2LiFe1-xCoxPO4-Li3V2（P04）3/C was synthesized using Fel-2xCo2xVO4 as precursor which was prepared by a simple co-precipitation method. 2LiFej-xCoxPO4-Li3V2（PO4）3/C samples were characterized by X-ray diffraction （...2LiFe1-xCoxPO4-Li3V2（P04）3/C was synthesized using Fel-2xCo2xVO4 as precursor which was prepared by a simple co-precipitation method. 2LiFej-xCoxPO4-Li3V2（PO4）3/C samples were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and electrochemical measurements. All 2LiFel-xCoxPOa-Li3V2（PO4）3/C composites are of the similar crystal structure. The XRD analysis and SEM images show that 2LiFe0.96Co0.04PO4-Li3V2（PO4）3/C sample has the best-ordered structure and the smallest particle size. The charge-discharge tests demonstrate that these powders have the best electrochemical properties with an initial discharge capacity of 144.1 mA.h/g and capacity retention of 95.6% after 100 cycles when cycled at a current density of 0.1C between 2.5 and 4.5 V.展开更多
基金Project(51072233) supported by National Natural Science Foundation of China
文摘2LiFe1-xCoxPO4-Li3V2（P04）3/C was synthesized using Fel-2xCo2xVO4 as precursor which was prepared by a simple co-precipitation method. 2LiFej-xCoxPO4-Li3V2（PO4）3/C samples were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and electrochemical measurements. All 2LiFel-xCoxPOa-Li3V2（PO4）3/C composites are of the similar crystal structure. The XRD analysis and SEM images show that 2LiFe0.96Co0.04PO4-Li3V2（PO4）3/C sample has the best-ordered structure and the smallest particle size. The charge-discharge tests demonstrate that these powders have the best electrochemical properties with an initial discharge capacity of 144.1 mA.h/g and capacity retention of 95.6% after 100 cycles when cycled at a current density of 0.1C between 2.5 and 4.5 V.