The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing...The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing compounds in the alloys produced by conventional casting process are detrimental to the strength of matrix. The effect of ultrasonic vibration （USV） on the morphology change of Fe-containing intermetallic compounds in the hypereutectic Al-17Si-xFe （x=2, 3, 4, 5） alloys was systematically studied. The results show that, the Fe-containing intermetallic compounds are mainly composed of long needle-like β-Al5FeSi phase with a small amount of plate-like δ-Al4FeSi2 phase in Al-17Si-2Fe alloy produced by conventional casting process. With the increase of Fe content from 2% to 5% in the alloys, the amount of plate-like or coarse needle-like δ-Al4FeSi2 phase increases while the amount of long needle-like β-Al5FeSi phases decreases. In Al-17Si-5Fe alloy, the Fe-containing intermetallic compounds exist mainly as coarse needle-like δ-Al4FeSi2 phase. After USV treatment, the Fe-containing compounds in the Al-17Si-xFe alloys are refined and exist mainly as δ-Al4FeSi2 particles, with average grain size ranging from 26 μm to 37 μm, and only a small amount of β-Al5FeSi phases remain. The mechanism of USV on the morphology of Fe-containing intermetallic compounds was also discussed.展开更多
This paper presents the effect of Fe on the microstructure and mechanical properties of Al-9Mg-2.6Si alloy.The Feaddition in the Al-9Mg-2.6Si alloy can slightly increase the yield strength but decrease the elongation....This paper presents the effect of Fe on the microstructure and mechanical properties of Al-9Mg-2.6Si alloy.The Feaddition in the Al-9Mg-2.6Si alloy can slightly increase the yield strength but decrease the elongation.With a much higher Feaddition around1.6wt.%,the elongation of the alloy can still maintain a usable level of5%.This alloy has shown a high toleranceon the Fe contamination展开更多
基金Project(2012CB619600)supported by the National Basic Research Program of ChinaProject(50775086)supported by the National Natural Science Foundation of China
文摘The Fe-containing intermetallic compounds with high melting point in hypereutectic Al-Si alloys can improve the heat resistance and wear resistance at elevated temperatures. However, the long needle-like Fe-containing compounds in the alloys produced by conventional casting process are detrimental to the strength of matrix. The effect of ultrasonic vibration （USV） on the morphology change of Fe-containing intermetallic compounds in the hypereutectic Al-17Si-xFe （x=2, 3, 4, 5） alloys was systematically studied. The results show that, the Fe-containing intermetallic compounds are mainly composed of long needle-like β-Al5FeSi phase with a small amount of plate-like δ-Al4FeSi2 phase in Al-17Si-2Fe alloy produced by conventional casting process. With the increase of Fe content from 2% to 5% in the alloys, the amount of plate-like or coarse needle-like δ-Al4FeSi2 phase increases while the amount of long needle-like β-Al5FeSi phases decreases. In Al-17Si-5Fe alloy, the Fe-containing intermetallic compounds exist mainly as coarse needle-like δ-Al4FeSi2 phase. After USV treatment, the Fe-containing compounds in the Al-17Si-xFe alloys are refined and exist mainly as δ-Al4FeSi2 particles, with average grain size ranging from 26 μm to 37 μm, and only a small amount of β-Al5FeSi phases remain. The mechanism of USV on the morphology of Fe-containing intermetallic compounds was also discussed.
文摘This paper presents the effect of Fe on the microstructure and mechanical properties of Al-9Mg-2.6Si alloy.The Feaddition in the Al-9Mg-2.6Si alloy can slightly increase the yield strength but decrease the elongation.With a much higher Feaddition around1.6wt.%,the elongation of the alloy can still maintain a usable level of5%.This alloy has shown a high toleranceon the Fe contamination