A novel micro-nano Ti−10Cu−10Ni−8Al−8Nb−4Zr−1.5Hf filler was used to vacuum braze Ti−47Al−2Nb−2Cr−0.15B alloy at 1160−1220℃ for 30 min.The interfacial microstructure and formation mechanism of TiAl joints and the rel...A novel micro-nano Ti−10Cu−10Ni−8Al−8Nb−4Zr−1.5Hf filler was used to vacuum braze Ti−47Al−2Nb−2Cr−0.15B alloy at 1160−1220℃ for 30 min.The interfacial microstructure and formation mechanism of TiAl joints and the relationships among brazing temperature,interfacial microstructure and joint strength were emphatically investigated.Results show that the TiAl joints brazed at 1160 and 1180℃ possess three interfacial layers and mainly consist of α_(2)-Ti_(3)Al,τ_(3)-Al_(3)NiTi_(2) and Ti_(2)Ni,but the brazing seams are no longer layered and Ti_(2)Ni is completely replaced by the uniformly distributed τ_(3)-Al_(3)NiTi_(2) at 1200 and 1220℃ due to the destruction of α_(2)-Ti_(3)Al barrier layer.This transformation at 1200℃ obviously improves the tensile strength of the joint and obtains a maximum of 343 MPa.Notably,the outward diffusion of Al atoms from the dissolution of TiAl substrate dominates the microstructure evolution and tensile strength of the TiAl joint at different brazing temperatures.展开更多
Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental...Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental observations, the molten interlayer reacts vigorously with base metals, forming several continuous reaction layers. The typical interfacial microstructure of the joint can be expressed as GH99/（Ni,Cr）ss（γ）/TiNi（β2）＋TiNi2Al（τ4）＋Ti2Ni（δ）/δ＋Ti3Al（α2）＋Al3NiTi2（τ3）/α2＋τ3/TiAl. The maximum shear strength is 258 MPa for the specimen brazed at 1000°C for 10 min. Higher brazing temperature or longer brazing time causes coarsening of the phases in the brazing seam and formation of brittle intermetallic layer, which greatly depresses the shear strength of the joints.展开更多
A series of Al?Si?Ge filler metals were studied for brazing aluminum. The microstructures and properties of the filler metals were investigated systematically. The results show that the liquidus temperature of Al?Si?G...A series of Al?Si?Ge filler metals were studied for brazing aluminum. The microstructures and properties of the filler metals were investigated systematically. The results show that the liquidus temperature of Al?Si?Ge filler metals drops from 592 to 519 °C as the content of Ge increases from 0 to 30% (mass fraction). As the content of Ge increases, bright eutectic Ge forms. However, as the Ge content exceeds 20%, the aggregation growth of the eutectic structure tends to happen and coarsened primary Si?Ge particle forms, which is detrimental to the properties of alloys. The Al?10.8Si?10Ge filler metal has good processability and wettability with the base metal Al. When this filler metal is used to braze 1060 aluminum, the complete joint can be achieved. Furthermore, the shear strength test results show that the fracture of brazed joint with Al?10.8Si?10Ge filler metal occurs in the base metal.展开更多
The influence of brazing temperature and brazing time on the microstructure and shear strength ofγ-TiAl/GH536 joints brazed with Ti-Zr-Cu-Ni-Fe-Co-Mo filler was investigated using SEM,EDS,XRD and universal testing ma...The influence of brazing temperature and brazing time on the microstructure and shear strength ofγ-TiAl/GH536 joints brazed with Ti-Zr-Cu-Ni-Fe-Co-Mo filler was investigated using SEM,EDS,XRD and universal testing machine.Results show that all the brazed joints mainly consist of four reaction layers regardless of the brazing temperature and brazing time.The thickness of the brazed seam and the average shear strength of the joint increase firstly and then decrease with brazing temperature in the range of 1090-1170℃and brazing time varying from 0 to 20 min.The maximum shear strength of 262 MPa is obtained at 1150℃for 10 min.The brittle Al3NiTi2 and TiNi3 intermetallics are the main controlling factors for the crack generation and deterioration of joint strength.The fracture surface is characterized as typical cleavage fracture and it mainly consists of massive brittle Al3NiTi2 intermetallics.展开更多
基金the National Natural Science Foundation of China(No.51865012)the Natural Science Foundation of Jiangxi Province,China(No.20202BABL204040)+3 种基金the Open Foundation of National Engineering Research Center of Near-net-shape Forming for Metallic Materials,China(No.2016005)the Science Foundation of Educational Department of Jiangxi Province,China(No.GJJ170372)the GF Basic Scientific Research Project,China(No.JCKY2020205C002)the Civil Population Supporting Planning and Development Project,China(No.JPPT125GH038).
