Three poly(vinyl acetate)(PVAc)oligomers with controlled molecular weight and narrow molecular distribution are synthesized by reversible addition-fragmentation chain transfer(RAFT)polymerization.The effects of the re...Three poly(vinyl acetate)(PVAc)oligomers with controlled molecular weight and narrow molecular distribution are synthesized by reversible addition-fragmentation chain transfer(RAFT)polymerization.The effects of the reaction temperature and the added amount of initiator of the PVAc polymerization are discussed.In addition,the phase behavior of the prepared PVAc in pressured CO2 is determined via the cloud point method.The results indicate that the cloud point of PVAc increases with the increase in the molecular weight,the PVAc concentration,and the temperature.The cloud point pressures for the PVAc mass concentration of 0.12%with the molecular weight of 1 550,2 120,and 2 960 g/mol are 13.48,13.83 and 15.43 MPa,respectively,at the temperature of 35℃.It reveals that the solubility of PVAc in ScCO2 at relatively low pressure is remarkably limited.展开更多
A quartz crystal microbalance （QCM） is used to determine the phase equilibrium of paclitaxel-carbon dioxide system in the pressure range of 0-11 MPa and at temperatures of 35 °C,40 °C and 45 °C.The ex...A quartz crystal microbalance （QCM） is used to determine the phase equilibrium of paclitaxel-carbon dioxide system in the pressure range of 0-11 MPa and at temperatures of 35 °C,40 °C and 45 °C.The experimental results indicated that gaseous CO2 could be absorbed poorly into paclitaxel.The swelling of paclitaxel film in CO2 was observed before paclitaxel dissolved into supercritical carbon dioxide （ScCO2） with the increase of pressure.It was found that ScCO2 was not a good solvent for paclitaxel.The mole fraction of paclitaxel in ScCO2 was in the range of （4.5×10-9）-（7.8×10-9） under all our experimental conditions.Therefore,a much higher pressure than the CO2 supercritical point and/or a cosolvent must be used in any processes wherever paclitaxel dissolution in ScCO2 is required.展开更多
基金The Natural Science Foundation of Jiangsu Province(No.BK20130602)the Applied Basic Research Program of Suzhou(No.SYG201836)the Project of the Collaborative Innovation Center of Suzhou Nano Science and Technology
文摘Three poly(vinyl acetate)(PVAc)oligomers with controlled molecular weight and narrow molecular distribution are synthesized by reversible addition-fragmentation chain transfer(RAFT)polymerization.The effects of the reaction temperature and the added amount of initiator of the PVAc polymerization are discussed.In addition,the phase behavior of the prepared PVAc in pressured CO2 is determined via the cloud point method.The results indicate that the cloud point of PVAc increases with the increase in the molecular weight,the PVAc concentration,and the temperature.The cloud point pressures for the PVAc mass concentration of 0.12%with the molecular weight of 1 550,2 120,and 2 960 g/mol are 13.48,13.83 and 15.43 MPa,respectively,at the temperature of 35℃.It reveals that the solubility of PVAc in ScCO2 at relatively low pressure is remarkably limited.
基金Supported by the Jiangsu High-tech Project(BG2006038)
文摘A quartz crystal microbalance （QCM） is used to determine the phase equilibrium of paclitaxel-carbon dioxide system in the pressure range of 0-11 MPa and at temperatures of 35 °C,40 °C and 45 °C.The experimental results indicated that gaseous CO2 could be absorbed poorly into paclitaxel.The swelling of paclitaxel film in CO2 was observed before paclitaxel dissolved into supercritical carbon dioxide （ScCO2） with the increase of pressure.It was found that ScCO2 was not a good solvent for paclitaxel.The mole fraction of paclitaxel in ScCO2 was in the range of （4.5×10-9）-（7.8×10-9） under all our experimental conditions.Therefore,a much higher pressure than the CO2 supercritical point and/or a cosolvent must be used in any processes wherever paclitaxel dissolution in ScCO2 is required.