The corrosion behavior of the Cu-Ti alloys with different Ti contents in 3.5%(mass fraction)NaCl solution was investigated using electrochemical measurements,immersion tests,mass loss measurements and SEM observation....The corrosion behavior of the Cu-Ti alloys with different Ti contents in 3.5%(mass fraction)NaCl solution was investigated using electrochemical measurements,immersion tests,mass loss measurements and SEM observation.The results show that Ti dissolved in the Cu matrix changes the corrosion process of the alloys.Pure Cu sample exhibits a typical active–passive-transpassive corrosion behavior.The anodic polarization current densities of the Cu-Ti alloys steadily increase with increasing applied potential,indicating that active dissolution of copper proceeds due to the potential difference in the galvanic coupling of Cu and Ti.The increase of Ti content decreases the corrosion resistance of the Cu-Ti alloys.展开更多
The vacuum brazing of TiAl based alloy with 40Cr steel was investigated using Ag-Cu-Ti filler metal. The experimental results show that the Ag, Cu, Ti atoms in the filler metal and the base metal inter-diffuse toward ...The vacuum brazing of TiAl based alloy with 40Cr steel was investigated using Ag-Cu-Ti filler metal. The experimental results show that the Ag, Cu, Ti atoms in the filler metal and the base metal inter-diffuse toward each other during brazing and react at the interface to form an inter-metallic AlCu 2Ti compound which joins two parts to produce a brazing joint with higher strength.展开更多
基金Project(51374151)supported by the National Natural Science Foundation of China
文摘The corrosion behavior of the Cu-Ti alloys with different Ti contents in 3.5%(mass fraction)NaCl solution was investigated using electrochemical measurements,immersion tests,mass loss measurements and SEM observation.The results show that Ti dissolved in the Cu matrix changes the corrosion process of the alloys.Pure Cu sample exhibits a typical active–passive-transpassive corrosion behavior.The anodic polarization current densities of the Cu-Ti alloys steadily increase with increasing applied potential,indicating that active dissolution of copper proceeds due to the potential difference in the galvanic coupling of Cu and Ti.The increase of Ti content decreases the corrosion resistance of the Cu-Ti alloys.
文摘The vacuum brazing of TiAl based alloy with 40Cr steel was investigated using Ag-Cu-Ti filler metal. The experimental results show that the Ag, Cu, Ti atoms in the filler metal and the base metal inter-diffuse toward each other during brazing and react at the interface to form an inter-metallic AlCu 2Ti compound which joins two parts to produce a brazing joint with higher strength.