The effect of base oils,sulfur-containing multi-functional additives and dispersants in formulated diesel lubricants on lead corrosion was evaluated by a self-established high temperature corrosion bench test.Test lea...The effect of base oils,sulfur-containing multi-functional additives and dispersants in formulated diesel lubricants on lead corrosion was evaluated by a self-established high temperature corrosion bench test.Test lead coupons were analyzed by XPS to determine the resulting surface chemistry.The results showed a close correlation between the oxidation stability of base oil blend and the lead corrosion of formulated diesel lubricants.The zinc dialkyldithiophosphate(ZDDP)and zinc dialkyldithiocarbamate(ZDDC)have formed different protective films on lead coupon surfaces.A more or less amount of the protective film formed is the main factor affecting the degree of lead corrosion.The glassy zinc phosphates protective film formed by ZDDP is more effective than the zinc sulfides film formed by ZDDC.The interaction between dispersants and ZDDP had a significant impact on lead corrosion.展开更多
One‐step production of pyruvic acid through selective oxidation of glycerol was investigated using lead promoted platinum/activated carbon(Pb‐Pt/AC)catalysts under mild conditions.The results of N2physisorption,X‐r...One‐step production of pyruvic acid through selective oxidation of glycerol was investigated using lead promoted platinum/activated carbon(Pb‐Pt/AC)catalysts under mild conditions.The results of N2physisorption,X‐ray diffraction,X‐ray photoelectron spectroscopy,and high‐resolution transmission electron microscopy revealed that the alloy phases of PtPb and PtxPb were favorable for pyruvic acid production from glycerol oxidation,whereas the Pb3(CO3)2(OH)2and surface Pb0species inhibited the glycerol conversion.The loading of Pb and the catalyst preparation method(including impregnation and deposition precipitation)affected the formation of different metal species.Pyruvic acid was obtained at a yield of18.4%on a5.0wt%Pb‐5.0wt%Pt/AC catalyst prepared by co‐deposition precipitation method and500°C argon treatment.展开更多
In this paper, the effect of MMT on the induction period of unleaded motor gasoline was studied, the manganese concentration, storage period of MMT-blended gasoline and environmental variables such as temperature and ...In this paper, the effect of MMT on the induction period of unleaded motor gasoline was studied, the manganese concentration, storage period of MMT-blended gasoline and environmental variables such as temperature and radiation intensity were considered to be main factors affecting the induction period of gasoline,when MMT-blended gasoline was exposed to light. It is found from experiments that the addition of MMT can improve the induction period of gasoline that is shielded from light, and reduce the induction period remarkably,when the gasoline is exposed to light. However, the radiation intensity is proved to be the leading influencing factor among all the environmental variables investigated.展开更多
A series of bimetallic Pd-Pb catalysts with a constant Pd content of 1 wt%and Pb/Pd atomic ratio from 0 to 1.6 supported on γ-Al2O3 were prepared and used for glycerol oxidation with H2O2 as the oxidizing agent at at...A series of bimetallic Pd-Pb catalysts with a constant Pd content of 1 wt%and Pb/Pd atomic ratio from 0 to 1.6 supported on γ-Al2O3 were prepared and used for glycerol oxidation with H2O2 as the oxidizing agent at atmospheric pressure,45℃ and pH =11.The morphology and dispersion of the catalysts were characterized by scanning electron microscopy-energy dispersive X-ray spectroscopy（SEM-EDX） and transmission electron microscopy（TEM）.The presence of an alloy phase in the bimetallic catalyst was detected by X-ray photoelectron spectroscopy（XPS）.Glycerol conversion obtained with the monometallic Pd catalyst was 19%,which was increased to 100%with the addition of Pb.The four bimetallic PdPb catalysts were able to oxidize glycerol to dihydroxyacetone（DIHA） and the selectivity to DIHA reached 59%,58%,34%and 25%for PdPb0.25,PdPb0.50,PdPb1.00 and PdPbl.60 catalysts,respectively.展开更多
基金financilly supported by the Research Project of China Petroleum&Chemical Corporation(112066)
文摘The effect of base oils,sulfur-containing multi-functional additives and dispersants in formulated diesel lubricants on lead corrosion was evaluated by a self-established high temperature corrosion bench test.Test lead coupons were analyzed by XPS to determine the resulting surface chemistry.The results showed a close correlation between the oxidation stability of base oil blend and the lead corrosion of formulated diesel lubricants.The zinc dialkyldithiophosphate(ZDDP)and zinc dialkyldithiocarbamate(ZDDC)have formed different protective films on lead coupon surfaces.A more or less amount of the protective film formed is the main factor affecting the degree of lead corrosion.The glassy zinc phosphates protective film formed by ZDDP is more effective than the zinc sulfides film formed by ZDDC.The interaction between dispersants and ZDDP had a significant impact on lead corrosion.
基金supported by the National Natural Science Foundation of China(21176236)~~
文摘One‐step production of pyruvic acid through selective oxidation of glycerol was investigated using lead promoted platinum/activated carbon(Pb‐Pt/AC)catalysts under mild conditions.The results of N2physisorption,X‐ray diffraction,X‐ray photoelectron spectroscopy,and high‐resolution transmission electron microscopy revealed that the alloy phases of PtPb and PtxPb were favorable for pyruvic acid production from glycerol oxidation,whereas the Pb3(CO3)2(OH)2and surface Pb0species inhibited the glycerol conversion.The loading of Pb and the catalyst preparation method(including impregnation and deposition precipitation)affected the formation of different metal species.Pyruvic acid was obtained at a yield of18.4%on a5.0wt%Pb‐5.0wt%Pt/AC catalyst prepared by co‐deposition precipitation method and500°C argon treatment.
文摘In this paper, the effect of MMT on the induction period of unleaded motor gasoline was studied, the manganese concentration, storage period of MMT-blended gasoline and environmental variables such as temperature and radiation intensity were considered to be main factors affecting the induction period of gasoline,when MMT-blended gasoline was exposed to light. It is found from experiments that the addition of MMT can improve the induction period of gasoline that is shielded from light, and reduce the induction period remarkably,when the gasoline is exposed to light. However, the radiation intensity is proved to be the leading influencing factor among all the environmental variables investigated.
基金supported by CONICET(PIP 0276)UNLP(Projects X 700)+1 种基金UNNOBA(SIB 2924/14)Ministry of Education and Sports(Call "Jorge Sabato" Project 44-144-415),Argentina
文摘A series of bimetallic Pd-Pb catalysts with a constant Pd content of 1 wt%and Pb/Pd atomic ratio from 0 to 1.6 supported on γ-Al2O3 were prepared and used for glycerol oxidation with H2O2 as the oxidizing agent at atmospheric pressure,45℃ and pH =11.The morphology and dispersion of the catalysts were characterized by scanning electron microscopy-energy dispersive X-ray spectroscopy（SEM-EDX） and transmission electron microscopy（TEM）.The presence of an alloy phase in the bimetallic catalyst was detected by X-ray photoelectron spectroscopy（XPS）.Glycerol conversion obtained with the monometallic Pd catalyst was 19%,which was increased to 100%with the addition of Pb.The four bimetallic PdPb catalysts were able to oxidize glycerol to dihydroxyacetone（DIHA） and the selectivity to DIHA reached 59%,58%,34%and 25%for PdPb0.25,PdPb0.50,PdPb1.00 and PdPbl.60 catalysts,respectively.