Thermal fatigue and high temperature wear are the two principle failure mechanisms for thixoforming dies. Samples of Inconel 617 and Stellite 6 alloys were submitted to thermal cycling under conditions which approxima...Thermal fatigue and high temperature wear are the two principle failure mechanisms for thixoforming dies. Samples of Inconel 617 and Stellite 6 alloys were submitted to thermal cycling under conditions which approximate thixoforming of steels and to sliding wear tests at 750 ℃. The experimental results thus obtained were compared with those of the X32CrMoV33 hot work tool steel. The Inconel 617 and Stellite 6 samples are much more resistant to oxidation and to softening than the hot work tool steel, providing a superior resistance to thermal fatigue cracking. The wear resistance of the Inconel 617 and Stellite 6 alloys at 750 ℃ is also markedly superior. The adhesive oxides growing slowly on Inconel 617 and Stellite 6 alloys sustain the wear action without spalling and are claimed to be responsible for the superior wear resistance of these alloys at 750 ℃.展开更多
A visco-plastic rate-dependent homogenization theory for particle-reinforced composites was derived and the equivalent elastic constants and the equivalent visco-plastic parameters of these composites were obtained. A...A visco-plastic rate-dependent homogenization theory for particle-reinforced composites was derived and the equivalent elastic constants and the equivalent visco-plastic parameters of these composites were obtained. A framework of homogenization the- ory for particle-reinforced W-Ni-Fe composites, a kind of tungsten alloy, was established. Based on the homogenization theory and a fixed-point iteration method, a unit cell model with typical microstructnres of the composite was established by using dynamic analysis program. The effects of tungsten content, tungsten particle shape and particle size and interface strength on the mechanical properties and the crack propagation of the W-Ni-Fe composite are analyzed under quasi-static and dynamic loadings. The stress-strain curves of the composite are given and the relation between the macro-mechanical characteristics and the microstructure parameters is explored, which provides an important theoretical basis for the optimization of the W-Ni-Fe composites.展开更多
文摘Thermal fatigue and high temperature wear are the two principle failure mechanisms for thixoforming dies. Samples of Inconel 617 and Stellite 6 alloys were submitted to thermal cycling under conditions which approximate thixoforming of steels and to sliding wear tests at 750 ℃. The experimental results thus obtained were compared with those of the X32CrMoV33 hot work tool steel. The Inconel 617 and Stellite 6 samples are much more resistant to oxidation and to softening than the hot work tool steel, providing a superior resistance to thermal fatigue cracking. The wear resistance of the Inconel 617 and Stellite 6 alloys at 750 ℃ is also markedly superior. The adhesive oxides growing slowly on Inconel 617 and Stellite 6 alloys sustain the wear action without spalling and are claimed to be responsible for the superior wear resistance of these alloys at 750 ℃.
基金supported by the National Natural Science Foundation of China (Grant No. 11032002 and 91016013)the program for New Century Excellent Talents in University+1 种基金National Basic Research Program of China (Grant No. 2010CB832706)the project of State Key Laboratory of Explosion Science and Technology (Beijing Institute of Technology)(Grant No. ZDKT10-03a)
文摘A visco-plastic rate-dependent homogenization theory for particle-reinforced composites was derived and the equivalent elastic constants and the equivalent visco-plastic parameters of these composites were obtained. A framework of homogenization the- ory for particle-reinforced W-Ni-Fe composites, a kind of tungsten alloy, was established. Based on the homogenization theory and a fixed-point iteration method, a unit cell model with typical microstructnres of the composite was established by using dynamic analysis program. The effects of tungsten content, tungsten particle shape and particle size and interface strength on the mechanical properties and the crack propagation of the W-Ni-Fe composite are analyzed under quasi-static and dynamic loadings. The stress-strain curves of the composite are given and the relation between the macro-mechanical characteristics and the microstructure parameters is explored, which provides an important theoretical basis for the optimization of the W-Ni-Fe composites.
