In order to remove or reduce the negative effect of MgO in calcium aluminate slags, the method of adding Na2O into calcium aluminate slags was studied and its effect on leaching mechanism was also analyzed. The result...In order to remove or reduce the negative effect of MgO in calcium aluminate slags, the method of adding Na2O into calcium aluminate slags was studied and its effect on leaching mechanism was also analyzed. The results show that the alumina leaching efficiency of the calcium aluminate slag increases from 68.73% to 80.86% with Na2O content increasing from 0 to 4% when MgO content is 3%. The XRD results show that the quaternary compound C20A13M3S3 disappears when Na2O content increases to 4%. The addition of Na2O cannot remove the negative effect of MgO on leachability completely. XRD and EDS results indicate that Na2O can come into the lattice of 12CaO·7Al2O3 and promote the formation of 12CaO·7Al2O3展开更多
SiO2 in calcium aluminate slag exists in the form of γ-2CaO·SiO2 which is more stable than β-2CaO·SiO2. However, it is decomposed by sodium carbonate solution during leaching process, leading to the second...SiO2 in calcium aluminate slag exists in the form of γ-2CaO·SiO2 which is more stable than β-2CaO·SiO2. However, it is decomposed by sodium carbonate solution during leaching process, leading to the secondary reaction. The extent of secondary reaction and reaction mechanism of calcium aluminate slag were studied using XRD. The results show that the decomposition rate of γ-2CaO·SiO2 increases with the increase in leaching time and sodium carbonate concentration. The main products of secondary reaction are the mixture of hydrogarnet and sodium hydrate alumina-silicate. SiO2 concentration rises firstly and then drops with the increase of leaching temperature. XRD results indicate that the stable product of secondary reaction at low temperature is hydrogarnet. But hydrogarnet is transformed into sodium hydrate alumina-silicate at high temperature.展开更多
基金Project (51104053) supported by the National Natural Science Foundation of ChinaProject (XL200921) supported by the Foundation Research funds for Hebei University of Science and Technology, China
文摘In order to remove or reduce the negative effect of MgO in calcium aluminate slags, the method of adding Na2O into calcium aluminate slags was studied and its effect on leaching mechanism was also analyzed. The results show that the alumina leaching efficiency of the calcium aluminate slag increases from 68.73% to 80.86% with Na2O content increasing from 0 to 4% when MgO content is 3%. The XRD results show that the quaternary compound C20A13M3S3 disappears when Na2O content increases to 4%. The addition of Na2O cannot remove the negative effect of MgO on leachability completely. XRD and EDS results indicate that Na2O can come into the lattice of 12CaO·7Al2O3 and promote the formation of 12CaO·7Al2O3
基金Project(51104053)supported by the National Natural Science Foundation of ChinaProject(E2012208047)supported by the Natural Science Foundation of Hebei Province,China
文摘SiO2 in calcium aluminate slag exists in the form of γ-2CaO·SiO2 which is more stable than β-2CaO·SiO2. However, it is decomposed by sodium carbonate solution during leaching process, leading to the secondary reaction. The extent of secondary reaction and reaction mechanism of calcium aluminate slag were studied using XRD. The results show that the decomposition rate of γ-2CaO·SiO2 increases with the increase in leaching time and sodium carbonate concentration. The main products of secondary reaction are the mixture of hydrogarnet and sodium hydrate alumina-silicate. SiO2 concentration rises firstly and then drops with the increase of leaching temperature. XRD results indicate that the stable product of secondary reaction at low temperature is hydrogarnet. But hydrogarnet is transformed into sodium hydrate alumina-silicate at high temperature.