Ultrasonic vibrations in coal lead to cavitation bubble oscillation, growth, shrinkage, and collapse, and the strong vibration of cavitation bubbles not only makes coal pores break and cracks propagate, but plays an i...Ultrasonic vibrations in coal lead to cavitation bubble oscillation, growth, shrinkage, and collapse, and the strong vibration of cavitation bubbles not only makes coal pores break and cracks propagate, but plays an important role in enhancing the permeability of coal. In this paper, the influence of ultrasonic cavitation on coal and the effects of the sonic waves on crack generation, propagation, connection, as well as the effect of cracks on the coal permeability, are studied. The experimental results show that cracks in coal are generated even connected rapidly after ultrasonic cavitation. Under the effect of ultrasonic cavitation,the permeability increases between 30% and 60%, and the number of cracks in coal also significantly increased. Numerical experiments show that the effective sound pressure is beneficial to fracture propagation and connection, and it is closely related to the permeability. Moreover, the numerical simulations and physical experiments provide a guide for the coal permeability improvement.展开更多
The brazing of 55% SiCp/A356 (volume fraction) composites in air using Zn-Al alloy as a filler metal was investigated.During the brazing process,ultrasonic vibrations were applied to samples for bonding and a signific...The brazing of 55% SiCp/A356 (volume fraction) composites in air using Zn-Al alloy as a filler metal was investigated.During the brazing process,ultrasonic vibrations were applied to samples for bonding and a significant dissolution of the filler metal into the matrix alloy in the base materials occurred.As brazing temperatures were increased,the thickness of the partial melting layers in the base material increased.SiC particles in the partial melting layer of the base material were transferred into the liquid filler under ultrasonic action and a bond with homogeneously distributed reinforcements was obtained after solidification.The volume fraction of SiC particles in the bonds could be varied by changing the brazing temperature.The maximum SiC particle volume fraction of the bond material reached 37% at a brazing temperature of 500 ℃.The shear strength of the brazed bonds was improved at pressures up to 244 MPa (at 20 ℃) and increased by 133.8% (at 200 ℃) compared with the filler of the Zn-based alloy.展开更多
基金supported by the National Natural Science Foundation of China (No. 51574114)the National Key Research and Development Program (No. 2016YFC0600901)
文摘Ultrasonic vibrations in coal lead to cavitation bubble oscillation, growth, shrinkage, and collapse, and the strong vibration of cavitation bubbles not only makes coal pores break and cracks propagate, but plays an important role in enhancing the permeability of coal. In this paper, the influence of ultrasonic cavitation on coal and the effects of the sonic waves on crack generation, propagation, connection, as well as the effect of cracks on the coal permeability, are studied. The experimental results show that cracks in coal are generated even connected rapidly after ultrasonic cavitation. Under the effect of ultrasonic cavitation,the permeability increases between 30% and 60%, and the number of cracks in coal also significantly increased. Numerical experiments show that the effective sound pressure is beneficial to fracture propagation and connection, and it is closely related to the permeability. Moreover, the numerical simulations and physical experiments provide a guide for the coal permeability improvement.
基金Project(50375039) supported by the National Natural Science Foundation of ChinaProject supported by the Excellence Team Program at the Harbin Institute of Technology,China
文摘The brazing of 55% SiCp/A356 (volume fraction) composites in air using Zn-Al alloy as a filler metal was investigated.During the brazing process,ultrasonic vibrations were applied to samples for bonding and a significant dissolution of the filler metal into the matrix alloy in the base materials occurred.As brazing temperatures were increased,the thickness of the partial melting layers in the base material increased.SiC particles in the partial melting layer of the base material were transferred into the liquid filler under ultrasonic action and a bond with homogeneously distributed reinforcements was obtained after solidification.The volume fraction of SiC particles in the bonds could be varied by changing the brazing temperature.The maximum SiC particle volume fraction of the bond material reached 37% at a brazing temperature of 500 ℃.The shear strength of the brazed bonds was improved at pressures up to 244 MPa (at 20 ℃) and increased by 133.8% (at 200 ℃) compared with the filler of the Zn-based alloy.