Electron beam welding was carried out between aluminum alloy and steel with Ag interlayer. Seam morphology, structure and mechanical properties of the joints were investigated with different action positions of the el...Electron beam welding was carried out between aluminum alloy and steel with Ag interlayer. Seam morphology, structure and mechanical properties of the joints were investigated with different action positions of the electron beam spot. The results show that with the increment of the beam offset to the silver side from the interface between silver and steel, the seam morphology was improved, and the porosity in the Ag interlayer vanished. A transition layer mainly composed of Ag2Al and Al eutectic was formed at the interface between silver and aluminum, and became thin and spiccato as the beam offset increased. When the beam offset was too large, two IMC layers composed of FeAl and FeAl3 respectively were formed at the interface between steel and Ag interlayer. The optimal beam offset was 0.2 mm, and the maximum tensile strength of the joint was 193 MPa, 88.9% that of the aluminum alloy, and the fracture occurred at the interface between steel and Ag interlayer.展开更多
Effects of laser pulse distance and reinforcing of 5456 aluminum alloy were investigated on laser weldability of Al alloy to duplex stainless steel (DSS) plates. The aluminum alloy plate was reinforced by nickel-base ...Effects of laser pulse distance and reinforcing of 5456 aluminum alloy were investigated on laser weldability of Al alloy to duplex stainless steel (DSS) plates. The aluminum alloy plate was reinforced by nickel-base BNi-2 brazing powder via friction stir processing. The DSS plates were laser welded to the Al5456/BNi-2 composite and also to the Al5456 alloy plates. The welding zones were studied by scanning electron microscopy, X-ray diffractometry, micro-hardness and shear tests. The weld interface layer became thinner from 23 to 5 μm, as the laser pulse distance was increased from 0.2 to 0.5 mm. Reinforcing of the Al alloy modified the phases at interface layer from Al-Fe intermetallic compounds (IMCs) in the DSS/Al alloy weld, to Al-Ni-Fe IMCs in the DSS/Al composite one, since more nickel was injected in the weld pool by BNi-2 reinforcements. This led to a remarkable reduction in crack tendency of the welds and decreased the hardness of the interface layer from ~950 HV to ~600 HV. Shear strengths of the DSS/Al composite welds were significantly increased by ~150%, from 46 to 114 MPa, in comparison to the DSS/Al alloy ones.展开更多
Defect-free butt joints of 3003 Al alloy to mild steel plates with 3 mm thickness were performed using friction stir welding （FSW）. A heat input model reported for similar FSW was simplified and used to investigate ...Defect-free butt joints of 3003 Al alloy to mild steel plates with 3 mm thickness were performed using friction stir welding （FSW）. A heat input model reported for similar FSW was simplified and used to investigate the effects of welding speed, rotation speed and tool shoulder diameter on the microstructure and properties of dissimilar welds. The comparison between microstructure, intermetallics and strength of welds shows the good conformity between the results and the calculated heat input factor （HIF） achieved from the model. The joint strength is controlled by Al/Fe interface at HIF of 0.2-0.4, by TMAZ at HIF of 0.4-0.8 and by intermetallics and/or defects at HIF0.8.展开更多
Commercial pure aluminum and galvanized carbon steel were lap-welded using the weld-brazing(WB)technique.Three types of aluminum filler materials(4043,4047,and 5356) were used for WB.The joint strength and intermetall...Commercial pure aluminum and galvanized carbon steel were lap-welded using the weld-brazing(WB)technique.Three types of aluminum filler materials(4043,4047,and 5356) were used for WB.The joint strength and intermetallic compounds at the interface of three series of samples were analyzed and compared.Depending on the Si content,a variety of ternary Al-Fe-Si intermetallic compounds(IMCs) such as Fe_(4)(Al,Si)_(13),Fe_(2) Al_(8) Si(τ_(5)),and Fe_(2) Al_(9) Si_(2)(τ_(6)) were formed at the interface.Mg element in 5356 filler material cannot contribute to the formation of Al-Fe intermetallic phases due to the positive mixing enthalpy of Mg-Fe.The presence of Mg enhances the hot cracking phenomenon near the Al-Fe intermetallic compound at the interface.Zn coating does not participate in intermetallic formation due to its evaporation during WB.It was concluded that the softening of the base metal in the heat-affected zone rather than the IMCs determines the joint efficiency.展开更多
TIG welding-brazing process with high frequency induction hot wire technology was presented to create joints between 5A06 aluminum alloy and SUS32! stainless steel using ER1100 filler wire with different temperature. ...TIG welding-brazing process with high frequency induction hot wire technology was presented to create joints between 5A06 aluminum alloy and SUS32! stainless steel using ER1100 filler wire with different temperature. The joints were evaluated by mechanical test and microstructural analyses. The welding procedure using hot fiUer wire （400 ℃ ） significantly increases strength stability by 71% and average value of tensile strength by 30. 8 % of the joints, compared with cold wire. The research of microstructures in interfaces and welded seams reveals that using 400 ℃ hot filler wire can decrease the thickness of intermetallic compounds （ IMCs ） from 6 to 3.5 txm approximately, which is the main reason of mechanical property improvement.展开更多
