results show that the presence of surfactants in the synthesis slurry could influence the physicochemical properties of the final Pd-only TWC. The FTS catalyst prepared with the mixed surfactant of Tween-80 and Span-20 exhibited excellent three-way catalytic performance. After being aged at 1000℃ for 4 h, the catalytic performances of Pd-only TWCs slightly decreased, but the FTS catalyst still demonstrated higher catalytic performance and better thermal stability compared with the Pd-only catalysts prepared with single surfactant or without any surfactant. And the FTS catalyst has a wider 2 value （operation window） than other catalysts, even after being aged at 1000℃.展开更多
Two-dimensional(2 D) transition metal phosphides(TMPs) are predicted with many novel properties and various applications. As a member of TMPs family, molybdenum phosphide(MoP) exhibits many exotic physicochemical prop...Two-dimensional(2 D) transition metal phosphides(TMPs) are predicted with many novel properties and various applications. As a member of TMPs family, molybdenum phosphide(MoP) exhibits many exotic physicochemical properties. However, the synthesis of high-quality2 D MoP single crystals is not reported due to the lack of reliable fabrication method, which limits the exploration of 2 D MoP. Here, we report the growth of high-quality ultrathin MoP single crystals with thickness down to 10 nm on liquid metals via chemical vapor deposition(CVD). The smooth surface of liquid Ga is regarded as a suitable growth substrate for producing 2 D MoP single crystals. The Mo source diffuses toward the Ga surface due to the high surface energy to react with phosphorus source, thus to fabricate ultrathin MoP single crystals. Then, we study the second harmonic generation(SHG) of 2 D MoP for the first time due to its intrinsic noncentrosymmetric structure. Our study provides an new approach to synthesize and explore other 2 D TMPs for future applications.展开更多
基金supported by the National Natural Science Foundation of China(51502221)~~
文摘α‐,β‐,δ‐,andγ‐MnO2nanocrystals are successfully prepared.We then evaluated the NH3selective catalytic reduction(SCR)performance of the MnO2catalysts with different phases.The NOx conversion efficiency decreased in the order:γ‐MnO2>α‐MnO2>δ‐MnO2>β‐MnO2.The NOx conversion with the use ofγ‐MnO2andα‐MnO2catalysts reached90%in the temperature range of140–200°C,while that based onβ‐MnO2reached only40%at200°C.Theγ‐MnO2andα‐MnO2nanowire crystal morphologies enabled good dispersion of the catalysts and resulted in a relatively high specific surface area.We found thatγ‐MnO2andα‐MnO2possessed stronger reducing abilities and more and stronger acidic sites than the other catalysts.In addition,more chemisorbed oxygen existed on the surface of theγ‐MnO2andα‐MnO2catalysts.Theγ‐MnO2andα‐MnO2catalysts showed excellent performance in the low‐temperature SCR of NO to N2with NH3.
基金financially supported by the National Basic Research Program of China(2010CB732300)the National Natural Science Foundation of China(21273150)the National High Technology Research and Development Program of China(2011AA03A406)
文摘Pd-only three-way catalyst （TWC）, Pd supported on washcoating （the mixture of alumina and Ce-Zr solid solution）/cordierite, was prepared and its catalytic performance and the operation window （2-value） at 450 ℃ were evaluated with the simulated automotive exhaust feed gas. Surfactants such as Tween-80 and Span-20 were added in the process of preparing the catalyst in order to improve the thermal stability and catalytic performance of Pd-only TWC. The fresh and aged catalysts at 1000 ℃ for 4 h were characterized by low-temperature N2 adsorption, XRD, XPS, and H2-TPR techniques. The results show that the presence of surfactants in the synthesis slurry could influence the physicochemical properties of the final Pd-only TWC. The FTS catalyst prepared with the mixed surfactant of Tween-80 and Span-20 exhibited excellent three-way catalytic performance. After being aged at 1000℃ for 4 h, the catalytic performances of Pd-only TWCs slightly decreased, but the FTS catalyst still demonstrated higher catalytic performance and better thermal stability compared with the Pd-only catalysts prepared with single surfactant or without any surfactant. And the FTS catalyst has a wider 2 value （operation window） than other catalysts, even after being aged at 1000℃.
基金supported by the National Natural Science Foundation of China (21673161 and 21905210)the Sino-German Center for Research Promotion (GZ 1400)。
文摘Two-dimensional(2 D) transition metal phosphides(TMPs) are predicted with many novel properties and various applications. As a member of TMPs family, molybdenum phosphide(MoP) exhibits many exotic physicochemical properties. However, the synthesis of high-quality2 D MoP single crystals is not reported due to the lack of reliable fabrication method, which limits the exploration of 2 D MoP. Here, we report the growth of high-quality ultrathin MoP single crystals with thickness down to 10 nm on liquid metals via chemical vapor deposition(CVD). The smooth surface of liquid Ga is regarded as a suitable growth substrate for producing 2 D MoP single crystals. The Mo source diffuses toward the Ga surface due to the high surface energy to react with phosphorus source, thus to fabricate ultrathin MoP single crystals. Then, we study the second harmonic generation(SHG) of 2 D MoP for the first time due to its intrinsic noncentrosymmetric structure. Our study provides an new approach to synthesize and explore other 2 D TMPs for future applications.