In order to perfectly reflect the dynamic corrosion of reinforced concrete (RC) cover in practical engineering,an analytic model of non-uniform corrosion induced cracking was presented based on the elastic-plastic fra...In order to perfectly reflect the dynamic corrosion of reinforced concrete (RC) cover in practical engineering,an analytic model of non-uniform corrosion induced cracking was presented based on the elastic-plastic fracture mechanics theory.Comparisons with the published experimental data show that the predictions given by the present model are in good agreement with the results both for natural exposed experiments and short-time indoor tests (the best difference is about 2.7%).Also it obviously provides much better precision than those models under the assumption of uniform corrosion (the maximal improved precision is about 48%).Therefore,it is pointed out that the so-called uniform corrosion models to describe the cover cracking of RC should be adopted cautiously.Finally,the influences of thickness of local rusty layer around the reinforcing steel bar on the critical corrosion-induced crack indexes were investigated.It is found that the thickness of local rusty layer has great effect on the critical mass loss of reinforcing steel,threshold expansion pressure,and time to cover cracking.For local rusty layer thickness with a size of a=0.5 mm,the time to cover cracking will increase by about one times when a/b (a,semi-minor axis;b,semi-major axis) changes from 0.1 to 1 mm.展开更多
An analytical model for predicting the corrosion-induced cracking of concrete cover of reinforced concrete(RC) structures was developed.The effects of influence factors such as practical initial defects,corrosion rate...An analytical model for predicting the corrosion-induced cracking of concrete cover of reinforced concrete(RC) structures was developed.The effects of influence factors such as practical initial defects,corrosion rate,strength and elastic modulus of concrete on the corrosion-induced cracking of concrete cover were investigated.It was found that the size of practical initial defects was the most effective factor.Therefore,improving the compactness of concrete is an effective way to improve the durability of RC structures.It was also demonstrated that the accelerated corrosion tests may be unfavorable in the study of the relationship between cracking time and crack width.展开更多
基金Project(50925829) supported by the National Science Fund for Distinguished Young Scholars of ChinaProject(50908148) supported by the National Natural Science Foundation of ChinaProjects(2009-K4-23,2010-11-33) supported by the Research of Ministry of Housing and Urban Rural Development of China
文摘In order to perfectly reflect the dynamic corrosion of reinforced concrete (RC) cover in practical engineering,an analytic model of non-uniform corrosion induced cracking was presented based on the elastic-plastic fracture mechanics theory.Comparisons with the published experimental data show that the predictions given by the present model are in good agreement with the results both for natural exposed experiments and short-time indoor tests (the best difference is about 2.7%).Also it obviously provides much better precision than those models under the assumption of uniform corrosion (the maximal improved precision is about 48%).Therefore,it is pointed out that the so-called uniform corrosion models to describe the cover cracking of RC should be adopted cautiously.Finally,the influences of thickness of local rusty layer around the reinforcing steel bar on the critical corrosion-induced crack indexes were investigated.It is found that the thickness of local rusty layer has great effect on the critical mass loss of reinforcing steel,threshold expansion pressure,and time to cover cracking.For local rusty layer thickness with a size of a=0.5 mm,the time to cover cracking will increase by about one times when a/b (a,semi-minor axis;b,semi-major axis) changes from 0.1 to 1 mm.
基金Supported by National Natural Science Foundation of China (No. 50908148)Natural Science Foundation for Team Project of Guangdong Province(No. 9351806001000001)+1 种基金Scientific Research Foundation for Returned Overseas Chinese Scholars,Ministry of Education(41 Batch)Open Fund of State Key Laboratory of Coastal and Of fshore Engineering of Dalian University of Technology (No. LP1111)
文摘An analytical model for predicting the corrosion-induced cracking of concrete cover of reinforced concrete(RC) structures was developed.The effects of influence factors such as practical initial defects,corrosion rate,strength and elastic modulus of concrete on the corrosion-induced cracking of concrete cover were investigated.It was found that the size of practical initial defects was the most effective factor.Therefore,improving the compactness of concrete is an effective way to improve the durability of RC structures.It was also demonstrated that the accelerated corrosion tests may be unfavorable in the study of the relationship between cracking time and crack width.