The powders of Mo2FeB2 cermet were prepared with Mo powders, Fe-B alloy powders and Fe powders as raw materials. Mo2FeB2 cermet coatings were prepared on Q235 steel by reactive thermal spraying （RTS） method and heat...The powders of Mo2FeB2 cermet were prepared with Mo powders, Fe-B alloy powders and Fe powders as raw materials. Mo2FeB2 cermet coatings were prepared on Q235 steel by reactive thermal spraying （RTS） method and heated at 1 000 ℃ in vacuum oven of 1 kPa for 5 h. The properties of coatings were investigated. The results indicate that Fe2B appears after milling for 15 h in the powder at room temperature, a part of ternary borides （Mo2FeB2） are generated in powder sintered at 900 ℃. The coatings are composed of the major phases Mo2FeB2 and a-Fe, a little of Fe203, FeO and some pores. The bonding strength between the substrate and the ceramic coating is 32.73 MPa, the thermal-shock times is about 43 and the wear resistance is enhanced by approximately 5.28 times compared with that of the substrate, respectively. The comprehensive properties of Mo2FeB2 cermet coatings can be imoroved further after vacuum heat-treatment at 1 000 ℃ for 5 h.展开更多
The effects of grit blasting (GB),shot peening (SP) pretreatment and high velocity oxygen fuel(HVOF) sprayed WC-17Co cermet coating on the fatigue properties of the novel ultra-high strength TC21 titanium alloy were i...The effects of grit blasting (GB),shot peening (SP) pretreatment and high velocity oxygen fuel(HVOF) sprayed WC-17Co cermet coating on the fatigue properties of the novel ultra-high strength TC21 titanium alloy were investigated with a rotating bending fatigue test machine.The basic properties and surface integrity of the coating were investigated by using X-ray diffraction (XRD),surface roughness meter,microscopic hardness tester,scanning electron microscopy (SEM) and X-ray stress test instruments.The results showed that the residual compressive stress could be introduced into the surface of TC21 alloy by GB and SP pretreatment,and that HVOF sprayed WC-17Co coating was compactly bonded with TC21 alloy substrate and it significantly improved the surface hardness of the substrate.However,there was a certain residual tensile stress in the sublayer of the coating.SP could significantly increase fatigue resistance of TC21 alloy due to the surface residual compressive stress.There was no significant effect on fatigue resistance by GB treatment due to the offset between the influence of surface residual compressive stress and the surface notch effect.The fatigue resistance of TC21 alloy was significantly reduced by HVOF WC-17Co coating prepared with GB pretreatment.This could be attributed to the relaxation of surface residual compressive stress during the HVOF heating process,pore defects and residual tensile stress distribution in the WC-17Co coating with low toughness,and the surface notch induced by GB.The fatigue resistance of TC21 alloy was slightly reduced by HVOF WC-17Co coating prepared with SP pretreatment.This was attributed to the offset between the advantage effect by SP and disadvantageous effect of WC-17Co coating and high temperature factor during the HVOF process.展开更多
基金Project(2007T069)supported by Liaoning Education Department Innovation Team,China
文摘The powders of Mo2FeB2 cermet were prepared with Mo powders, Fe-B alloy powders and Fe powders as raw materials. Mo2FeB2 cermet coatings were prepared on Q235 steel by reactive thermal spraying （RTS） method and heated at 1 000 ℃ in vacuum oven of 1 kPa for 5 h. The properties of coatings were investigated. The results indicate that Fe2B appears after milling for 15 h in the powder at room temperature, a part of ternary borides （Mo2FeB2） are generated in powder sintered at 900 ℃. The coatings are composed of the major phases Mo2FeB2 and a-Fe, a little of Fe203, FeO and some pores. The bonding strength between the substrate and the ceramic coating is 32.73 MPa, the thermal-shock times is about 43 and the wear resistance is enhanced by approximately 5.28 times compared with that of the substrate, respectively. The comprehensive properties of Mo2FeB2 cermet coatings can be imoroved further after vacuum heat-treatment at 1 000 ℃ for 5 h.
基金supported by the National Natural Science Foundation of China (Grant Nos. 51171154 and 51101127)
文摘The effects of grit blasting (GB),shot peening (SP) pretreatment and high velocity oxygen fuel(HVOF) sprayed WC-17Co cermet coating on the fatigue properties of the novel ultra-high strength TC21 titanium alloy were investigated with a rotating bending fatigue test machine.The basic properties and surface integrity of the coating were investigated by using X-ray diffraction (XRD),surface roughness meter,microscopic hardness tester,scanning electron microscopy (SEM) and X-ray stress test instruments.The results showed that the residual compressive stress could be introduced into the surface of TC21 alloy by GB and SP pretreatment,and that HVOF sprayed WC-17Co coating was compactly bonded with TC21 alloy substrate and it significantly improved the surface hardness of the substrate.However,there was a certain residual tensile stress in the sublayer of the coating.SP could significantly increase fatigue resistance of TC21 alloy due to the surface residual compressive stress.There was no significant effect on fatigue resistance by GB treatment due to the offset between the influence of surface residual compressive stress and the surface notch effect.The fatigue resistance of TC21 alloy was significantly reduced by HVOF WC-17Co coating prepared with GB pretreatment.This could be attributed to the relaxation of surface residual compressive stress during the HVOF heating process,pore defects and residual tensile stress distribution in the WC-17Co coating with low toughness,and the surface notch induced by GB.The fatigue resistance of TC21 alloy was slightly reduced by HVOF WC-17Co coating prepared with SP pretreatment.This was attributed to the offset between the advantage effect by SP and disadvantageous effect of WC-17Co coating and high temperature factor during the HVOF process.