The separation and recovery of V from chromium-containing vanadate solution were investigated by a cyclic metallurgical process including selective precipitation of vanadium,vanadium leaching and preparation of vanadi...The separation and recovery of V from chromium-containing vanadate solution were investigated by a cyclic metallurgical process including selective precipitation of vanadium,vanadium leaching and preparation of vanadium pentoxide.By adding Ca(OH)_(2) and ball milling,not only the V in the solution can be selectively precipitated,but also the leaching kinetics of the precipitate is significantly improved.The precipitation efficiency of V is 99.59%by adding Ca(OH)_(2) according to Ca/V molar ratio of 1.75:1 into chromium-containing vanadate solution and ball milling for 60 min at room temperature,while the content of Cr in the precipitate is 0.04%.The leaching rate of V reaches 99.35%by adding NaHCO_(3) into water according to NaHCO_(3)/V molar ratio of 2.74:1 to leach V from the precipitate with L/S ratio of 4:1 mL/g and stirring for 60 min at room temperature.The crystals of NH_(4)VO_(3) are obtained by adjusting the leaching solution pH to be 8.0 with CO2 and then adding NH_(4)HCO_(3) according to NH_(4)HCO_(3)/NaVO_(3) molar ratio of 1:1 and stirring for 8 h at room temperature.After filtration,the crystallized solution containing ammonia is reused to leach the precipitate of calcium vanadates,and the leaching efficiency of V is>99%after stirring for 1 h at room temperature.Finally,the product of V_(2)O_(5) with purity of 99.6%is obtained by calcining the crystals at 560℃ for 2 h.展开更多
基金The authors are grateful for the financial supports from the National Natural Science Foundation of China(51974369)the Postgraduate Research Innovation Project of Central South University,China(2019zzts244).
文摘The separation and recovery of V from chromium-containing vanadate solution were investigated by a cyclic metallurgical process including selective precipitation of vanadium,vanadium leaching and preparation of vanadium pentoxide.By adding Ca(OH)_(2) and ball milling,not only the V in the solution can be selectively precipitated,but also the leaching kinetics of the precipitate is significantly improved.The precipitation efficiency of V is 99.59%by adding Ca(OH)_(2) according to Ca/V molar ratio of 1.75:1 into chromium-containing vanadate solution and ball milling for 60 min at room temperature,while the content of Cr in the precipitate is 0.04%.The leaching rate of V reaches 99.35%by adding NaHCO_(3) into water according to NaHCO_(3)/V molar ratio of 2.74:1 to leach V from the precipitate with L/S ratio of 4:1 mL/g and stirring for 60 min at room temperature.The crystals of NH_(4)VO_(3) are obtained by adjusting the leaching solution pH to be 8.0 with CO2 and then adding NH_(4)HCO_(3) according to NH_(4)HCO_(3)/NaVO_(3) molar ratio of 1:1 and stirring for 8 h at room temperature.After filtration,the crystallized solution containing ammonia is reused to leach the precipitate of calcium vanadates,and the leaching efficiency of V is>99%after stirring for 1 h at room temperature.Finally,the product of V_(2)O_(5) with purity of 99.6%is obtained by calcining the crystals at 560℃ for 2 h.