By the directional solidification of metal-gas eutectic method（GASAR）,porous Cu-Mn alloy with oriented pores was fabricated successfully.The variation of pore structure was studied by experiments.The results show th...By the directional solidification of metal-gas eutectic method（GASAR）,porous Cu-Mn alloy with oriented pores was fabricated successfully.The variation of pore structure was studied by experiments.The results show that the pore structure is primarily dependent on the solidification mode（planar,columnar cellular,columnar dendritic,equiaxed dendritic）,which is controlled by the solidification process.By numerical simulation,it is noted that along with solidification,the solidification mode of the alloy transforms from cellular to columnar dendritic and finally to equiaxed dendritic.Through increasing melt temperature and mold preheating,the range of equiaxed dendrite could be decreased,which helps to extend the region of oriented pore structure.展开更多
Supported PtCu alloys have been broadly applied in heterogeneous catalysis and electrocatalysis owing to their excellent catalytic performance and high CO tolerance. It is important to analyze the outermost surface c...Supported PtCu alloys have been broadly applied in heterogeneous catalysis and electrocatalysis owing to their excellent catalytic performance and high CO tolerance. It is important to analyze the outermost surface composition of the supported alloy nanoparticles to understand the nature of the catalytically active sites. In this paper, homogeneous face-centered cubic PtCu nanoparticles with a narrow particle size distribution were successfully fabricated and dispersed on a high-surface-area Ti〇2 powder support. The samples were oxidized and reduced in situ and then introduced into the ultrahigh vacuum chamber to measure the topmost surface composition by high-sensitivity low-energy ion scattering spectroscopy, and to determine the oxidation states of the elements by X-ray photoelectron spectroscopy. The surface composition and morphology, elemental distribu-tion, and oxidation states of the components were found to be significantly affected by the support and treatment conditions. The PtCu is de-alloyed upon oxidation with CuO wetting on the TiO2 sur-face and re-alloyed upon reduction. Phase diagrams of the surface composition and the bulk com-position were plotted and compared for the supported and unsupported materials.展开更多
The microstructure and its effects on the high temperature mechanical behavior of Cu-2.7%Al_2O_3 （volume fraction） dispersion strengthened copper （ADSC） alloy were investigated. The results indicate that fine alum...The microstructure and its effects on the high temperature mechanical behavior of Cu-2.7%Al_2O_3 （volume fraction） dispersion strengthened copper （ADSC） alloy were investigated. The results indicate that fine alumina particles are uniformly distributed in the copper matrix, while a few coarse ones are distributed on the grain boundaries. Tensile tests results show that Hall-Petch mechanism is the main contribution to the yield strength of ADSC alloy at room temperature. Its high temperature strength is attributed to the strong pinning effects of alumina particles on the grain and sub-grain boundaries with dislocations. The ultimate tensile strength can reach 237 MPa and the corresponding yield strength reaches 226 MPa at 700℃. Tensile fracture morphology indicates that the ADSC alloy shows brittleness at elevated temperatures. Creep tests results demonstrate that the steady state creep rates at 400 ℃ are lower than those at 700 ℃. The stress exponents at 400 ℃ and 700℃ are 7 and 5, respectively, and the creep strain rates of the ADSC alloy are controlled by dislocation core diffusion and lattice diffusion.展开更多
A physically based numerical model to predict the microstructure evolution and yield strength of high Cu-to-Mg mass ratio Al-Cu-Mg-Ag alloys during the whole ageing process was developed.A thermodynamically-based prec...A physically based numerical model to predict the microstructure evolution and yield strength of high Cu-to-Mg mass ratio Al-Cu-Mg-Ag alloys during the whole ageing process was developed.A thermodynamically-based precipitation model,employing the classical nucleation and growth theories,was adapted to deal with the precipitation kinetics (evolution of radius and volume fraction of precipitates for Ω phase) of aged Al-Cu-Mg-Ag alloys.The model gives an estimation of the precipitation kinetics (evolution of radius and density of precipitates for both θ' and Ω phases) of the alloy.The strengthening model based on Orowan mechanism was deduced.The microstructural development and strength predictions of the model are generally in good agreement with the experimental data.展开更多
