The effects of current pulsing on the microstructure, hardness and tensile properties at different temperatures of gas tungsten arc （GTA） weldments of titanium matrix composites were studied. Full-penetration butt j...The effects of current pulsing on the microstructure, hardness and tensile properties at different temperatures of gas tungsten arc （GTA） weldments of titanium matrix composites were studied. Full-penetration butt joints were made with or without current pulsing. Optical microscopy, hardness test and scanning electron microscopy were employed to evaluate the metallurgical characteristics of welded joints. Tensile properties of weldments at different temperatures were studied and correlated with the microstructure. The results exhibit that current pulsing leads to the refinement of the weld microstrucmre and TiB whisker and the redistribution of reinforcements resulting in higher hardness, tensile strength and ductility of weldments in the as-welded condition.展开更多
The properties of the joints are dictated by the nature, distribution, and morphology of the phases formed at the interface. The mechanical properties of brazed joints are well documented in the literature, contrarily...The properties of the joints are dictated by the nature, distribution, and morphology of the phases formed at the interface. The mechanical properties of brazed joints are well documented in the literature, contrarily to their electrochemical behaviour. Thus, the main objective of this study was to understand the influence of the phases formed at the interface on the corrosion behaviour of commercially pure Ti brazed joints, produced by using TiCuNi, eutectic Ag Cu, and Ag filler foils. The electrochemical behaviour of the Ti joints was accessed by open circuit potential and potentiodynamic polarization tests in phosphate buffer saline solution electrolyte at body temperature. Results showed that Ag-based fillers induced susceptibility to micro-galvanic corrosion between the Ag-rich and Ti phases formed at the interface and commercially pure Ti base metal. However, no significant differences were observed between the joint system and the base material when brazing with TiCuNi filler.展开更多
A series of tests was performed with three-point single-edge-notched-bend (SENB) specimens in a condenser material (Titanium alloy). Results show that the J-integral values of welded joint and HAZ are obviously smalle...A series of tests was performed with three-point single-edge-notched-bend (SENB) specimens in a condenser material (Titanium alloy). Results show that the J-integral values of welded joint and HAZ are obviously smaller than those of the base metal. It signifies that the welding process can result in a reduced toughness of Titanium alloy and the effect of crack orientation on toughness value is not negligible for engineering applications. Besides, the J-integral values of L-T direction specimens are much higher than those of L-S ones. The J-integral values of rolled ring are:JC-R>JC-L>JL-R.展开更多
基金Project(51371114)supported by the National Natural Science Foundation of ChinaProject(2012CB619600)supported by the National Basic Research Program of China+1 种基金Project(10SG15)supported by the Dawn Program of Shanghai Education Commission,ChinaProject(12XD1402800)supported by Shanghai Science and Technology Committee,China
文摘The effects of current pulsing on the microstructure, hardness and tensile properties at different temperatures of gas tungsten arc （GTA） weldments of titanium matrix composites were studied. Full-penetration butt joints were made with or without current pulsing. Optical microscopy, hardness test and scanning electron microscopy were employed to evaluate the metallurgical characteristics of welded joints. Tensile properties of weldments at different temperatures were studied and correlated with the microstructure. The results exhibit that current pulsing leads to the refinement of the weld microstrucmre and TiB whisker and the redistribution of reinforcements resulting in higher hardness, tensile strength and ductility of weldments in the as-welded condition.
基金supported by Portuguese FCT,under the reference project UIDB/04436/2020 and M-ERA-NET/0001/2015 project。
文摘The properties of the joints are dictated by the nature, distribution, and morphology of the phases formed at the interface. The mechanical properties of brazed joints are well documented in the literature, contrarily to their electrochemical behaviour. Thus, the main objective of this study was to understand the influence of the phases formed at the interface on the corrosion behaviour of commercially pure Ti brazed joints, produced by using TiCuNi, eutectic Ag Cu, and Ag filler foils. The electrochemical behaviour of the Ti joints was accessed by open circuit potential and potentiodynamic polarization tests in phosphate buffer saline solution electrolyte at body temperature. Results showed that Ag-based fillers induced susceptibility to micro-galvanic corrosion between the Ag-rich and Ti phases formed at the interface and commercially pure Ti base metal. However, no significant differences were observed between the joint system and the base material when brazing with TiCuNi filler.
文摘A series of tests was performed with three-point single-edge-notched-bend (SENB) specimens in a condenser material (Titanium alloy). Results show that the J-integral values of welded joint and HAZ are obviously smaller than those of the base metal. It signifies that the welding process can result in a reduced toughness of Titanium alloy and the effect of crack orientation on toughness value is not negligible for engineering applications. Besides, the J-integral values of L-T direction specimens are much higher than those of L-S ones. The J-integral values of rolled ring are:JC-R>JC-L>JL-R.