用微型催化反应装置结合X射线衍射(XRD)、H2化学吸附、NH3吸附-程序升温脱附(NH3-TPD)和H2-程序升温还原等多种物理化学手段研究了丙烷脱氢负载型Pt Sn Na/SUZ-4催化剂中Na+助剂组分的作用。结果表明,Na+组分可中和SUZ-4载体表面的强酸...用微型催化反应装置结合X射线衍射(XRD)、H2化学吸附、NH3吸附-程序升温脱附(NH3-TPD)和H2-程序升温还原等多种物理化学手段研究了丙烷脱氢负载型Pt Sn Na/SUZ-4催化剂中Na+助剂组分的作用。结果表明,Na+组分可中和SUZ-4载体表面的强酸中心、提高催化剂的Pt金属分散度、抑制脱氢产物的裂解和积炭的生成,从而提高催化剂的丙烷脱氢选择性和反应稳定性。但是过量Na+组分的存在会削弱Sn物种与载体之间的相互作用,使其易被还原,导致催化剂丙烷脱氢活性显著下降。展开更多
The conventional collector for diaspore mineral is oleic acid （OLA）, which is highly insoluble and must be used in high dosage in bauxite flotation. Firstly flotation experiments with every reagent （sodium oleate, ...The conventional collector for diaspore mineral is oleic acid （OLA）, which is highly insoluble and must be used in high dosage in bauxite flotation. Firstly flotation experiments with every reagent （sodium oleate, tween-20）were carried out and it was shown that sodium oleate was an effective diaspore collector, whereas nonionic surfactant tween-20 showed little collectivity. Then experiments were carried out with sodium oleate as the main collector with the addition of tween-20 to study the influences of potentiator on diaspore flotation. It could be seen from the experiments that potentiator had a marked influence on the recovery of diaspore, which was raised by more than 12 % and that addition sequence also affected the flotation behavior. It gave the best results with the reagents mixed thoroughly before added and the best ratio of collector oleic acid and potentiator tween-20 slLood at 10： 1. From the calculation of the ingredients in the sodium oleate solution, at the pH 9, sodium oleate acted with surface of the mineral with the acid-soap polymer [ HOL ~ OL- ]. Zeta potential test showed that the potentiator promoted the absorption of collector on the mineral surface, which lowered zeta potential. As could be seen from surface tension experiments, the addition of potentiator tween-20 lowered the CMC （ critical micelle concentration） value of oleic acid solution, which was equivalent to raise the power of the agents. By the adsorptive capability tests, with the addition of tween-20, the adsorption of oleic acid on diaspore got more.展开更多
文摘用微型催化反应装置结合X射线衍射(XRD)、H2化学吸附、NH3吸附-程序升温脱附(NH3-TPD)和H2-程序升温还原等多种物理化学手段研究了丙烷脱氢负载型Pt Sn Na/SUZ-4催化剂中Na+助剂组分的作用。结果表明,Na+组分可中和SUZ-4载体表面的强酸中心、提高催化剂的Pt金属分散度、抑制脱氢产物的裂解和积炭的生成,从而提高催化剂的丙烷脱氢选择性和反应稳定性。但是过量Na+组分的存在会削弱Sn物种与载体之间的相互作用,使其易被还原,导致催化剂丙烷脱氢活性显著下降。
基金National Key Fundamental Research and Development Program(No.2005cbc237601)
文摘The conventional collector for diaspore mineral is oleic acid （OLA）, which is highly insoluble and must be used in high dosage in bauxite flotation. Firstly flotation experiments with every reagent （sodium oleate, tween-20）were carried out and it was shown that sodium oleate was an effective diaspore collector, whereas nonionic surfactant tween-20 showed little collectivity. Then experiments were carried out with sodium oleate as the main collector with the addition of tween-20 to study the influences of potentiator on diaspore flotation. It could be seen from the experiments that potentiator had a marked influence on the recovery of diaspore, which was raised by more than 12 % and that addition sequence also affected the flotation behavior. It gave the best results with the reagents mixed thoroughly before added and the best ratio of collector oleic acid and potentiator tween-20 slLood at 10： 1. From the calculation of the ingredients in the sodium oleate solution, at the pH 9, sodium oleate acted with surface of the mineral with the acid-soap polymer [ HOL ~ OL- ]. Zeta potential test showed that the potentiator promoted the absorption of collector on the mineral surface, which lowered zeta potential. As could be seen from surface tension experiments, the addition of potentiator tween-20 lowered the CMC （ critical micelle concentration） value of oleic acid solution, which was equivalent to raise the power of the agents. By the adsorptive capability tests, with the addition of tween-20, the adsorption of oleic acid on diaspore got more.