NA novel smelting reduction process based on FeO-SiO2-Al2O3 slag system for spent lithium ion batteries with Al cans was developed, while using copper slag as the only slag former. The feasibility of the process and t...NA novel smelting reduction process based on FeO-SiO2-Al2O3 slag system for spent lithium ion batteries with Al cans was developed, while using copper slag as the only slag former. The feasibility of the process and the mechanism of copper loss in slag were investigated. 98.83% Co, 98.39% Ni and 93.57% Cu were recovered under the optimum conditions of slag former/battery mass ratio of 4.0：1, smelting temperature of 1723 K, and smelting mass ratio of time of 30 min. The FeO-SiO2-Al2O3 slag system for the smelting process is appropriate under the conditions of m（FeO）：m（SiO2）=0.58：1？1.03：1, and 17.19%？21.52% Al2O3 content. The obtained alloy was mainly composed of Fe-Co-Cu-Ni solid solution including small amounts of matte. The obtained slag mainly consisted of fayalite and hercynite. Meanwhile, the mechanism of copper loss is the mechanical entrainment from strip-like fayalite particles in the main form of copper sulfide and metallic copper.展开更多
An efficient chlorination roasting process for recovering zinc(Zn)and lead(Pb)from copper smelting slag was proposed.Thermodynamic models were established,illustrating that Zn and Pb in copper smelting slag can be eff...An efficient chlorination roasting process for recovering zinc(Zn)and lead(Pb)from copper smelting slag was proposed.Thermodynamic models were established,illustrating that Zn and Pb in copper smelting slag can be efficiently recycled during the chlorination roasting process.By decreasing the partial pressure of the gaseous products,chlorination was promoted.The Box−Behnken design was applied to assessing the interactive effects of the process variables and optimizing the chlorination roasting process.CaCl_(2) dosage and roasting temperature and time were used as variables,and metal recovery efficiencies were used as responses.When the roasting temperature was 1172℃ with a CaCl_(2) addition amount of 30 wt.%and a roasting time of 100 min,the predicted optimal recovery efficiencies of Zn and Pb were 87.85%and 99.26%,respectively,and the results were validated by experiments under the same conditions.The residual Zn-and Pb-containing phases in the roasting slags were ZnFe_(2)O_(4),Zn_(2)SiO_(4),and PbS.展开更多
In order to reasonably utilize the iron resources of copper slags, the smelting chlorination process was used to remove copper from copper slags. Higher holding temperature and O2 flow rate are beneficial to increasin...In order to reasonably utilize the iron resources of copper slags, the smelting chlorination process was used to remove copper from copper slags. Higher holding temperature and O2 flow rate are beneficial to increasing copper removal rate. However,the Cu2O mode is formed by the reaction of surplus O2 and CuCl with O2 flow rate increasing over 0.4 L/min, causing CuCl volatilization rate and copper removal rate to decrease. The resulting copper removal rate of 84.34% is obtained under the optimum conditions of holding temperature of 1573 K, residence time of 10 min, Ca Cl2 addition amount of 0.1(mass ratio of CaCl2 and the copper slag) and oxygen flow rate of 0.4 L/min. The efficient removal of copper from copper slags through chlorination is feasible.展开更多
Most Zn hydrometallurgy factories adopt Cu2SO4 as a dechlorination reagent from zinc solution nowadays, thus much CuCl residue is produced. The existing process of treating this residue is washing with water or sodium...Most Zn hydrometallurgy factories adopt Cu2SO4 as a dechlorination reagent from zinc solution nowadays, thus much CuCl residue is produced. The existing process of treating this residue is washing with water or sodium carbonate solution, which would cause a lot of troubles to water treatment and waste discharge. A method of microwave roasting was adopted for dechlorination of CuCl residue. A 1.5 kW microwave roasting equipment with dust collection and tail gas adsorption systems was set up and applied during the experiment. By investigating the effect of temperature, heat preservation time, moisture content of raw material and grain size of samples on the dechlorination, the optimal experimental condition is obtained. When the samples with 2% moisture and <150 μm grain size are microwave roasted at 400 °C for 2 h, the Cl content turns from 14.27% to 1.35% and the dechlorination rate is as high as 90%, while that with conventional heating is only 60%-80%. The phase change of the roasting process investigated with X-ray diffraction verifies that CuCl in CuCl residue is removed by being transformed into CuO.展开更多
基金Project(JS-211)supported by the State-Owned Enterprise Electric Vehicle Industry Alliance,China
文摘NA novel smelting reduction process based on FeO-SiO2-Al2O3 slag system for spent lithium ion batteries with Al cans was developed, while using copper slag as the only slag former. The feasibility of the process and the mechanism of copper loss in slag were investigated. 98.83% Co, 98.39% Ni and 93.57% Cu were recovered under the optimum conditions of slag former/battery mass ratio of 4.0：1, smelting temperature of 1723 K, and smelting mass ratio of time of 30 min. The FeO-SiO2-Al2O3 slag system for the smelting process is appropriate under the conditions of m（FeO）：m（SiO2）=0.58：1？1.03：1, and 17.19%？21.52% Al2O3 content. The obtained alloy was mainly composed of Fe-Co-Cu-Ni solid solution including small amounts of matte. The obtained slag mainly consisted of fayalite and hercynite. Meanwhile, the mechanism of copper loss is the mechanical entrainment from strip-like fayalite particles in the main form of copper sulfide and metallic copper.
