The effects of 0.01 wt.%Ga on microstructure and electrochemical performance of Al−0.4Mg−0.05Sn−0.03Hg anodes in NaOH solutions were investigated.Potentiodynamic polarization,electrochemical impedance spectroscopy,and...The effects of 0.01 wt.%Ga on microstructure and electrochemical performance of Al−0.4Mg−0.05Sn−0.03Hg anodes in NaOH solutions were investigated.Potentiodynamic polarization,electrochemical impedance spectroscopy,and galvanostatic discharge tests were used to assess the electrochemical performance of the Al−Mg−Sn−Hg−Ga anodes.The results show that the addition of 0.01 wt.%Ga in Al−0.4Mg−0.05Sn−0.03Hg anode enhances its corrosion resistance and discharge activity.It is benefited from the refined second phases and homogenous microstructure of Al−Mg−Sn−Hg−Ga anode,which restrains the local crystallographic corrosion and chunk effect.Compared with Al−Mg−Sn−Hg anode,the corrosion current density and the mass loss rate of Al−Mg−Sn−Hg−Ga anode decrease by 57%and 93%,respectively.When discharging at the current density of 20 mA/cm^(2),the discharge voltage,current efficiency and specific capacity of the single Al−air battery with Al−0.4Mg−0.05Sn−0.03Hg−0.01Ga anode are 1.46 V,33.1%,and 1019.2 A·h·kg^(−1),respectively.The activation mechanism of Ga on Al−Mg−Sn−Hg−Ga anode materials was also discussed.展开更多
基金This work is supported by the Equipment Pre-research Laboratory Foundation in Central South University,China(No.6142912200104).
文摘The effects of 0.01 wt.%Ga on microstructure and electrochemical performance of Al−0.4Mg−0.05Sn−0.03Hg anodes in NaOH solutions were investigated.Potentiodynamic polarization,electrochemical impedance spectroscopy,and galvanostatic discharge tests were used to assess the electrochemical performance of the Al−Mg−Sn−Hg−Ga anodes.The results show that the addition of 0.01 wt.%Ga in Al−0.4Mg−0.05Sn−0.03Hg anode enhances its corrosion resistance and discharge activity.It is benefited from the refined second phases and homogenous microstructure of Al−Mg−Sn−Hg−Ga anode,which restrains the local crystallographic corrosion and chunk effect.Compared with Al−Mg−Sn−Hg anode,the corrosion current density and the mass loss rate of Al−Mg−Sn−Hg−Ga anode decrease by 57%and 93%,respectively.When discharging at the current density of 20 mA/cm^(2),the discharge voltage,current efficiency and specific capacity of the single Al−air battery with Al−0.4Mg−0.05Sn−0.03Hg−0.01Ga anode are 1.46 V,33.1%,and 1019.2 A·h·kg^(−1),respectively.The activation mechanism of Ga on Al−Mg−Sn−Hg−Ga anode materials was also discussed.