The failure caused by the corrosion-wear of molten aluminum and its alloys is one of the main problems in aluminum industry. In this work, the resistance behavior of various materials, including Fe-based alloys, ceram...The failure caused by the corrosion-wear of molten aluminum and its alloys is one of the main problems in aluminum industry. In this work, the resistance behavior of various materials, including Fe-based alloys, ceramics and corresponding high apparatus of corrosion-wear in molten aluminum and its alloys, were reviewed. The synergistic effect of corrosion and wear was discussed based on corrosion and wear mechanics. The effects of dynamic agitation due to rotating of friction pairs, physical property of liquid metal and size of grain etc., on the corrosion-wear resistance performance were investigated. In addition, the characteristics of corrosion-wear resistance performance of materials in molten aluminum and its alloy were summarized. According to our recent progress referred to kinds of materials, especially a TiA13/Ti3A1C2/A1203 composite, the ceramics/metal composites with a co-continuous structure will be of great advantage in the field of corrosion-wear environment of molten aluminum and its alloys.展开更多
The microstructure evolution, mechanical and corrosion properties of Al-11Si-2Cu-0.8Zn die cast alloy treated with Bi, Sb and Sr additions were investigated. The results of mechanical testing showed that all additions...The microstructure evolution, mechanical and corrosion properties of Al-11Si-2Cu-0.8Zn die cast alloy treated with Bi, Sb and Sr additions were investigated. The results of mechanical testing showed that all additions increased impact toughness, ultimate tensile strength, and elongation of the alloy as a result of change in eutectic Si morphology. The analysis of fracture surfaces revealed that with addition of Sr and to lesser extent Bi and Sb, the alloy exhibited a predominantly ductile fracture rather than quasi-cleavage brittle fracture. Moreover, with the additions of Sr, Bi and Sb, the quality index increased to 164.7 MPa, 156.3 MPa and 152.6 MPa respectively from 102 MPa for the base alloy. Polarization corrosion tests conducted in sodium chloride solution showed that the corrosion potential shifted to more negative values with additions of Sb, Bi and Sr, respectively. Corrosion immersion tests also revealed that the element additions have a detrimental effect on the corrosion rate of alloys, due to the increase of boundaries between the Al and eutectic Si phases.展开更多
基金Project(51271080) supported by the National Natural Science Foundation of China
文摘The failure caused by the corrosion-wear of molten aluminum and its alloys is one of the main problems in aluminum industry. In this work, the resistance behavior of various materials, including Fe-based alloys, ceramics and corresponding high apparatus of corrosion-wear in molten aluminum and its alloys, were reviewed. The synergistic effect of corrosion and wear was discussed based on corrosion and wear mechanics. The effects of dynamic agitation due to rotating of friction pairs, physical property of liquid metal and size of grain etc., on the corrosion-wear resistance performance were investigated. In addition, the characteristics of corrosion-wear resistance performance of materials in molten aluminum and its alloy were summarized. According to our recent progress referred to kinds of materials, especially a TiA13/Ti3A1C2/A1203 composite, the ceramics/metal composites with a co-continuous structure will be of great advantage in the field of corrosion-wear environment of molten aluminum and its alloys.
文摘The microstructure evolution, mechanical and corrosion properties of Al-11Si-2Cu-0.8Zn die cast alloy treated with Bi, Sb and Sr additions were investigated. The results of mechanical testing showed that all additions increased impact toughness, ultimate tensile strength, and elongation of the alloy as a result of change in eutectic Si morphology. The analysis of fracture surfaces revealed that with addition of Sr and to lesser extent Bi and Sb, the alloy exhibited a predominantly ductile fracture rather than quasi-cleavage brittle fracture. Moreover, with the additions of Sr, Bi and Sb, the quality index increased to 164.7 MPa, 156.3 MPa and 152.6 MPa respectively from 102 MPa for the base alloy. Polarization corrosion tests conducted in sodium chloride solution showed that the corrosion potential shifted to more negative values with additions of Sb, Bi and Sr, respectively. Corrosion immersion tests also revealed that the element additions have a detrimental effect on the corrosion rate of alloys, due to the increase of boundaries between the Al and eutectic Si phases.