Considering the different geochemical enrichment behaviors of W and Mo,Fe?Mn binary oxide(FMBO),ferric hydroxide(Fe(OH)3)and manganese dioxide(MnO2)were studied to separate W from molybdate solution,respectively.The e...Considering the different geochemical enrichment behaviors of W and Mo,Fe?Mn binary oxide(FMBO),ferric hydroxide(Fe(OH)3)and manganese dioxide(MnO2)were studied to separate W from molybdate solution,respectively.The experimental results demonstrated that Fe?Mn binary oxide(FMBO)was the most suitable adsorbent for the separation.Under a wide pH(6.9?11.3)region,more than80%W removal efficiency and less than3%Mo loss could be obtained.In addition,the Fe?Mn binary oxide adsorbent can be regenerated by treating with3mol/L NaOH,and the W adsorption efficiency was retained after five adsorption?desorption?regeneration cycles.All these indicate that the Fe?Mn binary oxides have the potential for the separation of W from molybdate solution.展开更多
The removal of tungsten(W)and vanadium(V)from molybdate solutions was studied using the poly hydroxyl chelating resin D403in batch and column experiments.The batch experiments indicated that tungsten and vanadium coul...The removal of tungsten(W)and vanadium(V)from molybdate solutions was studied using the poly hydroxyl chelating resin D403in batch and column experiments.The batch experiments indicated that tungsten and vanadium could be preferentially adsorbed by the D403resin for4h in molybdate solution at a pH of approximately9.25.Separation factors,αVMo andαWMo,wereabove45and18,respectively,when the molar ratios of Mo/V and Mo/W in the solution exceeded40.Elution tests illustrated that vanadium and tungsten could be easily eluted from the resin with1mol/L sodium hydroxide solution in only1h.To further explore the sorption mechanism of the resin,the experimental equilibrium isotherm data of the three metals fitted well with the Freundlich model.The column experiments confirmed the adaptability of the D403resin in the production of sodium molybdate with a removal rate of tungsten surpassing90%and that of vanadium of99.4%.展开更多
基金Projects(51334008,51304243,51604160)supported by the National Natural Science Foundation of ChinaProject(2016zzts037)supported by the Fundamental Research Funds for the Central Universities,China
文摘Considering the different geochemical enrichment behaviors of W and Mo,Fe?Mn binary oxide(FMBO),ferric hydroxide(Fe(OH)3)and manganese dioxide(MnO2)were studied to separate W from molybdate solution,respectively.The experimental results demonstrated that Fe?Mn binary oxide(FMBO)was the most suitable adsorbent for the separation.Under a wide pH(6.9?11.3)region,more than80%W removal efficiency and less than3%Mo loss could be obtained.In addition,the Fe?Mn binary oxide adsorbent can be regenerated by treating with3mol/L NaOH,and the W adsorption efficiency was retained after five adsorption?desorption?regeneration cycles.All these indicate that the Fe?Mn binary oxides have the potential for the separation of W from molybdate solution.
基金Project(2014CB643405)supported by the National Basic Research Program of China
文摘The removal of tungsten(W)and vanadium(V)from molybdate solutions was studied using the poly hydroxyl chelating resin D403in batch and column experiments.The batch experiments indicated that tungsten and vanadium could be preferentially adsorbed by the D403resin for4h in molybdate solution at a pH of approximately9.25.Separation factors,αVMo andαWMo,wereabove45and18,respectively,when the molar ratios of Mo/V and Mo/W in the solution exceeded40.Elution tests illustrated that vanadium and tungsten could be easily eluted from the resin with1mol/L sodium hydroxide solution in only1h.To further explore the sorption mechanism of the resin,the experimental equilibrium isotherm data of the three metals fitted well with the Freundlich model.The column experiments confirmed the adaptability of the D403resin in the production of sodium molybdate with a removal rate of tungsten surpassing90%and that of vanadium of99.4%.