The suitable titanium slag composition with high titanium content for electric furnace smelting of vanadium titanomagnetite was investigated through thermodynamics and related phase diagram analysis.According to the t...The suitable titanium slag composition with high titanium content for electric furnace smelting of vanadium titanomagnetite was investigated through thermodynamics and related phase diagram analysis.According to the thermodynamic results,low-melting-point regions and MgTi2O5primary phase area in the phase diagrams,the suggested titanium slag composition for the present vanadium titanomagnetite metallized pellets should consist of50%TiO2,8%-12%MgO and13%Al2O3(mass fraction)with a binary basicity of0.8-1.2.Finally,the verified smelting experiments were conducted and successful separation of the molten iron from the titanium slag is obtained.The obtained vanadium-containing molten iron contains0.681%V and0.267%Ti,and the obtained titanium slag contains52.21%TiO2(mass fraction),in which MgTi2O5is the primary phase.The titanium resource in the final titanium slag production could be used to produce TiO2pigment by acid leaching methods.展开更多
文摘The suitable titanium slag composition with high titanium content for electric furnace smelting of vanadium titanomagnetite was investigated through thermodynamics and related phase diagram analysis.According to the thermodynamic results,low-melting-point regions and MgTi2O5primary phase area in the phase diagrams,the suggested titanium slag composition for the present vanadium titanomagnetite metallized pellets should consist of50%TiO2,8%-12%MgO and13%Al2O3(mass fraction)with a binary basicity of0.8-1.2.Finally,the verified smelting experiments were conducted and successful separation of the molten iron from the titanium slag is obtained.The obtained vanadium-containing molten iron contains0.681%V and0.267%Ti,and the obtained titanium slag contains52.21%TiO2(mass fraction),in which MgTi2O5is the primary phase.The titanium resource in the final titanium slag production could be used to produce TiO2pigment by acid leaching methods.