Influence of heat treatment on the microstructures and mechanical properties of sand-cast Mg-4Y-2Nd-1Gd-0.4Zr magnesium alloy was investigated,and the tensile fracture mechanisms of the studied alloys under different ...Influence of heat treatment on the microstructures and mechanical properties of sand-cast Mg-4Y-2Nd-1Gd-0.4Zr magnesium alloy was investigated,and the tensile fracture mechanisms of the studied alloys under different conditions were also discussed.The results show that the optimum T4 and T6 heat treatment conditions for the as-cast Mg-4Y-2Nd-1Gd-0.4Zr alloy are 525°C,8 h and（525°C,8 h）＋（225°C,16 h）,respectively,with regard to the microstructure observation,DSC heating curve and mechanical properties.The hardness,yield strength,ultimate tensile strength and elongation of the Mg-4Y-2Nd-1Gd-0.4Zr alloy treated by optimum T6 heat treatment are HV91,180 MPa,297 MPa and 7.4%,respectively.Moreover,the Mg-4Y-2Nd-1Gd-0.4Zr alloys under different heat treatment conditions exhibit different tensile fracture modes.展开更多
The effect of complex melt-refining treatment （melt flux incorporating with rotating gas bubble stirring） on microstructure and mechanical behavior of the sand-cast Mg-10Gd-3Y-0.5Zr alloy was investigated. In additi...The effect of complex melt-refining treatment （melt flux incorporating with rotating gas bubble stirring） on microstructure and mechanical behavior of the sand-cast Mg-10Gd-3Y-0.5Zr alloy was investigated. In addition, the melt purifying mechanism of the complex melt-refining treatment for the sand-cast alloy was discussed systematically. The results show that the new melt-refining method can significantly improve melt quality and mechanical behavior of the tested alloy, i.e., compared to the reference unpttdfied alloy, the volume fraction of inclusions decreased from 0.47% to 0.28%, the ultimate tensile strength and elongation for T6-treated alloy increased from 245 MPa and 0.7% to 312 MPa and 4.5%, respectively. Especially, combining 1% flux with rotating gas bubble stirring can get even better purifying effectiveness than conventional sole 2% flux purification; the use of melt flux decreased by 50% and significantly reduced environmental pollution.展开更多
This study focused on modifying heat treatment schemes to enhance the mechanical properties of sand cast Al−2Li−2Cu−0.5Mg−0.2Sc−0.2Zr alloy.Different three-stage solution treatment schemes((460℃,32 h)+(520℃,24 h)+(5...This study focused on modifying heat treatment schemes to enhance the mechanical properties of sand cast Al−2Li−2Cu−0.5Mg−0.2Sc−0.2Zr alloy.Different three-stage solution treatment schemes((460℃,32 h)+(520℃,24 h)+(530/540/550℃,4/12/24/32 h))and aging temperatures(125,175,225℃)were designed for comparison.The microstructure evolutions were analyzed by optical microscopy(OM),scanning electron microscopy(SEM)and transmission electron microscopy(TEM).The results showed that the three-stage solution treatment of(460℃,32 h)+(520℃,24 h)+(530℃,12 h)could dissolve most of the secondary phases.The TEM results illustrated that fineδ'(Al_(3)Li)particles were homogeneously distributed in the matrix after aging at 175℃for 8 h,accompanied by a small amount of lath-shaped S′(Al_(2)CuMg)and plate-like T_(1)(Al_(2)CuLi)phases.The best comprehensive properties of yield strength of 376 MPa,ultimate tensile strength of 458 MPa and elongation of 4.1%were obtained by the optimal heat treatment scheme((460℃,32 h)+(520℃,24 h)+(530℃,12 h)+(175℃,8 h)).展开更多
基金Project(0502)supported by the Aerospace Science and Technology Innovation Fund of China Aerospace Science and Technology CorporationProject(2007CB613701)supported by the National Basic Research Program of ChinaProject(2009AA033501)supported by the National High-tech Research and Development Program of China
文摘Influence of heat treatment on the microstructures and mechanical properties of sand-cast Mg-4Y-2Nd-1Gd-0.4Zr magnesium alloy was investigated,and the tensile fracture mechanisms of the studied alloys under different conditions were also discussed.The results show that the optimum T4 and T6 heat treatment conditions for the as-cast Mg-4Y-2Nd-1Gd-0.4Zr alloy are 525°C,8 h and（525°C,8 h）＋（225°C,16 h）,respectively,with regard to the microstructure observation,DSC heating curve and mechanical properties.The hardness,yield strength,ultimate tensile strength and elongation of the Mg-4Y-2Nd-1Gd-0.4Zr alloy treated by optimum T6 heat treatment are HV91,180 MPa,297 MPa and 7.4%,respectively.Moreover,the Mg-4Y-2Nd-1Gd-0.4Zr alloys under different heat treatment conditions exhibit different tensile fracture modes.
基金Project(USCAST2012-15) supported by the SAST-SJTU Joint Research Centre of Advanced Aerospace TechnologyProject(B type,14QB1403200) supported by the Shanghai Rising-Star Program,China+1 种基金Projects(20120073120011,20130073110052) supported by the Research Fund for the Doctoral Program of Higher Education of ChinaProject(IPP9084) supported by IPP program in SJTU,China
文摘The effect of complex melt-refining treatment （melt flux incorporating with rotating gas bubble stirring） on microstructure and mechanical behavior of the sand-cast Mg-10Gd-3Y-0.5Zr alloy was investigated. In addition, the melt purifying mechanism of the complex melt-refining treatment for the sand-cast alloy was discussed systematically. The results show that the new melt-refining method can significantly improve melt quality and mechanical behavior of the tested alloy, i.e., compared to the reference unpttdfied alloy, the volume fraction of inclusions decreased from 0.47% to 0.28%, the ultimate tensile strength and elongation for T6-treated alloy increased from 245 MPa and 0.7% to 312 MPa and 4.5%, respectively. Especially, combining 1% flux with rotating gas bubble stirring can get even better purifying effectiveness than conventional sole 2% flux purification; the use of melt flux decreased by 50% and significantly reduced environmental pollution.
基金the National Natural Science Foundation of China(Nos.51871148,51821001)the United Fund of National Department of Education and Equipment Development,China(No.6141A02033245).
文摘This study focused on modifying heat treatment schemes to enhance the mechanical properties of sand cast Al−2Li−2Cu−0.5Mg−0.2Sc−0.2Zr alloy.Different three-stage solution treatment schemes((460℃,32 h)+(520℃,24 h)+(530/540/550℃,4/12/24/32 h))and aging temperatures(125,175,225℃)were designed for comparison.The microstructure evolutions were analyzed by optical microscopy(OM),scanning electron microscopy(SEM)and transmission electron microscopy(TEM).The results showed that the three-stage solution treatment of(460℃,32 h)+(520℃,24 h)+(530℃,12 h)could dissolve most of the secondary phases.The TEM results illustrated that fineδ'(Al_(3)Li)particles were homogeneously distributed in the matrix after aging at 175℃for 8 h,accompanied by a small amount of lath-shaped S′(Al_(2)CuMg)and plate-like T_(1)(Al_(2)CuLi)phases.The best comprehensive properties of yield strength of 376 MPa,ultimate tensile strength of 458 MPa and elongation of 4.1%were obtained by the optimal heat treatment scheme((460℃,32 h)+(520℃,24 h)+(530℃,12 h)+(175℃,8 h)).