The support of catalyst for the direct synthesis of diphenyl carbonate （DPC） by heterogeneous catalytic reaction was prepared by the sol-gel method. Compared with activated charcoal, molecular sieve, porous ceramics...The support of catalyst for the direct synthesis of diphenyl carbonate （DPC） by heterogeneous catalytic reaction was prepared by the sol-gel method. Compared with activated charcoal, molecular sieve, porous ceramics, hopcalite, the support prepared by the sol-gel method has higher activity. The characterization of the support by X-ray diffraction （XRD） and transmission electron microscope （TEM） show that the mare crystal phase is Co2MnO4 and the average particle diameter is about 40 nm. The optimum conditions for synthesis of the support were determined by orthogonal experiments, which indicate that the proportion of Cu, Mn, and Co is the first important factor influencing the yield and selectivity of DPC. Temperature of calcination is the second one. The optimum conditions are： molar proportion of Cu, Mn, and Co being 1 ： 1 ： 1, temperature of calcination 700℃, drying at 100~C, temperature of water bath 85~C. The yield and selectivity of DPC in the process can reach 38% and 99% in the batch operation, respectively. The copper cobalt manganese mixed oxides chosen as the support contribute more to the high catalytic activity than the sol-gel method.展开更多
A new solid acid catalyst,SO4^2-/TiO2 modified with tin,was prepared using a sol-gel method and its physicochemical properties were revealed by nitrogen adsorption-desorption,X-ray powder diffraction,scanning electron...A new solid acid catalyst,SO4^2-/TiO2 modified with tin,was prepared using a sol-gel method and its physicochemical properties were revealed by nitrogen adsorption-desorption,X-ray powder diffraction,scanning electron microscopy,Fourier transform infrared spectroscopy,infrared spectroscopy of adsorbed pyridine,temperature-programmed desorption of ammonia and thermal gravimetric analysis.The structure,acidity and thermal stability of the SO4^2-/TiO2-SnO2 catalyst were studied.Incorporating tin enlarged the specific surface area and decreased crystallite size of the SO4^2-/TiO2 catalyst.The total acid sites of the modified catalyst increased and Bronsted acid strength remarkably increased with increasing tin content.The decomposition temperature of sulfate radical in the modified catalyst was 100 ℃ greater and its mass loss was more than twice that of the SO4^2-/TiO2 catalyst.The SO4^2-/TiO2-SnO2 catalyst was designed to synthesize 1,6-hexanediol diacrylate by esterification of 1,6-hexanediol with crylic acid.The yield of 1,6-hexanediol diacrylate exceeded 87% under the optimal reaction conditions：crylic acid to 1,6-hexanediol molar ratio = 3.5,catalyst loading = 7%,reaction temperature = 130 ℃ and reaction time = 3 h.The modified catalyst exhibited excellent reusability and after 10 cycles the conversion of 1,6-hexanediol was above 81%.展开更多
文摘The support of catalyst for the direct synthesis of diphenyl carbonate （DPC） by heterogeneous catalytic reaction was prepared by the sol-gel method. Compared with activated charcoal, molecular sieve, porous ceramics, hopcalite, the support prepared by the sol-gel method has higher activity. The characterization of the support by X-ray diffraction （XRD） and transmission electron microscope （TEM） show that the mare crystal phase is Co2MnO4 and the average particle diameter is about 40 nm. The optimum conditions for synthesis of the support were determined by orthogonal experiments, which indicate that the proportion of Cu, Mn, and Co is the first important factor influencing the yield and selectivity of DPC. Temperature of calcination is the second one. The optimum conditions are： molar proportion of Cu, Mn, and Co being 1 ： 1 ： 1, temperature of calcination 700℃, drying at 100~C, temperature of water bath 85~C. The yield and selectivity of DPC in the process can reach 38% and 99% in the batch operation, respectively. The copper cobalt manganese mixed oxides chosen as the support contribute more to the high catalytic activity than the sol-gel method.
文摘A new solid acid catalyst,SO4^2-/TiO2 modified with tin,was prepared using a sol-gel method and its physicochemical properties were revealed by nitrogen adsorption-desorption,X-ray powder diffraction,scanning electron microscopy,Fourier transform infrared spectroscopy,infrared spectroscopy of adsorbed pyridine,temperature-programmed desorption of ammonia and thermal gravimetric analysis.The structure,acidity and thermal stability of the SO4^2-/TiO2-SnO2 catalyst were studied.Incorporating tin enlarged the specific surface area and decreased crystallite size of the SO4^2-/TiO2 catalyst.The total acid sites of the modified catalyst increased and Bronsted acid strength remarkably increased with increasing tin content.The decomposition temperature of sulfate radical in the modified catalyst was 100 ℃ greater and its mass loss was more than twice that of the SO4^2-/TiO2 catalyst.The SO4^2-/TiO2-SnO2 catalyst was designed to synthesize 1,6-hexanediol diacrylate by esterification of 1,6-hexanediol with crylic acid.The yield of 1,6-hexanediol diacrylate exceeded 87% under the optimal reaction conditions：crylic acid to 1,6-hexanediol molar ratio = 3.5,catalyst loading = 7%,reaction temperature = 130 ℃ and reaction time = 3 h.The modified catalyst exhibited excellent reusability and after 10 cycles the conversion of 1,6-hexanediol was above 81%.
