Biolatex, a new type of paper coating adhesive that has been developed in recent years, has mainly been used in pre-coating and middle coating, due to its advantages of decreasing the associated cost and pollution by ...Biolatex, a new type of paper coating adhesive that has been developed in recent years, has mainly been used in pre-coating and middle coating, due to its advantages of decreasing the associated cost and pollution by partly replacing petro-latex. In this paper, application of biolatex as a surface sizing agent and effects of various factors, such as titanium dioxide addition, on the properties of the sized paper were compared. The results showed that, addition of titanium dioxide to biolatex could improve the whiteness, internal bond strength, and ink absorption. Furthermore, application of the No.4 biolatex resulted in better surface strength, bond strength, and ink absorption of the sized paper than application of polyvinyl alcohol.展开更多
A metal-ligand coordinated surfactant system formed by calcium dodecylsulfate(Ca(DS)2)/tetradecyldimethylamine oxide (C14DMAO)/H2O was studied in terms of surface tension,conductivity,negative-staining TEM,phase behav...A metal-ligand coordinated surfactant system formed by calcium dodecylsulfate(Ca(DS)2)/tetradecyldimethylamine oxide (C14DMAO)/H2O was studied in terms of surface tension,conductivity,negative-staining TEM,phase behavior and rheological operation.In C14DMAO solution,when Ca(DS)2 is added,metal-ligand complexes form between the Ca 2+and N→O group of C14DMAO.Under this metal-ligand driving force,different phases can be obtained at different concentrations and different ratios of Ca(DS)2 and C14DMAO.At the fixed C14DMAO concentration,L1-phase consisting of spherical micelles forms at first.With the addition of Ca(DS)2,the spherical micelles elongate to be wormlike micelles and then after an L1/L-two phase region,the birefringent vesicle-phase(Lv-phase)region is observed.When Ca(DS)2 concentration continues to increase,a gel-phase region is found after the Lv-phase region and then precipitates of undissolved Ca(DS)2 appear.The transition between different phases is affected by temperature remarkably.The wormlike micellar solutions and vesicle solutions were checked by rheological measurements and showed apparent viscoelasticity at high surfactant concentrations.展开更多
文摘Biolatex, a new type of paper coating adhesive that has been developed in recent years, has mainly been used in pre-coating and middle coating, due to its advantages of decreasing the associated cost and pollution by partly replacing petro-latex. In this paper, application of biolatex as a surface sizing agent and effects of various factors, such as titanium dioxide addition, on the properties of the sized paper were compared. The results showed that, addition of titanium dioxide to biolatex could improve the whiteness, internal bond strength, and ink absorption. Furthermore, application of the No.4 biolatex resulted in better surface strength, bond strength, and ink absorption of the sized paper than application of polyvinyl alcohol.
基金supported by the National Natural Science Foundation of China (20833010 and 20803045)the Foundation of Ministry of Education of China for New Teachers (200804221008)
文摘A metal-ligand coordinated surfactant system formed by calcium dodecylsulfate(Ca(DS)2)/tetradecyldimethylamine oxide (C14DMAO)/H2O was studied in terms of surface tension,conductivity,negative-staining TEM,phase behavior and rheological operation.In C14DMAO solution,when Ca(DS)2 is added,metal-ligand complexes form between the Ca 2+and N→O group of C14DMAO.Under this metal-ligand driving force,different phases can be obtained at different concentrations and different ratios of Ca(DS)2 and C14DMAO.At the fixed C14DMAO concentration,L1-phase consisting of spherical micelles forms at first.With the addition of Ca(DS)2,the spherical micelles elongate to be wormlike micelles and then after an L1/L-two phase region,the birefringent vesicle-phase(Lv-phase)region is observed.When Ca(DS)2 concentration continues to increase,a gel-phase region is found after the Lv-phase region and then precipitates of undissolved Ca(DS)2 appear.The transition between different phases is affected by temperature remarkably.The wormlike micellar solutions and vesicle solutions were checked by rheological measurements and showed apparent viscoelasticity at high surfactant concentrations.