Contact reactive brazing of 6063 Al alloy and 1Cr18Ni9Ti stainless steel was researched by using Cu as interlayer. Effect of brazing time on microstructure of the joints, as well as the dissolution behaviors of Cu int...Contact reactive brazing of 6063 Al alloy and 1Cr18Ni9Ti stainless steel was researched by using Cu as interlayer. Effect of brazing time on microstructure of the joints, as well as the dissolution behaviors of Cu interlayer was analyzed. The results show that the product of reaction zone near 1Cr18Ni9Ti is composed of Fe2Al5, FeAl3 intermetallic compound （IMC）, and Cu-Al IMC; the near by area is composed of Al-Cu eutectic structure with Al （Cu） solid solution. With increasing the brazing time, the thickness of IMC layer at the interface increases, while the width of Al-Cu eutectic structure with Al（Cu） solution decreases. Calculation shows the dissolution rate of Cu interlayer is very fast. The complete dissolution time is about 0.47 s for Cu interlayer with 10 μm in thickness used in this study.展开更多
The driving force for using powder metallurgy(PM)mostly relies on its near net-shape ability and cost-performance ratio.The automotive application is a main market of PM industry,requiring parts with competitive mecha...The driving force for using powder metallurgy(PM)mostly relies on its near net-shape ability and cost-performance ratio.The automotive application is a main market of PM industry,requiring parts with competitive mechanical or functional performance in a mass production scale.As the automobile technology transforms from traditional internal combustion engine vehicles to new energy vehicles,PM technology is undergoing significant changes in manufacturing and materials development.This review outlines the challenges and opportunities generated by the changes in the automotive technology for PM.Low-cost,high-performance and light-weight are critical aspects for future PM materials development.Therefore,the studies on PM lean-alloyed steel,aluminum alloys,and titanium alloy materials were reviewed.In addition,PM soft magnetic composite applied to new energy vehicles was discussed.Then new opportunities for advanced processing,such as metal injection molding(MIM)and additive manufacturing(AM),in automotive industry were stated.In general,the change in automotive industry raises sufficient development space for PM.While,emerging technologies require more preeminent PM materials.Iron-based parts are still the main PM products due to their mechanical performance and low cost.MIM will occupy the growing market of highly flexible and complex parts.AM opens a door for fast prototyping,great flexibility and customizing at low cost,driving weight and assembling reduction.展开更多
基金Project (2010CB731704) supported by the National Basic Research Program of ChinaProject (51075089) supported by the National Natural Science Foundation of china
文摘Electron beam welding was carried out between aluminum alloy and steel with Ag interlayer. Seam morphology, structure and mechanical properties of the joints were investigated with different action positions of the electron beam spot. The results show that with the increment of the beam offset to the silver side from the interface between silver and steel, the seam morphology was improved, and the porosity in the Ag interlayer vanished. A transition layer mainly composed of Ag2Al and Al eutectic was formed at the interface between silver and aluminum, and became thin and spiccato as the beam offset increased. When the beam offset was too large, two IMC layers composed of FeAl and FeAl3 respectively were formed at the interface between steel and Ag interlayer. The optimal beam offset was 0.2 mm, and the maximum tensile strength of the joint was 193 MPa, 88.9% that of the aluminum alloy, and the fracture occurred at the interface between steel and Ag interlayer.
文摘Effects of laser pulse distance and reinforcing of 5456 aluminum alloy were investigated on laser weldability of Al alloy to duplex stainless steel (DSS) plates. The aluminum alloy plate was reinforced by nickel-base BNi-2 brazing powder via friction stir processing. The DSS plates were laser welded to the Al5456/BNi-2 composite and also to the Al5456 alloy plates. The welding zones were studied by scanning electron microscopy, X-ray diffractometry, micro-hardness and shear tests. The weld interface layer became thinner from 23 to 5 μm, as the laser pulse distance was increased from 0.2 to 0.5 mm. Reinforcing of the Al alloy modified the phases at interface layer from Al-Fe intermetallic compounds (IMCs) in the DSS/Al alloy weld, to Al-Ni-Fe IMCs in the DSS/Al composite one, since more nickel was injected in the weld pool by BNi-2 reinforcements. This led to a remarkable reduction in crack tendency of the welds and decreased the hardness of the interface layer from ~950 HV to ~600 HV. Shear strengths of the DSS/Al composite welds were significantly increased by ~150%, from 46 to 114 MPa, in comparison to the DSS/Al alloy ones.
