In order to improve the property of traditional Ce-based conversion coatings, Ce-silane-ZrO2 composite coatings were successfully prepared on 1060 aluminum. The microstructure, chemical element composition and corrosi...In order to improve the property of traditional Ce-based conversion coatings, Ce-silane-ZrO2 composite coatings were successfully prepared on 1060 aluminum. The microstructure, chemical element composition and corrosion resistance of Ce-based conversion coatings and Ce-silane-ZrO2 composite coatings were investigated by SEM, AFM, XPS and EIS analyses. Stacking structure of the composite coating can be observed. The inner layer of the composite coatings mainly consists of oxide and hydroxide of Ce（Ⅲ）, and the silane network is composed of the outer layer together with a small amount of Ce（Ⅳ） hydroxide. By adding silane and ZrO2 nanoparticles into Ce-based conversion coatings, the porosity and the micro cracks of the coatings decrease apparently accompanying with the improvement of the corrosion resistance.展开更多
基金Project(51172217)supported by the National Natural Science Foundation of ChinaProject(2010GGX10310)supported by Shandong Science and Technology Program,China+1 种基金Project(10-3-4-1-jch)supported by Science and Technology Program on Basic Research Project of Qingdao,ChinaProject(4500-841313001)supported by Fundamental Research Funds for the Central Universities,China
文摘In order to improve the property of traditional Ce-based conversion coatings, Ce-silane-ZrO2 composite coatings were successfully prepared on 1060 aluminum. The microstructure, chemical element composition and corrosion resistance of Ce-based conversion coatings and Ce-silane-ZrO2 composite coatings were investigated by SEM, AFM, XPS and EIS analyses. Stacking structure of the composite coating can be observed. The inner layer of the composite coatings mainly consists of oxide and hydroxide of Ce（Ⅲ）, and the silane network is composed of the outer layer together with a small amount of Ce（Ⅳ） hydroxide. By adding silane and ZrO2 nanoparticles into Ce-based conversion coatings, the porosity and the micro cracks of the coatings decrease apparently accompanying with the improvement of the corrosion resistance.