The coupling between electrochemically active material and conductive matrix is vitally important for high efficiency lithium ion batteries （LIBs）. By introducing oxygen groups into the nanoporous carbon framework, ...The coupling between electrochemically active material and conductive matrix is vitally important for high efficiency lithium ion batteries （LIBs）. By introducing oxygen groups into the nanoporous carbon framework, we accom- plish sustainably enhanced electrochemical performance for a SnO2/carbon LIB. 2-5 nm SnO2 nanoparticles are hydro- thermally grown in different nanoporous carbon frameworks, which are pristine, nitrogen- or oxygen-doped carbons. Compared with pristine and nitrogen-doped carbon hosts, the SnO2/oxygen-doped activated carbon （OAC） composite ex- hibits a higher discharge capacity of 1,122mAhg^-1 at 500 mA g^-1 after 320 cycles operation and a larger lithium storage capacity up to 680 mAhg-I at a high rate of 2,000 mA g^-1. The exceptional electrochemical performance originated from the oxygen groups, which could act as Lewis acid sites to attract electrons effectively from Sn during the charge process, thus accelerating reversible conversion of Sn to SnO2. Meanwhile, SnO2 nanoparticles are effectively bonded with carbon through such oxygen groups, thus preventing the electrochemical sintering and maintaining the cycling stability of the SnO2/OAC composite anode. The high electrochemical performance, low biomass cost, and facile preparation renders the SnO2/OAC composites a promising candidate for anode materials.展开更多
基金supported by the National High Technology Research and Development Program of China(2012AA053305 and 2014AA052501)the National Natural Science Foundation of China(21506224)
文摘The coupling between electrochemically active material and conductive matrix is vitally important for high efficiency lithium ion batteries （LIBs）. By introducing oxygen groups into the nanoporous carbon framework, we accom- plish sustainably enhanced electrochemical performance for a SnO2/carbon LIB. 2-5 nm SnO2 nanoparticles are hydro- thermally grown in different nanoporous carbon frameworks, which are pristine, nitrogen- or oxygen-doped carbons. Compared with pristine and nitrogen-doped carbon hosts, the SnO2/oxygen-doped activated carbon （OAC） composite ex- hibits a higher discharge capacity of 1,122mAhg^-1 at 500 mA g^-1 after 320 cycles operation and a larger lithium storage capacity up to 680 mAhg-I at a high rate of 2,000 mA g^-1. The exceptional electrochemical performance originated from the oxygen groups, which could act as Lewis acid sites to attract electrons effectively from Sn during the charge process, thus accelerating reversible conversion of Sn to SnO2. Meanwhile, SnO2 nanoparticles are effectively bonded with carbon through such oxygen groups, thus preventing the electrochemical sintering and maintaining the cycling stability of the SnO2/OAC composite anode. The high electrochemical performance, low biomass cost, and facile preparation renders the SnO2/OAC composites a promising candidate for anode materials.