A high-purity Ti-48Al-2Nb-2Cr alloy powder with an oxygen content as low as 0.0572 wt.%and a particle size of<150μm was produced from a mixture of TiO_(2),Al_(2)O_(3),Nb_(2)O_(5),and Cr_(2)O_(3)powders through red...A high-purity Ti-48Al-2Nb-2Cr alloy powder with an oxygen content as low as 0.0572 wt.%and a particle size of<150μm was produced from a mixture of TiO_(2),Al_(2)O_(3),Nb_(2)O_(5),and Cr_(2)O_(3)powders through reduction with magnesium and deoxidation with calcium.The phase and composition of the products were analyzed.The final product mainly includedγ-TiAl and minorα_(2)-Ti_(3)Al phases,and Ti,Al,Cr,and Nb were homogenously distributed in the powder with a mole ratio of 49.73:43.51:2.05:1.98.The reduction and deoxidation mechanisms were investigated by thermodynamic modeling using the HSC Chemistry software and Pandat software based on the Ti alloy database.展开更多
基金financially supported by the National Natural Science Foundation of China(No.52004342)Innovation-driven Project of Central South University,China(No.502501015)the Natural Science Fund for Distinguished Young Scholar of Hunan Province,China(No.2019JJ20031)。
文摘A high-purity Ti-48Al-2Nb-2Cr alloy powder with an oxygen content as low as 0.0572 wt.%and a particle size of<150μm was produced from a mixture of TiO_(2),Al_(2)O_(3),Nb_(2)O_(5),and Cr_(2)O_(3)powders through reduction with magnesium and deoxidation with calcium.The phase and composition of the products were analyzed.The final product mainly includedγ-TiAl and minorα_(2)-Ti_(3)Al phases,and Ti,Al,Cr,and Nb were homogenously distributed in the powder with a mole ratio of 49.73:43.51:2.05:1.98.The reduction and deoxidation mechanisms were investigated by thermodynamic modeling using the HSC Chemistry software and Pandat software based on the Ti alloy database.