Room-temperature mechanical properties of Cu50Zr40Ti10-xNix（0≤x≤4,mole fraction,%） bulk metallic glasses （BMG） with aspect ratios in the range of 1：1-2.5：1 and loading rates in the range of1×10^-5-1×...Room-temperature mechanical properties of Cu50Zr40Ti10-xNix（0≤x≤4,mole fraction,%） bulk metallic glasses （BMG） with aspect ratios in the range of 1：1-2.5：1 and loading rates in the range of1×10^-5-1×10^-2s^-1were systematically investigated by room-temperatureuniaxialcompression test.In the condition of an aspect ratio of 1：1, the superplasticity can be clearly observed for Cu50Zr40Ti10BMG when the loading rate is1×10^-4s^-1, while for Cu50Zr40Ti10-xNix（x=1-3, mole fraction, %） BMGs when the loading rate is1×10^-2s^-1. The plastic strain （εp）, yielding strength （σy） and fracture strength （σf） of the studied Cu-based BMGs significantly depend on the aspect ratio and the loading rate. In addition, theσyof the studied Cu-based BMGs with an aspect ratio of 1：1 is close to the σfof those with the other aspect ratios when the loading rate is1×10^-2s^-1. The mechanism for the mechanical response to the loading rate and the aspect ratiowas also discussed.展开更多
基金Projects(50874045,51301194)supported by the National Natural Science Foundation of ChinaProject(2144057)supported by the Beijing Natural Science Foundation,China
文摘Room-temperature mechanical properties of Cu50Zr40Ti10-xNix（0≤x≤4,mole fraction,%） bulk metallic glasses （BMG） with aspect ratios in the range of 1：1-2.5：1 and loading rates in the range of1×10^-5-1×10^-2s^-1were systematically investigated by room-temperatureuniaxialcompression test.In the condition of an aspect ratio of 1：1, the superplasticity can be clearly observed for Cu50Zr40Ti10BMG when the loading rate is1×10^-4s^-1, while for Cu50Zr40Ti10-xNix（x=1-3, mole fraction, %） BMGs when the loading rate is1×10^-2s^-1. The plastic strain （εp）, yielding strength （σy） and fracture strength （σf） of the studied Cu-based BMGs significantly depend on the aspect ratio and the loading rate. In addition, theσyof the studied Cu-based BMGs with an aspect ratio of 1：1 is close to the σfof those with the other aspect ratios when the loading rate is1×10^-2s^-1. The mechanism for the mechanical response to the loading rate and the aspect ratiowas also discussed.