The corrosion and tribocorrosion behaviors of AISI 316 stainless steel and Ti6Al4V alloys sliding against Al2O3 in artificial seawater using a pin-on-disk test rig were investigated. And the synergistic effect between...The corrosion and tribocorrosion behaviors of AISI 316 stainless steel and Ti6Al4V alloys sliding against Al2O3 in artificial seawater using a pin-on-disk test rig were investigated. And the synergistic effect between corrosion and wear was emphatically evaluated. The results show that the open circuit potentials of both alloys drop down to more negative value due to friction. The corrosion current densities obtained under tribocorrosion condition are much higher than those under corrosion-only condition. Friction obviously accelerates the corrosion of the alloys. The wear loss for both alloys is larger in seawater than that in pure water. Wear loss is obviously accelerated by corrosion. And AISI 316 stainless steel is less resistant to sliding damage than Ti6Al4V alloy. The synergistic effect between wear and corrosion is a significant factor for the materials loss in tribocorrosion. In this surface-on-surface contact geometry friction system, the material loss is large but the ratio of wear-accelerated-corrosion to the total wear loss is very low.展开更多
A S-containing additive, sulfuration modified rapeseed oil （named as SRO）, was prepared by chemical modification of rapeseed oil with sulfur compounds. The results indicate that the friction and wear of the magnesiu...A S-containing additive, sulfuration modified rapeseed oil （named as SRO）, was prepared by chemical modification of rapeseed oil with sulfur compounds. The results indicate that the friction and wear of the magnesium alloy-steel tribomates could be effectively reduced by formulating SRO into rapeseed oil lubricant. The friction coefficients and the wear volumes of magnesium alloy decrease with increasing contents of SRO. The surface lubricated with SRO-doped rapeseed oil was characterized by less wear as compared with that lubricated with neat rapeseed oil. The enhanced anti-wear and friction-reducing abilities of rapeseed oil by SRO in the lubrication of magnesium alloy against steel were ascribed to the formation of a composite boundary lubrication film due to the strong adsorption of SRO and rapeseed oil onto the lubricated surfaces and their tribochemical reactions with magnesium alloy.展开更多
Defibrator is a very important machine in the wood industry for producing fiberboard. The refiner plates are the key parts of defibrator that directly act with the wood, and broken easily. The working life of the refi...Defibrator is a very important machine in the wood industry for producing fiberboard. The refiner plates are the key parts of defibrator that directly act with the wood, and broken easily. The working life of the refiner plates is of significance to the wood industry. It may affect refining quality, production efficiency, and power consumption. In this paper, the abrasion resistance of the refiner plate made of different materials, the stainless steels and high chromium cast irons, were tested and compared. The results showed that abrasion resistance of refiner plate made of high chromium cast irons was better than that of the stainless steel materials. Although the two kinds of materials have the same compositions, their abrasion resistances have ap-parent difference. The main reason is that the material microstructures have very important effects on their performance. The refiner plates made of developed high chromium cast irons don抰 demand the complex heat treatment. This can simplify the producing process, save the cost of production, decrease labor strength, and increase the production efficiency.展开更多
Using a closed field unbalanced magnetron sputtering system,the cemented carbide end mills were coated with a CrTiAlN hard coating,which consisted of a Cr adhesive layer,a CrN interlayer and a CrTiAlN top layer.The mi...Using a closed field unbalanced magnetron sputtering system,the cemented carbide end mills were coated with a CrTiAlN hard coating,which consisted of a Cr adhesive layer,a CrN interlayer and a CrTiAlN top layer.The microstructure and mechanical properties of the coating were investigated by X-ray diffraction（XRD）,scanning electron microscopy（SEM）,transmission electron microscopy（TEM）,micro indentation and scratch test.The cutting performance of the coated end mills were conducted by high-speed dry milling hardened steel（P20,HRC 45）.The results indicates that the coating is composed of（Cr,Ti,Al）N columnar grains with nanolayers.The coating exhibits good adhesion to cemented carbide substrate and high microhardness of around 30 GPa.The coated end mills show significant improvement on tool life and much lower cutting force as compared to the uncoated ones.And the related mechanisms were discussed.展开更多