The high temperature(HT)thermal stability and mechanical properties of Al-5%Cu(AC)and Al-5%Cu-0.2%Mn-0.2 Zr%(ACMZ)alloys from 573 to 673 K were systematically studied.The results displayed that micro-alloying addition...The high temperature(HT)thermal stability and mechanical properties of Al-5%Cu(AC)and Al-5%Cu-0.2%Mn-0.2 Zr%(ACMZ)alloys from 573 to 673 K were systematically studied.The results displayed that micro-alloying additions of Zr and Mn elements have presented a significant role in stabilizing the main strengthening metastableθ′precipitates at a temperature as high as 573 K.Simultaneously,the HT tensile test demonstrated that ACMZ alloy retained their strength of(88.6±8.8)MPa,which was much higher than that of AC alloy((32.5±0.8)MPa)after the thermal exposure at 573 K for 200 h.Finally,the underlying mechanisms of strength and ductility enhancement mechanism of the ACMZ alloy at HT were discussed in detail.展开更多
The exploration of efficient electrocatalysts for the reduction of CO2 to C2H4 is of significant importance but is also a challenging subject.Cu-based bimetallic catalysts are extremely promising for efficient CO2 red...The exploration of efficient electrocatalysts for the reduction of CO2 to C2H4 is of significant importance but is also a challenging subject.Cu-based bimetallic catalysts are extremely promising for efficient CO2 reduction.In this work,we synthesize a series of porous bimetallic Cu–Sb alloys with different compositions for the catalytic reduction of CO2 to C2H4.It is demonstrated that the alloy catalysts are much more efficient than the pure Cu catalyst.The performance of the alloy catalysts depended strongly on the composition.Further,the alloy with a Cu:Sb ratio of 10:1 yielded the best results;it exhibited a high C2H4 Faradaic efficiency of 49.7%and a high current density of 28.5 mA cm?2 at?1.19 V vs.a reversible hydrogen electrode(RHE)in 0.1 M KCl solution.To the best of our knowledge,the electrocatalytic reduction of CO2 to C2H4 using Cu–Sb alloys as catalysts has not been reported.The excellent performance of the porous alloy catalyst is attributed to its favorable electronic configuration,large surface area,high CO2 adsorption rate,and fast charge transfer rate.展开更多
基金Project(U0837603)supported by the NSFC-Yunnan Joint Foundation of ChinaProject(2092017)supported by the Natural Science Foundation of Beijing,China
文摘By the directional solidification of metal-gas eutectic method（GASAR）,porous Cu-Mn alloy with oriented pores was fabricated successfully.The variation of pore structure was studied by experiments.The results show that the pore structure is primarily dependent on the solidification mode（planar,columnar cellular,columnar dendritic,equiaxed dendritic）,which is controlled by the solidification process.By numerical simulation,it is noted that along with solidification,the solidification mode of the alloy transforms from cellular to columnar dendritic and finally to equiaxed dendritic.Through increasing melt temperature and mold preheating,the range of equiaxed dendrite could be decreased,which helps to extend the region of oriented pore structure.
基金supported by the National Basic Research Program of China(973 Program,2013CB933102)the National Natural Science Foundation of China(21273178,21573180,91545204)Xiamen-Zhuoyue Biomass Energy Co.Ltd~~
文摘Supported PtCu alloys have been broadly applied in heterogeneous catalysis and electrocatalysis owing to their excellent catalytic performance and high CO tolerance. It is important to analyze the outermost surface composition of the supported alloy nanoparticles to understand the nature of the catalytically active sites. In this paper, homogeneous face-centered cubic PtCu nanoparticles with a narrow particle size distribution were successfully fabricated and dispersed on a high-surface-area Ti〇2 powder support. The samples were oxidized and reduced in situ and then introduced into the ultrahigh vacuum chamber to measure the topmost surface composition by high-sensitivity low-energy ion scattering spectroscopy, and to determine the oxidation states of the elements by X-ray photoelectron spectroscopy. The surface composition and morphology, elemental distribu-tion, and oxidation states of the components were found to be significantly affected by the support and treatment conditions. The PtCu is de-alloyed upon oxidation with CuO wetting on the TiO2 sur-face and re-alloyed upon reduction. Phase diagrams of the surface composition and the bulk com-position were plotted and compared for the supported and unsupported materials.
