The solidified structures of horizontally continuous casting（HCC） of super-thin slab and its relations with the current were studied under the electromagnetic vibration（EMV）.The results show that,under the action ...The solidified structures of horizontally continuous casting（HCC） of super-thin slab and its relations with the current were studied under the electromagnetic vibration（EMV）.The results show that,under the action of the periodical forces from EMV,the solidified structures of the super-thin slab of pure tin is greatly refined,and the extent of grain refinement is increased with the magnitude of alternating current.For the Sn-10%Pb alloy,it is shown that the EMV promotes the growth of equiaxed grains in the center of super-thin slab,and the grains are refined with the alternating current increasing.This is useful to prevent some solidification defects in the horizontally continuous casting of super-thin slab,such as columnar grains butting,porosity,inclusions and gases gathering,and composition segregation in the centre of slab.展开更多
The distribution and characteristics of nonmetallic micro-inclusions of GCr15 bearing steel were explored through metallographic area method in virtue of tracer method and electronic microscope.The results show that t...The distribution and characteristics of nonmetallic micro-inclusions of GCr15 bearing steel were explored through metallographic area method in virtue of tracer method and electronic microscope.The results show that the micro-inclusions,of which the average value is 0.032%,are mainly the compounds formed via the adsorption/aggregation of multielement deoxidized compounds and secondarily deoxidized products on tundish liquid level.The micro-inclusions of diameters from 0 to 5 μm are 92.5% in total,which basically determines the characteristics of inclusions distribution in casting slab.The inclusions of diameters more than 10 μm only account for less than 1% in total,which have little influence on steel quality.The relationship between equilibrium compositions of the first deoxidation products and molten steel compositions was also calculated based on thermodynamic theory.展开更多
Based on hot metal pretreatment （HMPT）-basic oxygen furnace （BOF）-Rheinstahl Heraeus （RH）-compact strip production （CSP） process, parameters controlling on cold rolling deep drawing substrate SPHE were investi...Based on hot metal pretreatment （HMPT）-basic oxygen furnace （BOF）-Rheinstahl Heraeus （RH）-compact strip production （CSP） process, parameters controlling on cold rolling deep drawing substrate SPHE were investigated during smelting and rolling process by composition design and technology control. The influence of parameters on chemical compositions, mechanical properties and microstructure was revealed by scanning electron microscope （SEM）. The results show that, 1） main chemical components in SPHE are w（C）_〈40×10^-6, w（Si）_〈 0.01%, w（S）_〈0.009%, w（N）〈20×10^-6, w（O）〈_ 25×10^-6; 2） main mechanical properties of the SPHE are Crs=274 MPa, 00=334 MPa, A=48.9%; 3） main performances of deep drawing quality （DDQ） grade steel produced by SPHE are as follows, transversely crs=167 MPa, 00=298 MPa, n=0.219, r=2.46; vertically σs=166 MPa, 00=298 MPa, n=0.226, r=2.39; in 45° direction σ=171 MPa, 00=308 MPa, n=0.214, t=2.26; 4） microstrueture of DDQ is ferrite, average grain size is Grade 7.5, and inclusion size is 3-10μm.展开更多
基金Project(50674066)supported by the National Natural Science Foundation of China
文摘The solidified structures of horizontally continuous casting（HCC） of super-thin slab and its relations with the current were studied under the electromagnetic vibration（EMV）.The results show that,under the action of the periodical forces from EMV,the solidified structures of the super-thin slab of pure tin is greatly refined,and the extent of grain refinement is increased with the magnitude of alternating current.For the Sn-10%Pb alloy,it is shown that the EMV promotes the growth of equiaxed grains in the center of super-thin slab,and the grains are refined with the alternating current increasing.This is useful to prevent some solidification defects in the horizontally continuous casting of super-thin slab,such as columnar grains butting,porosity,inclusions and gases gathering,and composition segregation in the centre of slab.
基金Supported by Natural Science Foundation of Hebei Province (No.502265)
文摘The distribution and characteristics of nonmetallic micro-inclusions of GCr15 bearing steel were explored through metallographic area method in virtue of tracer method and electronic microscope.The results show that the micro-inclusions,of which the average value is 0.032%,are mainly the compounds formed via the adsorption/aggregation of multielement deoxidized compounds and secondarily deoxidized products on tundish liquid level.The micro-inclusions of diameters from 0 to 5 μm are 92.5% in total,which basically determines the characteristics of inclusions distribution in casting slab.The inclusions of diameters more than 10 μm only account for less than 1% in total,which have little influence on steel quality.The relationship between equilibrium compositions of the first deoxidation products and molten steel compositions was also calculated based on thermodynamic theory.
基金Project(50971135) supported by the National Natural Science Foundation of China
文摘Based on hot metal pretreatment （HMPT）-basic oxygen furnace （BOF）-Rheinstahl Heraeus （RH）-compact strip production （CSP） process, parameters controlling on cold rolling deep drawing substrate SPHE were investigated during smelting and rolling process by composition design and technology control. The influence of parameters on chemical compositions, mechanical properties and microstructure was revealed by scanning electron microscope （SEM）. The results show that, 1） main chemical components in SPHE are w（C）_〈40×10^-6, w（Si）_〈 0.01%, w（S）_〈0.009%, w（N）〈20×10^-6, w（O）〈_ 25×10^-6; 2） main mechanical properties of the SPHE are Crs=274 MPa, 00=334 MPa, A=48.9%; 3） main performances of deep drawing quality （DDQ） grade steel produced by SPHE are as follows, transversely crs=167 MPa, 00=298 MPa, n=0.219, r=2.46; vertically σs=166 MPa, 00=298 MPa, n=0.226, r=2.39; in 45° direction σ=171 MPa, 00=308 MPa, n=0.214, t=2.26; 4） microstrueture of DDQ is ferrite, average grain size is Grade 7.5, and inclusion size is 3-10μm.