Fabrication and anti-corrosion performance of superhydrophobic silane film on sintered NdFeB

An eco-friendly superhydrophobic protective film(DTMS/TEOS silane film)was fabricated on sintered NdFeB substrate through the utilization of electrochemically assisted deposition technology.The structure,properties,and film-forming mechanism of dodecyltrime-thoxysilane(DTMS)/tetraethoxysilane(TEOS)silane films were comprehensively analyzed using Fourier transform infrared spectroscopy(FT-IR),scanning electron microscopy(SEM),X-ray photoelectron spectroscopy(XPS),potentiodynamic polarization curves and electrochemical impedance spectroscopy(EIS).Based on the test results,it can be determined that this film has a superhydrophobic property with a hydrophobicity angle of 152°.This special property can be attributed to the long alkyl chains in the DTMS molecule,the rough morphology,and the low surface energy of the DTMS/TEOS silane film.The surface of sintered NdFeB is coated with a layered three-dimensional network silane film that forms through the condensation of silanol substances.This film provides excellent corrosion resistance to the sintered NdFeB substrate,reducing its corrosion current density to 2.02×10~(-6)A/cm~2.Moreover,the impact of film on the magnetic characteristics of sintered NdFeB was assessed and found to be minimal.

Effects of ultrasonic vibration on solidification structure and properties of Mg-8Li-3Al alloy

Ultrasonic vibration was introduced into the Mg-8Li-3A1 alloy melt during its solidification process. The microstructure, corrosion resistance and mechanical properties of the Mg-8Li-3A1 alloy under ultrasonic vibration were investigated. The experiment results show that the morphology of a phase is modified from coarse rosette-like structure to fine globular one with the application of ultrasonic vibration. The fine globular structure is obtained especially when the power is 170 W, and the refining effect also gets better with prolonging the ultrasonic treatment time. The corrosion resistance of the alloy with 170 W of ultrasonic vibration for 90 s is improved apparently compared with the alloy without ultrasonic vibration. The mechanical properties of alloys with ultrasonic vibration are also both improved apparently. The tensile strength and elongation of alloy improve by 9.5% and 45.7%, respectively, with 170 W of ultrasonic treatment for 90 s.

Enhanced corrosion resistance of micro-arc oxidation coated magnesium alloy by superhydrophobic Mg-Al layered double hydroxide coating

To further enhance the corrosion resistance of the porous micro-arc oxidation(MAO) ceramic layers on AZ31 magnesium alloy, superhydrophobic Mg-Al layered double hydroxide(LDH) coating was fabricated on MAO-coated AZ31 alloy by using in-situ growth method followed by surface modification with stearic acid. The characteristics of different coatings were investigated by XRD, SEM and EDS. The effect of the hydrothermal treatment time on the formation of the LDH coatings was studied. The results demonstrated that the micro-pores and cracks of MAO coating were gradually sealed via in-situ growing LDH with prolonging hydrothermal treating time. Electrochemical measurement displayed that the lowest corrosion current density, the most positive corrosion potential and the highest impedance modulus were observed for superhydrophobic LDH/MAO coating compared with those of MAO coating and LDH/MAO coating. Immersion experiment proved that the superhydrophobic LDH/MAO coating with the active anti-corrosion capability significantly enhanced the long-term corrosion protection for MAO coated alloy.

Characterization of mechanical and corrosion properties of cryorolled Al 1100 alloy:Effect of annealing and solution treatment

Effect of annealing and solution treatment prior to cryorolling on the formation of initial structure influencing microstructure formation from nano to micron scale and resultant mechanical and corrosion properties in Al 1100 alloy has been studied in detail.Before subjecting to 50%cryorolling,samples were pre-annealed at 250℃ for 2 h and pre-solution treated at 540℃ for 1 h.X-ray diffraction and HRTEM techniques were used to understand the crystallite size,lattice strain and dislocation configuration in the processed alloy.The results indicate that the pre-annealed sample has the highest grain aspect ratio(4.43),the smallest crystallite size(37.53 nm),the highest lattice strain(9.12×10^(−3))and the highest dislocation density(45.16×10^(13) m^(−2))among the tested sample.The pre-annealed sample shows a significant improvement of 43.44%,24.64%and 20.33%in hardness,ultimate tensile strength and yield strength.Both pre-annealed and pre-solution treated samples show improved corrosion resistance when compared to cryorolled samples without any pre-treatment,with the pre-annealed sample showing the best corrosion resistance.