电解铝液铸轧生产3102铝合金箔坯料工艺研究

用电解铝液做原料生产3102铝合金铸轧坯料,从熔炼、精炼、在线净化、晶粒细化、铸轧等各个生产环节入手,对影响铸轧板坯组织均匀性、晶粒度的工艺参数进行了研究,重点研究了铸轧速度和铸轧板厚度对3102铝合金箔材铸轧坯料的杯突值的影响。

Simulation of microstructures in solidification of aluminum twin-roll casting

Based on the research on the solidification of twin-roll continuous casting aluminum thin strip, the analytical model of heterogeneous nucleation, the growth kinetics of tip （KGT） and columnar dendrite transformation to equiaxed dendrite （CET） of twin-roll continuous casting aluminum thin strip solidification was established by means of the principle of metal solidification and modem computer emulational technology. Meantime, based on the cellular automaton, the emulational model of twin-roll continuous casting aluminum thin strip, solidification was established. The foundation for the emulational simulation of twin-roll casting thin strip solidification structure was laid. Meanwhile, the mathematical simulation feasibility was confirmed by using the solidification process of twin-roll continuous casting aluminum thin strip.

Asymmetric cast-rolling of 1050 aluminum alloy strip under multi-energy field

Technological parameters of asymmetric cast-rolling under multi-energy field were investigated on horizontal twin roll caster（d400 mm×500 mm）, and their effects on structures and properties of 1050 strips were analyzed by comparing with traditional cast-rolling. Results show that when length of cast-rolling area is 70 mm, melt temperature of head box is 670 °C, cast rolling speed is 1.3 m/min, exciting current is 10 A, center frequency is（13±1） Hz, ultrasonic power is 200 W and ultrasonic frequency is（20±0.2） kHz, the 1050 strip with the best microstructure can be prepared successfully; its center segregated layer disappears; the average grain size is reduced by about 40%; the crystal grains are distributed evenly; micro segregation decreases obviously; the precipitated phases are distributed along the grain boundaries evenly; and the tensile strength, yield strength, elongation and micro-hardness of cast-rolled strip are improved by 22.6%, 23.66%, 38.75% and 9.90%, respectively.

Al-Mn系铝合金箔拉伸试样星点纹路产生的原因分析

对不同回复退火工艺的Al-Mn系铝合金箔在经过拉伸试验后表面产生的星点纹路进行了对比,并对不同程度的星点纹路进行了EBSD分析。结果表明,星点纹路是因材料经过退火后其旋转立方织构及立方织构比例增加所造成的。铸轧晶粒组织越粗大,退火的温度越高、时间越长,拉伸后的试样表面更易出现星点纹路现象。通过铸轧晶粒组织的细化、退火工艺的调整可避免出现拉伸试样星点纹路的现象。

Microstructure evolution and mechanical properties of Cu-0.36Be-0.46Co alloy fabricated by heating-cooling combined mold horizontal continuous casting during cold rolling

Cu-0.36 wt.%Be-0.46 wt.%Co alloy plate with 300 mm in width and 10 mm in thickness prepared by heating-cooling combined mold(HCCM) horizontal continuous casting was cold rolled. Microstructure evolution and mechanical properties of the alloy as well as its deformation mechanism were investigated. The results showed that the as-cast alloy plate had columnar grains along the length direction, good surface quality and elongation of 35%, which was directly large-reduction cold rolled without surface treatment, and the accumulative cold rolling reduction reached 98%. When the reduction was small(20%), numerous dislocations and dislocation cells formed, and the deformation mechanism was dislocation slip. When the reduction was 40%, deformation twins appeared, and interactions between twins and dislocation cells induced strip-like dislocation cells. When the reduction exceeded 60%, shear bands formed and apparent crystal rotation in the micro-region happened. Further increasing the reduction, the amount of the shear bands rose and they interacted with each other, which refined the grains apparently. The tensile strength and hardness increased from 353 MPa and HV 119 of the as-cast alloy to 625 MPa and HV 208 with 95% reduction, respectively, and the elongation reduced from 35% to 7.6%. A process of HCCM horizontal continuous casting-cold rolling can work as a novel compact method to fabricate Cu-Be alloy sheet.

Microstructure characteristics of Ti-43Al alloy during twin-roll strip casting and heat treatment

To shorten the fabrication process of difficult-to-form TiAl sheets, twin-roll strip casting and microstructural control were investigated in Ti-43Al alloy. A crack-free sheet with dimensions of 1000 mm × 110 mm × 2 mm was obtained. The microstructure of stip casting sheets and heat treatments was systematically studied. The macrostructure consisted of columnar crystals extending inward and centrally located equiaxed crystals with severe Al segregation were observed along the thickness direction, due to the symmetrical solidification process and decreasing cooling rates. The strip casting alloy was characterized by fine duplex microstructure with a grain spacing of 20-30 μm and a lamellar spacing of 10-20 nm. Furthermore, multiple microstructures of near gamma, nearly lamellar and fully lamellar were obtained through heat treatment process with significantly improved homogeneity of the microstructure.

Effect of rolling temperature on microstructure and texture of twin roll cast ZK60 magnesium alloy

Twin roll cast ZK60 alloy strip/sheet with final thickness of 0.5 mm was prepared, and effect of rolling temperature on microstructure and texture development was investigated using OM and XRD technique, microstructure and texture were measured on specimens subjected to rolling experiment at different rolling temperature, and macrotexture was also evaluated by X-ray diffraction method. In addition, the （1010）and （0002） pole figures were measured, and the tensile test was performed to reveal the influence of rolling temperature on mechanical properties. The results show that the microstrucmre of ZK60 alloy sheet consisted of fibrous structure with elongated grains, and shear bands along the rolling direction after warm rolling. Dynamic recrystallization could be found during the warm rolling process at rolling temperature 350℃ and above. And many fine recrystallized grain could be observed in the shear bands area. It is a little difficult to see the recrystallized grain in the sheet warm rolled at 300℃ because of higher density of shear bands. The warm rolled ZK60 alloy sheet exhibited strong （0002） pole texture, the intensity of （0002） pole figure decreases with the increasing of rolling temperature and the basal pole tilted slightly to the transverse direction after warm rolling.

Influence of roll speed difference on microstructure, texture and mechanical properties of 7075 aluminum plates produced via combined continuous casting and rolling process

The influences of the dissimilarity in the roll speeds on the microstructure, texture and mechanical properties of 7075 aluminum plates produced via combined continuous casting and rolling(CCCR) process were investigated. Several experiments were conducted with three different upper/lower roll rotational speed ratios(ω/ω0, ω is the upper roll rotational speed and ω0 is the lower roll rotational speed), namely 1:1, 1:1.2 and 1:1.4. It was found that the greatest dissimilarity in the roll speed(ω/ω0=1:1.4) improved the yield strength and ultimate tensile strength of 7075 Al plate in the rolling direction by 41.5% and 21.9%, respectively. Moreover, at a roll speed ratio of ω/ω0=1:1.4, the average grain size was decreased by 36% whereas the mean hardness of the transverse cross-section of the finally rolled plate was increased by about 9.2%. Texture studies also revealed that the more the difference in the roll speeds was, the greater the isotropy and the hardness of the final product were. Nevertheless, conducting CCCR operation with different roll speeds resulted in about 6% reduction in the elongation of the deformed plate.