Performances of belite-rich Portland cement, or HBC （high belite cement）, and the resultant concrete are introduced by comparing with that of alite based PC （Portland cement） and concrete. The comparison study of ...Performances of belite-rich Portland cement, or HBC （high belite cement）, and the resultant concrete are introduced by comparing with that of alite based PC （Portland cement） and concrete. The comparison study of cement properties indicates that HBC possesses the properties of less water demand for normal consistency, better compatibility with water reducer, higher later age strength after 28-day under standard curing temperature of 20 ℃, unique strength gain under elevated curing temperatures of 38-70 ℃, lower hydration heat evolution and temperature rise, lower drying shrinkage and excellent resistance to sulphate attack. These results have been demonstrated by the comparison performance evaluation of concretes prepared by HBC and PC in terms of workability, physical mechanical properties and durability when making high performance high strength concrete and massive concrete.展开更多
Spent fuel reprocessing plays a pivotal role in achieving efficient recycling of nuclear fuel.Among thedifferent forms of failure encountered in spent fuel reprocessing,tribocorrosion stands out as a critical concern....Spent fuel reprocessing plays a pivotal role in achieving efficient recycling of nuclear fuel.Among thedifferent forms of failure encountered in spent fuel reprocessing,tribocorrosion stands out as a critical concern.Herein,the tribocorrosion behavior,as well as the corrosion behavior,of 304L stainless steel(SS)in high-temperatureconcentrated nitric acid was investigated.The results indicated that 304L SS formed a thin(1.54 nm)and stable passivefilm on the surface,imparting high resistance to nitric acid corrosion.Meanwhile,it was found that the synergistic effectbetween corrosion and wear accounted for a high total tribocorrosion weight loss of over 85%,implying the dominantrole of the synergistic effect in the tribocorrosion process.Furthermore,the wear of 304L SS in deionized water revealedboth abrasive and adhesive wear characterizations,whereas the tribocorrosion in nitric acid only exhibited abrasive wearfeature.Eventually,the tribocorrosion and corrosion models of 304L SS in hot concentrated nitric acid were proposedbased on the comprehensive experimental findings.展开更多
文摘Performances of belite-rich Portland cement, or HBC （high belite cement）, and the resultant concrete are introduced by comparing with that of alite based PC （Portland cement） and concrete. The comparison study of cement properties indicates that HBC possesses the properties of less water demand for normal consistency, better compatibility with water reducer, higher later age strength after 28-day under standard curing temperature of 20 ℃, unique strength gain under elevated curing temperatures of 38-70 ℃, lower hydration heat evolution and temperature rise, lower drying shrinkage and excellent resistance to sulphate attack. These results have been demonstrated by the comparison performance evaluation of concretes prepared by HBC and PC in terms of workability, physical mechanical properties and durability when making high performance high strength concrete and massive concrete.
基金Projects(52101105,52373321)supported by the National Natural Science Foundation of ChinaProject(2023-PY03)supported by the IMR Innovation Fund,ChinaProject(CNNC-LCKY-202274)supported by the LingChuang Research Project of China National Nuclear Corporation。
文摘Spent fuel reprocessing plays a pivotal role in achieving efficient recycling of nuclear fuel.Among thedifferent forms of failure encountered in spent fuel reprocessing,tribocorrosion stands out as a critical concern.Herein,the tribocorrosion behavior,as well as the corrosion behavior,of 304L stainless steel(SS)in high-temperatureconcentrated nitric acid was investigated.The results indicated that 304L SS formed a thin(1.54 nm)and stable passivefilm on the surface,imparting high resistance to nitric acid corrosion.Meanwhile,it was found that the synergistic effectbetween corrosion and wear accounted for a high total tribocorrosion weight loss of over 85%,implying the dominantrole of the synergistic effect in the tribocorrosion process.Furthermore,the wear of 304L SS in deionized water revealedboth abrasive and adhesive wear characterizations,whereas the tribocorrosion in nitric acid only exhibited abrasive wearfeature.Eventually,the tribocorrosion and corrosion models of 304L SS in hot concentrated nitric acid were proposedbased on the comprehensive experimental findings.