文摘Defect-free butt joints of 3003 Al alloy to mild steel plates with 3 mm thickness were performed using friction stir welding （FSW）. A heat input model reported for similar FSW was simplified and used to investigate the effects of welding speed, rotation speed and tool shoulder diameter on the microstructure and properties of dissimilar welds. The comparison between microstructure, intermetallics and strength of welds shows the good conformity between the results and the calculated heat input factor （HIF） achieved from the model. The joint strength is controlled by Al/Fe interface at HIF of 0.2-0.4, by TMAZ at HIF of 0.4-0.8 and by intermetallics and/or defects at HIF0.8.
基金Project(97.13966(97.11.15)) supported by the Deputy of Research and Technology of Arak University,Iran。
文摘Commercial pure aluminum and galvanized carbon steel were lap-welded using the weld-brazing(WB)technique.Three types of aluminum filler materials(4043,4047,and 5356) were used for WB.The joint strength and intermetallic compounds at the interface of three series of samples were analyzed and compared.Depending on the Si content,a variety of ternary Al-Fe-Si intermetallic compounds(IMCs) such as Fe_(4)(Al,Si)_(13),Fe_(2) Al_(8) Si(τ_(5)),and Fe_(2) Al_(9) Si_(2)(τ_(6)) were formed at the interface.Mg element in 5356 filler material cannot contribute to the formation of Al-Fe intermetallic phases due to the positive mixing enthalpy of Mg-Fe.The presence of Mg enhances the hot cracking phenomenon near the Al-Fe intermetallic compound at the interface.Zn coating does not participate in intermetallic formation due to its evaporation during WB.It was concluded that the softening of the base metal in the heat-affected zone rather than the IMCs determines the joint efficiency.
基金Acknowledgement The authors would like to appreciate the financial support from the National Natural Science Foundation of China （Grant No. 50874033 ）.
文摘TIG welding-brazing process with high frequency induction hot wire technology was presented to create joints between 5A06 aluminum alloy and SUS32! stainless steel using ER1100 filler wire with different temperature. The joints were evaluated by mechanical test and microstructural analyses. The welding procedure using hot fiUer wire （400 ℃ ） significantly increases strength stability by 71% and average value of tensile strength by 30. 8 % of the joints, compared with cold wire. The research of microstructures in interfaces and welded seams reveals that using 400 ℃ hot filler wire can decrease the thickness of intermetallic compounds （ IMCs ） from 6 to 3.5 txm approximately, which is the main reason of mechanical property improvement.
文摘Contact reactive brazing of 6063 Al alloy and 1Cr18Ni9Ti stainless steel was researched by using Cu as interlayer. Effect of brazing time on microstructure of the joints, as well as the dissolution behaviors of Cu interlayer was analyzed. The results show that the product of reaction zone near 1Cr18Ni9Ti is composed of Fe2Al5, FeAl3 intermetallic compound （IMC）, and Cu-Al IMC; the near by area is composed of Al-Cu eutectic structure with Al （Cu） solid solution. With increasing the brazing time, the thickness of IMC layer at the interface increases, while the width of Al-Cu eutectic structure with Al（Cu） solution decreases. Calculation shows the dissolution rate of Cu interlayer is very fast. The complete dissolution time is about 0.47 s for Cu interlayer with 10 μm in thickness used in this study.
基金Project(51625404)supported by the National Science Fund for Distinguished Young Scholars,China。
文摘The driving force for using powder metallurgy(PM)mostly relies on its near net-shape ability and cost-performance ratio.The automotive application is a main market of PM industry,requiring parts with competitive mechanical or functional performance in a mass production scale.As the automobile technology transforms from traditional internal combustion engine vehicles to new energy vehicles,PM technology is undergoing significant changes in manufacturing and materials development.This review outlines the challenges and opportunities generated by the changes in the automotive technology for PM.Low-cost,high-performance and light-weight are critical aspects for future PM materials development.Therefore,the studies on PM lean-alloyed steel,aluminum alloys,and titanium alloy materials were reviewed.In addition,PM soft magnetic composite applied to new energy vehicles was discussed.Then new opportunities for advanced processing,such as metal injection molding(MIM)and additive manufacturing(AM),in automotive industry were stated.In general,the change in automotive industry raises sufficient development space for PM.While,emerging technologies require more preeminent PM materials.Iron-based parts are still the main PM products due to their mechanical performance and low cost.MIM will occupy the growing market of highly flexible and complex parts.AM opens a door for fast prototyping,great flexibility and customizing at low cost,driving weight and assembling reduction.