Three La-doped CeO2-ZrO2-Al2O3(CZA)composite oxide samples,namely,CZA-I,CZA-II and CZA-III,were prepared following a co-precipitation method in the presence of La2O3,La(NO3)3-6H2O and H[La(EDTA)]-16H2O precursors,resp...Three La-doped CeO2-ZrO2-Al2O3(CZA)composite oxide samples,namely,CZA-I,CZA-II and CZA-III,were prepared following a co-precipitation method in the presence of La2O3,La(NO3)3-6H2O and H[La(EDTA)]-16H2O precursors,respectively.When the precursor samples are sintered at 1000°C,the as-prepared composite oxides mainly exhibit the CeO2-ZrO2 cubic fluorite phase,while theγ-Al2O3 andδ-Al2O3 phases appear when the precursor samples are subjected to sintering at 1100 and 1200°C.CZA-III exhibits improved redox properties after high-temperature treatment compared with CZA-I and CZA-II.CZA-III presents the largest surface area of 97.46 m2/g among the three CZAs when the CZA-III precursor sample is sintered at 1000°C.Furthermore,the corresponding oxygen storage capacity(OSC)is the largest with value of 400.27μmol/g when CZA-III precursor sample is sintered at 1000°C.Additionally,CZA-III exhibits the best thermal stability and the highest reduction temperature.However,by increasing the sintering temperature to 1200°C,there is a dramatic decline in the properties of surface area and OSC.And a decrease for CZA-III in surface area by 58.94%and a decrease of the OSC value by 74.56%are observed.展开更多
基金Project(14JJ4043)supported by the Natural Science Foundation of Hunan Province,China
文摘Three La-doped CeO2-ZrO2-Al2O3(CZA)composite oxide samples,namely,CZA-I,CZA-II and CZA-III,were prepared following a co-precipitation method in the presence of La2O3,La(NO3)3-6H2O and H[La(EDTA)]-16H2O precursors,respectively.When the precursor samples are sintered at 1000°C,the as-prepared composite oxides mainly exhibit the CeO2-ZrO2 cubic fluorite phase,while theγ-Al2O3 andδ-Al2O3 phases appear when the precursor samples are subjected to sintering at 1100 and 1200°C.CZA-III exhibits improved redox properties after high-temperature treatment compared with CZA-I and CZA-II.CZA-III presents the largest surface area of 97.46 m2/g among the three CZAs when the CZA-III precursor sample is sintered at 1000°C.Furthermore,the corresponding oxygen storage capacity(OSC)is the largest with value of 400.27μmol/g when CZA-III precursor sample is sintered at 1000°C.Additionally,CZA-III exhibits the best thermal stability and the highest reduction temperature.However,by increasing the sintering temperature to 1200°C,there is a dramatic decline in the properties of surface area and OSC.And a decrease for CZA-III in surface area by 58.94%and a decrease of the OSC value by 74.56%are observed.