The precursor prepared by coordinated co-precipitation was direct reduced by hydrogen to ultra-fine fibrous Fe-Ni alloy powder. The effects of concentrations of reactants, pH value, reaction temperature and additive o...The precursor prepared by coordinated co-precipitation was direct reduced by hydrogen to ultra-fine fibrous Fe-Ni alloy powder. The effects of concentrations of reactants, pH value, reaction temperature and additive on the preparation of precursor were systematically investigated. The structures, thermal decomposition processes and morphologies of the precursors were characterized by X-ray diffraction (XRD), thermal gravity-differential thermal analysis (TG-DTA) and scanning electron microscoy (SEM). The results show that using 2% polyvinylpyrrolidone (PVP) (in mass fraction) as additive, a well-dispersed precursor with a uniform morphology can be obtained in a solution with Fe2+ and Ni2+ total concentration (1:1) of 0.8 mol/L, pH value of 6.2 at 60 °C, and a pure and well dispersed fibrous iron-nickel powder can be prepared by direct reduction of this precursor in a mixed atmosphere of nitrogen and hydrogen at the temperature of 420 °C.展开更多
The alloying behavior and microstructures of the(CoCrFeNiMn)_(90)M_(10)(M=Al,Hf)high-entropy alloy(HEA)powders fabricated by mechanical alloying were studied.The CoCrFeNiMn)_(90)Al_(10) powders have duplex solid-solut...The alloying behavior and microstructures of the(CoCrFeNiMn)_(90)M_(10)(M=Al,Hf)high-entropy alloy(HEA)powders fabricated by mechanical alloying were studied.The CoCrFeNiMn)_(90)Al_(10) powders have duplex solid-solution structures.In contrast,nanocrystalline HfNi_(3) anchoring in amorphous structures is found in the(CoCrFeNiMn)_(90)Hf_(10) powders.The(CoCrFeNiMn)_(90)Al_(10) powders show better ferromagnetic behaviors,mainly explained by the facilitated motion of the magnetic domain induced by the coherent interface between duplex phases.Combined with our previous work,the rules of forming solid-solution and amorphous phase in as-milled HEA powders are preliminarily proposed.It is found that,compared with the as-cast HEA reported previously,the variation range of mixing enthalpy with atomic size difference of the solid-solution formed in as-milled HEA powders is broader.Moreover,the variation ranges between mixing enthalpy and entropy with atomic size difference of the amorphous phase in HEA powder become wider than those of high-entropy bulk metallic glass.展开更多
基金Project (20090162120080) supported by the Research Fund for Doctoral Program of Higher Education of ChinaProject (2010FJ3011)supported by the Program of Science and Technology of Hunan Province, ChinaProject supported by the Open-End Fund for the Valuable and Precision Instruments of Central South University, China
文摘The precursor prepared by coordinated co-precipitation was direct reduced by hydrogen to ultra-fine fibrous Fe-Ni alloy powder. The effects of concentrations of reactants, pH value, reaction temperature and additive on the preparation of precursor were systematically investigated. The structures, thermal decomposition processes and morphologies of the precursors were characterized by X-ray diffraction (XRD), thermal gravity-differential thermal analysis (TG-DTA) and scanning electron microscoy (SEM). The results show that using 2% polyvinylpyrrolidone (PVP) (in mass fraction) as additive, a well-dispersed precursor with a uniform morphology can be obtained in a solution with Fe2+ and Ni2+ total concentration (1:1) of 0.8 mol/L, pH value of 6.2 at 60 °C, and a pure and well dispersed fibrous iron-nickel powder can be prepared by direct reduction of this precursor in a mixed atmosphere of nitrogen and hydrogen at the temperature of 420 °C.
基金financial supports from the National Natural Science Foundation of China (No.51971102)the Major Basic Research Projects of Shandong Natural Science Foundation,China (No.ZR2020ZD06)+1 种基金the Open Research Fund of Songshan Lake Materials Laboratory,China (No.2021SLABFK08)the Science and Technology Program of University of Jinan,China (No.XKY2117)。
文摘The alloying behavior and microstructures of the(CoCrFeNiMn)_(90)M_(10)(M=Al,Hf)high-entropy alloy(HEA)powders fabricated by mechanical alloying were studied.The CoCrFeNiMn)_(90)Al_(10) powders have duplex solid-solution structures.In contrast,nanocrystalline HfNi_(3) anchoring in amorphous structures is found in the(CoCrFeNiMn)_(90)Hf_(10) powders.The(CoCrFeNiMn)_(90)Al_(10) powders show better ferromagnetic behaviors,mainly explained by the facilitated motion of the magnetic domain induced by the coherent interface between duplex phases.Combined with our previous work,the rules of forming solid-solution and amorphous phase in as-milled HEA powders are preliminarily proposed.It is found that,compared with the as-cast HEA reported previously,the variation range of mixing enthalpy with atomic size difference of the solid-solution formed in as-milled HEA powders is broader.Moreover,the variation ranges between mixing enthalpy and entropy with atomic size difference of the amorphous phase in HEA powder become wider than those of high-entropy bulk metallic glass.