Ti6Al4V alloy was subjected to hydrothermal treatment in the concentrated Ca3(PO4)2, Ca HPO4 and Ca(H2PO4)2 solutions for bioactive surface modification. The treated samples are covered by films composed of nano-parti...Ti6Al4V alloy was subjected to hydrothermal treatment in the concentrated Ca3(PO4)2, Ca HPO4 and Ca(H2PO4)2 solutions for bioactive surface modification. The treated samples are covered by films composed of nano-particles with the size of 60-240 nm. Such film can also be grown on the strut surface of a Ti6Al4 V scaffold prepared by electron beam melting(EBM) technology. XPS analysis indicates that Ti element on the surface presents as TiO2, and Ca and P elements are in the form of calcium phosphate. XRD and Raman analyses show that the surface layer is composed of anatase TiO2 and hydroxyapatite. Potentiodynamic polarization test in a Ca-free Hank's balanced solution demonstrates that the treated sample has markedly improved corrosion resistance compared with the polished sample. The present work provides a bioactive surface modification method that is easily-operated, low-temperature, less corrosion, and applicable to porous Ti6Al4 V alloy for biomedical applications.展开更多
In order to produceα-calcium sulfate hemihydrate(α-CaSO4·0.5H2O)whiskers with high aspect ratios,a minor amount of CuCl2·2H2O was used as the modifying agent in the process of hydrothermal treatment of cal...In order to produceα-calcium sulfate hemihydrate(α-CaSO4·0.5H2O)whiskers with high aspect ratios,a minor amount of CuCl2·2H2O was used as the modifying agent in the process of hydrothermal treatment of calcium sulfate dihydrate(CaSO4·2H2O)precursor.The presence of 2.60×10–3 mol/L CuCl2·2H2O resulted in the increase of the aspect ratios ofα-CaSO4·0.5H2O whiskers from 81 to 253.The preferential adsorption of Cu2+on the negative{110}and{100}facets ofα-CaSO4·0.5H2O crystal structures was confirmed by EDS and XPS.And ATR-FTIR demonstrated the ligand adsorption of Cu2+on the surface ofα-CaSO4·0.5H2O whiskers.The experimental results reveal that the whiskers with high aspect ratios are attributed to the adsorption of Cu2+,which promotes the 1-D growth ofα-CaSO4·0.5H2O whiskers along the c axis.展开更多
A precursor of cobaltous dihydroxycarbonate was firstly prepared by precipitation reaction of cobalt sulfate solution and ammonium carbonate solution,and then a hydrothermal process for the precursor was conducted to ...A precursor of cobaltous dihydroxycarbonate was firstly prepared by precipitation reaction of cobalt sulfate solution and ammonium carbonate solution,and then a hydrothermal process for the precursor was conducted to obtain the spherical cobalt carbonate with low sulfur content.The experimental results show that the feeding method,final p H value of the precipitation reaction slurry and the concentration of the cobalt sulfate solution have obvious effects on the sulfur content,morphology and particle size distribution of the precursor.The sulfur content of the precursor is 0.0115 wt.%under the optimized conditions.The hydrothermal treatment with temperatures of 125-150℃can transform the precursor of cobaltous dihydroxycarbonate into spherical cobalt carbonate and decrease the sulfur content to 0.0030 wt.%in the obtained product.展开更多
基金Projects(xjj2011096,CHD2011JC001)supported by the Fundamental Research Fund for the Central Universities,ChinaProjects(50901058,51374174)supported by the National Natural Science Foundation of ChinaProject(2013JZ015)supported by the Science and Technology Program of Shaanxi Province,China
文摘Ti6Al4V alloy was subjected to hydrothermal treatment in the concentrated Ca3(PO4)2, Ca HPO4 and Ca(H2PO4)2 solutions for bioactive surface modification. The treated samples are covered by films composed of nano-particles with the size of 60-240 nm. Such film can also be grown on the strut surface of a Ti6Al4 V scaffold prepared by electron beam melting(EBM) technology. XPS analysis indicates that Ti element on the surface presents as TiO2, and Ca and P elements are in the form of calcium phosphate. XRD and Raman analyses show that the surface layer is composed of anatase TiO2 and hydroxyapatite. Potentiodynamic polarization test in a Ca-free Hank's balanced solution demonstrates that the treated sample has markedly improved corrosion resistance compared with the polished sample. The present work provides a bioactive surface modification method that is easily-operated, low-temperature, less corrosion, and applicable to porous Ti6Al4 V alloy for biomedical applications.
基金Project(B14034)supported by the National 111 Project,ChinaProject(2015CX005)supported by the Innovation Driven Plan of Central South University,ChinaProject(2016zzts104)supported by the Fundamental Research Funds for the Central Universities,China
文摘In order to produceα-calcium sulfate hemihydrate(α-CaSO4·0.5H2O)whiskers with high aspect ratios,a minor amount of CuCl2·2H2O was used as the modifying agent in the process of hydrothermal treatment of calcium sulfate dihydrate(CaSO4·2H2O)precursor.The presence of 2.60×10–3 mol/L CuCl2·2H2O resulted in the increase of the aspect ratios ofα-CaSO4·0.5H2O whiskers from 81 to 253.The preferential adsorption of Cu2+on the negative{110}and{100}facets ofα-CaSO4·0.5H2O crystal structures was confirmed by EDS and XPS.And ATR-FTIR demonstrated the ligand adsorption of Cu2+on the surface ofα-CaSO4·0.5H2O whiskers.The experimental results reveal that the whiskers with high aspect ratios are attributed to the adsorption of Cu2+,which promotes the 1-D growth ofα-CaSO4·0.5H2O whiskers along the c axis.
基金Project(51874372)supported by the National Natural Science Foundation of China
文摘A precursor of cobaltous dihydroxycarbonate was firstly prepared by precipitation reaction of cobalt sulfate solution and ammonium carbonate solution,and then a hydrothermal process for the precursor was conducted to obtain the spherical cobalt carbonate with low sulfur content.The experimental results show that the feeding method,final p H value of the precipitation reaction slurry and the concentration of the cobalt sulfate solution have obvious effects on the sulfur content,morphology and particle size distribution of the precursor.The sulfur content of the precursor is 0.0115 wt.%under the optimized conditions.The hydrothermal treatment with temperatures of 125-150℃can transform the precursor of cobaltous dihydroxycarbonate into spherical cobalt carbonate and decrease the sulfur content to 0.0030 wt.%in the obtained product.