钛合金电子束焊缝金属微观结构的TEM观察

本文对不同电子束扫描频率的 ＴＣ４ 钛合金焊缝金属微观结构进行了透射电镜观察。研究结果表明，电子束扫描频率对钛合金焊缝金属微观结构有很大影响。电子束扫描作用在焊接凝固前沿的动压力以及焊接凝固过程的稳定性的综合作用，直接影响 ＴＣ４

Effect of VC/Cr_3C_2 on microstructure and mechanical properties of Ti(C,N)-based cermets

Effects of VC/Cr3C2 on the microstructure and mechanical properties of Ti（C,N）-based cermets were studied. The microstructure was investigated by means of optical microscopy, X-ray diffractometry as well as scanning electron microscopy in combination with energy dispersive spectrometry. Mechanical properties, such as transverse rupture strength, hardness and fracture toughness, were measured. The results show that there are black core-grey rim structure and white core-grey rim structure in the microstructure. The grains become fine due to the VC/Cr3C2, and the grains of cermet added with 0.75VC/0.25Cr3C2 are refined most remarkably. The black core becomes finer with the increase of VC addition and rim phase becomes thicker with the decrease of Cr3C2 addition. The porosity increases with the increase of VC addition in VC/Cr3C2. Compared with the cermet free of VC/Cr3C2, the transverse rupture strength and hardness of cermets with VC/Cr3C2 are both improved, and the maximum values are both found for the cermet with 0.25VC/0.75Cr3C2. The fracture toughness can be effectively promoted by adding VC/Cr3C2 with an appropriate ratio of VC to Cr3C2, and the maximum value is found for the cermet with 0.5VC/0.5Cr3C2.

Effect of joining temperature on microstructure and properties of diffusion bonded Mg/Al joints

The joining of AZ31B Mg alloy to 6061 Al alloy was investigated at different joining temperatures by vacuum diffusion bonding method. The microstructures of Mg/Al dissimilar joints were studied by means of optical microscopy （OM）, scanning electron microscopy （SEM） and energy dispersive X-ray （EDX）. The results show that the thickness of each layer in the diffusion zone increases with the increase of joining temperature, and the microstructure changes obviously. At joining temperature of 440 °C, the diffusion zone is composed of Mg2Al3 layer and Mg17Al12 layer. At joining temperatures of 460 and 480 °C, the diffusion zone is composed of Mg2Al3 layer, Mg17Al12 layer, eutectic layer of Mg17Al12 and Mg-based solid solution. The width of high-hardness zone in the joint increases with increasing joining temperature, and the micro-hardnesses at different locations in the diffusion zone are significantly different. The joining temperature of 440 °C offers the highest tensile strength of 37 MPa, and the corresponding joint exhibits brittle fracture at the intermetallic compound layer of Mg17Al12.

Microstructures and properties of A356-10%SiC particle composite castings at different solidification pressures

A356-based metal matrix composites with 10% SiC particles of 10 rtm were fabricated by stir casting and direct squeeze casting process under applied pressures of 0.1 （gravity）, 25, 50 and 75 MPa. The microstructures and mechanical properties of the as-cast and T6 heat-treated castings were investigated. The results show that as the applied pressures increase, the casting defects as particle-porosity clusters reduce and the incorporation between the particles and matrix can be improved. The tensile strength, hardness, and coefficients of thermal expansion （CTE） increase with the increase of the pressures. Compared with the as-cast composite castings, the tensile strength and hardness of the heat-treated casting are improved whereas CTEs tend to decrease in T6-treated condition. For the gravity cast composites, there are some particle-porosity clusters on the fracture surface, and the clusters are hardly detected on the fracture surface of the samples solidified at the external pressures. Different fracture behaviors are found between the composites solidified at the gravity and imposed pressures.

Directional solidification and characterization of NiAl-9Mo eutectic alloy

Ni-45.5Al-9Mo （mole fraction,%） alloy was directionally solidified with a constant temperature gradient （GL=334 K/cm） and growth rates ranging from 2 to 300 μm/s using a Bridgman type crystal growing facility with liquid metal cooling （LMC） technique. The effect of growth rate （v） on the solidified microstructures such as rod spacing （λ）, rod size （d） and rod volume fraction was experimentally investigated. Two types of the solidified interfaces, planar and cellular, were identified. On the condition of both planar and cellular eutectic microstructures, the relationships between λ, d and v were given as： λv1/2=5.90 μm·μm1/2·s1/2 and dv1/2=2.18μm·μm1/2·s1/2, respectively. It was observed that the volume fraction of Mo phase could be adjusted in a certain range. The variation of phase volume fraction was attributed to undercooling increase and the growth characteristics of the individual constituent phases during the eutectic growth.