基金The authors are grateful for the financial supports from the National Natural Science Foundation of China(Nos.51620105013,51904351)Innovation-Driven Project of Central South University,China(No.2020CX028)+1 种基金Natural Science Fund for Distinguished Young Scholar of Hunan Province,China(No.2019JJ20031)the National Key R&D Program of China(No.2019YFC1907400)。
文摘An efficient chlorination roasting process for recovering zinc(Zn)and lead(Pb)from copper smelting slag was proposed.Thermodynamic models were established,illustrating that Zn and Pb in copper smelting slag can be efficiently recycled during the chlorination roasting process.By decreasing the partial pressure of the gaseous products,chlorination was promoted.The Box−Behnken design was applied to assessing the interactive effects of the process variables and optimizing the chlorination roasting process.CaCl_(2) dosage and roasting temperature and time were used as variables,and metal recovery efficiencies were used as responses.When the roasting temperature was 1172℃ with a CaCl_(2) addition amount of 30 wt.%and a roasting time of 100 min,the predicted optimal recovery efficiencies of Zn and Pb were 87.85%and 99.26%,respectively,and the results were validated by experiments under the same conditions.The residual Zn-and Pb-containing phases in the roasting slags were ZnFe_(2)O_(4),Zn_(2)SiO_(4),and PbS.
基金Project(51204082)supported by the National Natural Science Foundation of ChinaProject(KKZ3201252011)supported by Talent Cultivation Project of Kunming University of Science and Technology,China
文摘In order to reasonably utilize the iron resources of copper slags, the smelting chlorination process was used to remove copper from copper slags. Higher holding temperature and O2 flow rate are beneficial to increasing copper removal rate. However,the Cu2O mode is formed by the reaction of surplus O2 and CuCl with O2 flow rate increasing over 0.4 L/min, causing CuCl volatilization rate and copper removal rate to decrease. The resulting copper removal rate of 84.34% is obtained under the optimum conditions of holding temperature of 1573 K, residence time of 10 min, Ca Cl2 addition amount of 0.1(mass ratio of CaCl2 and the copper slag) and oxygen flow rate of 0.4 L/min. The efficient removal of copper from copper slags through chlorination is feasible.
基金Project(51104073)supported by the National Natural Science Foundation of China
文摘Most Zn hydrometallurgy factories adopt Cu2SO4 as a dechlorination reagent from zinc solution nowadays, thus much CuCl residue is produced. The existing process of treating this residue is washing with water or sodium carbonate solution, which would cause a lot of troubles to water treatment and waste discharge. A method of microwave roasting was adopted for dechlorination of CuCl residue. A 1.5 kW microwave roasting equipment with dust collection and tail gas adsorption systems was set up and applied during the experiment. By investigating the effect of temperature, heat preservation time, moisture content of raw material and grain size of samples on the dechlorination, the optimal experimental condition is obtained. When the samples with 2% moisture and <150 μm grain size are microwave roasted at 400 °C for 2 h, the Cl content turns from 14.27% to 1.35% and the dechlorination rate is as high as 90%, while that with conventional heating is only 60%-80%. The phase change of the roasting process investigated with X-ray diffraction verifies that CuCl in CuCl residue is removed by being transformed into CuO.