基金Project (LSL-1310) supported by the Open Project of State Key Laboratory of Solid Lubrication,Collaborative Innovation Center of Nonferrous Metals of Henan Province,ChinaProject (51171059) supported by the National Natural Science Foundation of China
文摘The corrosion and tribocorrosion behaviors of AISI 316 stainless steel and Ti6Al4V alloys sliding against Al2O3 in artificial seawater using a pin-on-disk test rig were investigated. And the synergistic effect between corrosion and wear was emphatically evaluated. The results show that the open circuit potentials of both alloys drop down to more negative value due to friction. The corrosion current densities obtained under tribocorrosion condition are much higher than those under corrosion-only condition. Friction obviously accelerates the corrosion of the alloys. The wear loss for both alloys is larger in seawater than that in pure water. Wear loss is obviously accelerated by corrosion. And AISI 316 stainless steel is less resistant to sliding damage than Ti6Al4V alloy. The synergistic effect between wear and corrosion is a significant factor for the materials loss in tribocorrosion. In this surface-on-surface contact geometry friction system, the material loss is large but the ratio of wear-accelerated-corrosion to the total wear loss is very low.
基金Project (50975282) supported by the National Natural Science Foundation of China
文摘A S-containing additive, sulfuration modified rapeseed oil （named as SRO）, was prepared by chemical modification of rapeseed oil with sulfur compounds. The results indicate that the friction and wear of the magnesium alloy-steel tribomates could be effectively reduced by formulating SRO into rapeseed oil lubricant. The friction coefficients and the wear volumes of magnesium alloy decrease with increasing contents of SRO. The surface lubricated with SRO-doped rapeseed oil was characterized by less wear as compared with that lubricated with neat rapeseed oil. The enhanced anti-wear and friction-reducing abilities of rapeseed oil by SRO in the lubrication of magnesium alloy against steel were ascribed to the formation of a composite boundary lubrication film due to the strong adsorption of SRO and rapeseed oil onto the lubricated surfaces and their tribochemical reactions with magnesium alloy.
文摘Defibrator is a very important machine in the wood industry for producing fiberboard. The refiner plates are the key parts of defibrator that directly act with the wood, and broken easily. The working life of the refiner plates is of significance to the wood industry. It may affect refining quality, production efficiency, and power consumption. In this paper, the abrasion resistance of the refiner plate made of different materials, the stainless steels and high chromium cast irons, were tested and compared. The results showed that abrasion resistance of refiner plate made of high chromium cast irons was better than that of the stainless steel materials. Although the two kinds of materials have the same compositions, their abrasion resistances have ap-parent difference. The main reason is that the material microstructures have very important effects on their performance. The refiner plates made of developed high chromium cast irons don抰 demand the complex heat treatment. This can simplify the producing process, save the cost of production, decrease labor strength, and increase the production efficiency.
基金Projects (500120069,U1201245) supported by the National Natural Science Foundation of ChinaProject (2011J2200036) supported by Guangzhou Scientific and Technological Planning Project,ChinaProject supported by Guangdong Province Universities and Colleges Pearl River Scholar Funded Scheme(2012),China
文摘Using a closed field unbalanced magnetron sputtering system,the cemented carbide end mills were coated with a CrTiAlN hard coating,which consisted of a Cr adhesive layer,a CrN interlayer and a CrTiAlN top layer.The microstructure and mechanical properties of the coating were investigated by X-ray diffraction（XRD）,scanning electron microscopy（SEM）,transmission electron microscopy（TEM）,micro indentation and scratch test.The cutting performance of the coated end mills were conducted by high-speed dry milling hardened steel（P20,HRC 45）.The results indicates that the coating is composed of（Cr,Ti,Al）N columnar grains with nanolayers.The coating exhibits good adhesion to cemented carbide substrate and high microhardness of around 30 GPa.The coated end mills show significant improvement on tool life and much lower cutting force as compared to the uncoated ones.And the related mechanisms were discussed.