文摘A novel micro-nano Ti−10Cu−10Ni−8Al−8Nb−4Zr−1.5Hf filler was used to vacuum braze Ti−47Al−2Nb−2Cr−0.15B alloy at 1160−1220℃ for 30 min.The interfacial microstructure and formation mechanism of TiAl joints and the relationships among brazing temperature,interfacial microstructure and joint strength were emphatically investigated.Results show that the TiAl joints brazed at 1160 and 1180℃ possess three interfacial layers and mainly consist of α_(2)-Ti_(3)Al,τ_(3)-Al_(3)NiTi_(2) and Ti_(2)Ni,but the brazing seams are no longer layered and Ti_(2)Ni is completely replaced by the uniformly distributed τ_(3)-Al_(3)NiTi_(2) at 1200 and 1220℃ due to the destruction of α_(2)-Ti_(3)Al barrier layer.This transformation at 1200℃ obviously improves the tensile strength of the joint and obtains a maximum of 343 MPa.Notably,the outward diffusion of Al atoms from the dissolution of TiAl substrate dominates the microstructure evolution and tensile strength of the TiAl joint at different brazing temperatures.
基金Projects (50975062, 51105107, 51021002) supported by the National Natural Science Foundation of ChinaProjects (QC2011C044) supported by the Natural Science Foundation of Heilongjiang Province,China+1 种基金Project (20112302130005) supported by the Specialized Research Fund for the Doctoral Program of Higher Education,ChinaProject (CUGA4130902510) supported by the China Postdoctoral Science Foundation Funded
文摘Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental observations, the molten interlayer reacts vigorously with base metals, forming several continuous reaction layers. The typical interfacial microstructure of the joint can be expressed as GH99/（Ni,Cr）ss（γ）/TiNi（β2）＋TiNi2Al（τ4）＋Ti2Ni（δ）/δ＋Ti3Al（α2）＋Al3NiTi2（τ3）/α2＋τ3/TiAl. The maximum shear strength is 258 MPa for the specimen brazed at 1000°C for 10 min. Higher brazing temperature or longer brazing time causes coarsening of the phases in the brazing seam and formation of brittle intermetallic layer, which greatly depresses the shear strength of the joints.
基金Project(2010A080402014)supported by the Guangdong Provincial Science and Technology Foundation,China
文摘A series of Al?Si?Ge filler metals were studied for brazing aluminum. The microstructures and properties of the filler metals were investigated systematically. The results show that the liquidus temperature of Al?Si?Ge filler metals drops from 592 to 519 °C as the content of Ge increases from 0 to 30% (mass fraction). As the content of Ge increases, bright eutectic Ge forms. However, as the Ge content exceeds 20%, the aggregation growth of the eutectic structure tends to happen and coarsened primary Si?Ge particle forms, which is detrimental to the properties of alloys. The Al?10.8Si?10Ge filler metal has good processability and wettability with the base metal Al. When this filler metal is used to braze 1060 aluminum, the complete joint can be achieved. Furthermore, the shear strength test results show that the fracture of brazed joint with Al?10.8Si?10Ge filler metal occurs in the base metal.
基金Project(51865012)supported by the National Natural Science Foundation of ChinaProject(20202BABL204040)supported by the Natural Science Foundation of Jiangxi Province,China+3 种基金Project(2016005)supported by the Open Foundation of National Engineering Research Center of Near-net-shape Forming for Metallic Materials,ChinaProject(GJJ170372)supported by the Science Foundation of Educational Department of Jiangxi Province,ChinaProject(JCKY2016603C003)supported by the GF Basic Research Project,ChinaProject(JPPT125GH038)supported by the Research Project of Special Furnishment and Part,China。
文摘The influence of brazing temperature and brazing time on the microstructure and shear strength ofγ-TiAl/GH536 joints brazed with Ti-Zr-Cu-Ni-Fe-Co-Mo filler was investigated using SEM,EDS,XRD and universal testing machine.Results show that all the brazed joints mainly consist of four reaction layers regardless of the brazing temperature and brazing time.The thickness of the brazed seam and the average shear strength of the joint increase firstly and then decrease with brazing temperature in the range of 1090-1170℃and brazing time varying from 0 to 20 min.The maximum shear strength of 262 MPa is obtained at 1150℃for 10 min.The brittle Al3NiTi2 and TiNi3 intermetallics are the main controlling factors for the crack generation and deterioration of joint strength.The fracture surface is characterized as typical cleavage fracture and it mainly consists of massive brittle Al3NiTi2 intermetallics.