Porous Ti3SiC2with high purity was synthesized using TiH2,Si and C powders with mole ratio of Ti to Si to C being3:1.2:2by reactive synthesis method.The corrosion behaviors of porous Ti3SiC2in nitric acid and aqua reg...Porous Ti3SiC2with high purity was synthesized using TiH2,Si and C powders with mole ratio of Ti to Si to C being3:1.2:2by reactive synthesis method.The corrosion behaviors of porous Ti3SiC2in nitric acid and aqua regia were investigated byimmersing test.Scanning electron microscope(SEM),X-ray diffractometer(XRD),energy dispersive spectrometer(EDS)and X-rayphotoelectron spectroscopy(XPS)were used to analyze the morphology,compositions and element contents of the samples beforeand after corrosion to determine the corrosion product and corrosion mechanism.The mass loss values of porous Ti3SiC2are26.9and132.5μg/cm2,respectively after immersing in nitric acid and aqua regia for600h.The results indicate that Ti3SiC2transforms toTi5Si3which has better corrosion resistance in nitric acid and aqua regia with mass loss values of9.34and7.06μg/cm2under thesame immersing time,respectively.The dramatic dissolution of porous Ti3SiC2in the acids is due to its special microstructure.展开更多
基金Projects(51604305,51504296) supported by the National Natural Science Foundation of ChinaProject(2016M592445) supported by the China Postdoctoral Science FoundationProject(169715) supported by the Postdoctoral Science Foundation of Central South University,China
文摘Porous Ti3SiC2with high purity was synthesized using TiH2,Si and C powders with mole ratio of Ti to Si to C being3:1.2:2by reactive synthesis method.The corrosion behaviors of porous Ti3SiC2in nitric acid and aqua regia were investigated byimmersing test.Scanning electron microscope(SEM),X-ray diffractometer(XRD),energy dispersive spectrometer(EDS)and X-rayphotoelectron spectroscopy(XPS)were used to analyze the morphology,compositions and element contents of the samples beforeand after corrosion to determine the corrosion product and corrosion mechanism.The mass loss values of porous Ti3SiC2are26.9and132.5μg/cm2,respectively after immersing in nitric acid and aqua regia for600h.The results indicate that Ti3SiC2transforms toTi5Si3which has better corrosion resistance in nitric acid and aqua regia with mass loss values of9.34and7.06μg/cm2under thesame immersing time,respectively.The dramatic dissolution of porous Ti3SiC2in the acids is due to its special microstructure.