Two mixing techniques,the immersion method and the vortex method,were adopted in the production of Al-3%B master alloys since the generally used production route involving the direct addition of KBF4 salt to molten al...Two mixing techniques,the immersion method and the vortex method,were adopted in the production of Al-3%B master alloys since the generally used production route involving the direct addition of KBF4 salt to molten aluminum has several drawbacks.The experimental results demonstrate that the Al-B master alloys produced by the immersion method show a microstructure characterized by the appearances of AlB12 phase and many agglomerations of boride particles,while the Al-B master alloy produced by the vortex method exhibits a well dispersed microstructure of AlB2 particles in the matrix.The distinct microstructure features result from the differences in the stirring speed during the salt additions and the average size of the salt droplets achieved by the salt additions.展开更多
基金The project was supported by the North China University of Water Conservancy and Electric Power High-level Experts Scientific Research Foundation,China(201114)Henan Provincial Education Department,China(14A150024)+4 种基金Jiangxi Provincial Education Department,China(GJJ14230)Sponsored Program for Cultivating Youths of Outstanding Ability in Jiangxi Normal University,ChinaYoung Scientist Foundation of Jiangxi Province,China(20133BCB23011)"Gan-Po Talent 555"Project of Jiangxi Province,ChinaNational Natural Science Foundation of China(21103074)~~
基金Project(u0837601)supported by the National Natural Science Foundation of China
文摘Two mixing techniques,the immersion method and the vortex method,were adopted in the production of Al-3%B master alloys since the generally used production route involving the direct addition of KBF4 salt to molten aluminum has several drawbacks.The experimental results demonstrate that the Al-B master alloys produced by the immersion method show a microstructure characterized by the appearances of AlB12 phase and many agglomerations of boride particles,while the Al-B master alloy produced by the vortex method exhibits a well dispersed microstructure of AlB2 particles in the matrix.The distinct microstructure features result from the differences in the stirring speed during the salt additions and the average size of the salt droplets achieved by the salt additions.