基金Project(51271203)supported by the National Natural Science Foundation of Chinathe PPP project between the CSC(China Scholarship Council)and the DAAD(German Academic Exchange Service)+2 种基金Project(11JJ2025)supported by Hunan Provincial Natural Science Foundation of ChinaProject(YSZN2013CL06)supported by the Nonferrous Metals Science Foundation of HNG-CSUProject supported by the Aid program for Science Technology Innovative Research Team in Higher Educational Institutions of Hunan Province,China
文摘The microstructure and its effects on the high temperature mechanical behavior of Cu-2.7%Al_2O_3 （volume fraction） dispersion strengthened copper （ADSC） alloy were investigated. The results indicate that fine alumina particles are uniformly distributed in the copper matrix, while a few coarse ones are distributed on the grain boundaries. Tensile tests results show that Hall-Petch mechanism is the main contribution to the yield strength of ADSC alloy at room temperature. Its high temperature strength is attributed to the strong pinning effects of alumina particles on the grain and sub-grain boundaries with dislocations. The ultimate tensile strength can reach 237 MPa and the corresponding yield strength reaches 226 MPa at 700℃. Tensile fracture morphology indicates that the ADSC alloy shows brittleness at elevated temperatures. Creep tests results demonstrate that the steady state creep rates at 400 ℃ are lower than those at 700 ℃. The stress exponents at 400 ℃ and 700℃ are 7 and 5, respectively, and the creep strain rates of the ADSC alloy are controlled by dislocation core diffusion and lattice diffusion.
基金Project(2005CB623705-04) supported by the National Basic Research Program of ChinaProject(1810-752300020) supported by Central South University and Ministry of Education of China for the Domestic Exchange PhD student
文摘A physically based numerical model to predict the microstructure evolution and yield strength of high Cu-to-Mg mass ratio Al-Cu-Mg-Ag alloys during the whole ageing process was developed.A thermodynamically-based precipitation model,employing the classical nucleation and growth theories,was adapted to deal with the precipitation kinetics (evolution of radius and volume fraction of precipitates for Ω phase) of aged Al-Cu-Mg-Ag alloys.The model gives an estimation of the precipitation kinetics (evolution of radius and density of precipitates for both θ' and Ω phases) of the alloy.The strengthening model based on Orowan mechanism was deduced.The microstructural development and strength predictions of the model are generally in good agreement with the experimental data.
基金financial supports from the National Natural Science Foundation of China(No.52071207)the China Postdoctoral Science Foundation(Nos.2019TQ0193,2019M661497)+1 种基金the National Key Research and Development Program of China(No.2018YFB1106302)Anhui Provincial Engineering Research Center of Aluminum Matrix Composites,China(No.2017WAMC002)。
文摘The high temperature(HT)thermal stability and mechanical properties of Al-5%Cu(AC)and Al-5%Cu-0.2%Mn-0.2 Zr%(ACMZ)alloys from 573 to 673 K were systematically studied.The results displayed that micro-alloying additions of Zr and Mn elements have presented a significant role in stabilizing the main strengthening metastableθ′precipitates at a temperature as high as 573 K.Simultaneously,the HT tensile test demonstrated that ACMZ alloy retained their strength of(88.6±8.8)MPa,which was much higher than that of AC alloy((32.5±0.8)MPa)after the thermal exposure at 573 K for 200 h.Finally,the underlying mechanisms of strength and ductility enhancement mechanism of the ACMZ alloy at HT were discussed in detail.
文摘The exploration of efficient electrocatalysts for the reduction of CO2 to C2H4 is of significant importance but is also a challenging subject.Cu-based bimetallic catalysts are extremely promising for efficient CO2 reduction.In this work,we synthesize a series of porous bimetallic Cu–Sb alloys with different compositions for the catalytic reduction of CO2 to C2H4.It is demonstrated that the alloy catalysts are much more efficient than the pure Cu catalyst.The performance of the alloy catalysts depended strongly on the composition.Further,the alloy with a Cu:Sb ratio of 10:1 yielded the best results;it exhibited a high C2H4 Faradaic efficiency of 49.7%and a high current density of 28.5 mA cm?2 at?1.19 V vs.a reversible hydrogen electrode(RHE)in 0.1 M KCl solution.To the best of our knowledge,the electrocatalytic reduction of CO2 to C2H4 using Cu–Sb alloys as catalysts has not been reported.The excellent performance of the porous alloy catalyst is attributed to its favorable electronic configuration,large surface area,high CO2 adsorption rate,and fast charge transfer rate.