In this study,hydrogels of P(NIPA-co-NVP)/clay were synthesized byγ-ray radiation.Different thermo-sensitive hydrogels were made under different experimental conditions such as dose,monomer ratio,and con- tent of cla...In this study,hydrogels of P(NIPA-co-NVP)/clay were synthesized byγ-ray radiation.Different thermo-sensitive hydrogels were made under different experimental conditions such as dose,monomer ratio,and con- tent of clay.X-ray diffraction shows that the layer distance between Na-clays is changed from 1.6 to 2.7 nm because Na-clay pieces can be intercalated or exfoliated by HTMAB,and that between P(NIPA-co-NVP)/clay pieces is 3.4 nm. The swelling property tests show that the LCST of P(NIPA-co-NVP) is higher than PNIPA.With the increase of NVP content,LCST is higher.As the ratio of NIPA/NVP is 95/5,hydrogel shows the best swelling property and LCST is 37℃.LCST of P(NIPA-co-NVP)/clay hydrogel is not changed,but the strength and swelling properties are better.展开更多
基金Supported by Natural Science Foundation of Henan Province,China(0611023900)
文摘In this study,hydrogels of P(NIPA-co-NVP)/clay were synthesized byγ-ray radiation.Different thermo-sensitive hydrogels were made under different experimental conditions such as dose,monomer ratio,and con- tent of clay.X-ray diffraction shows that the layer distance between Na-clays is changed from 1.6 to 2.7 nm because Na-clay pieces can be intercalated or exfoliated by HTMAB,and that between P(NIPA-co-NVP)/clay pieces is 3.4 nm. The swelling property tests show that the LCST of P(NIPA-co-NVP) is higher than PNIPA.With the increase of NVP content,LCST is higher.As the ratio of NIPA/NVP is 95/5,hydrogel shows the best swelling property and LCST is 37℃.LCST of P(NIPA-co-NVP)/clay hydrogel is not changed,but the strength and swelling properties are better.