To study the distribution law and random characteristics of casting defects in steel castings,24 civil engineering structural cast steel joints were divided into two groups:simple cast steel joints and complex cast st...To study the distribution law and random characteristics of casting defects in steel castings,24 civil engineering structural cast steel joints were divided into two groups:simple cast steel joints and complex cast steel joints.Three kinds of nondestructive testing(NDT)methods,namely,visual,magnetic particle,and ultrasonic inspections,were used to detect the macroscopic defects in joints.The NDT results were then statistically analyzed.The results show that the unfused core support is a common defect of complex cast steel joints,and the defect can be seen visually,so excavation and repair welding should be carried out before castings leave factories.Casting cracks are extremely likely to occur in the intersection area of tubes,which is called the ultrasonic inspection blind zone.The occurrence probability of gas pores on simple cast steel joints is the largest,and the occurrence probability of core support incomplete fusions on complex cast steel joints is the largest.However,when cast steel joints are counted as a whole sample,the occurrence probability of gas pores is larger than that of core support incomplete fusions.Therefore,it is the most common defect in cast steel joints.展开更多
基金The National Key R&D Program of China(No.2017YFC0805100)the National Natural Science Foundation of China(No.51578137)+1 种基金the Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutionsthe Open Research Fund Program of Jiangsu Key Laboratory of Engineering Mechanics。
文摘To study the distribution law and random characteristics of casting defects in steel castings,24 civil engineering structural cast steel joints were divided into two groups:simple cast steel joints and complex cast steel joints.Three kinds of nondestructive testing(NDT)methods,namely,visual,magnetic particle,and ultrasonic inspections,were used to detect the macroscopic defects in joints.The NDT results were then statistically analyzed.The results show that the unfused core support is a common defect of complex cast steel joints,and the defect can be seen visually,so excavation and repair welding should be carried out before castings leave factories.Casting cracks are extremely likely to occur in the intersection area of tubes,which is called the ultrasonic inspection blind zone.The occurrence probability of gas pores on simple cast steel joints is the largest,and the occurrence probability of core support incomplete fusions on complex cast steel joints is the largest.However,when cast steel joints are counted as a whole sample,the occurrence probability of gas pores is larger than that of core support incomplete fusions.Therefore,it is the most common defect in cast steel joints.