Stir casting was used to produce AA6061/15%TiC （mass fraction） aluminum matrix composites （AMCs）. An empirical relationship was developed to predict the effect of stir casting parameters on the ultimate tensile ...Stir casting was used to produce AA6061/15%TiC （mass fraction） aluminum matrix composites （AMCs）. An empirical relationship was developed to predict the effect of stir casting parameters on the ultimate tensile strength （UTS） of AA6061/TiC AMCs. A central composite rotatable design consisting of four factors and five levels was used to minimize the number of experiments, i.e., castings. The factors considered were stirring speed, stirring time, blade angle and casting temperature. The effect of those factors on the UTS of AA6061/TiC AMCs was derived using the developed empirical relationship and elucidated using microstructural characterization. Each factor significantly influenced the UTS. The variation in the UTS was attributed to porosity content, cluster formation, segregation of TiC particles at the grain boundaries and homogenous distribution in the aluminum matrix.展开更多
Production of A6063/SiC-B4C hybrid composite using vacuum assisted block mould investment casting was investigated. Firstly,SiC-B4C hybrid preforms were fabricated in cylindrical shape.The preferred mean particle size...Production of A6063/SiC-B4C hybrid composite using vacuum assisted block mould investment casting was investigated. Firstly,SiC-B4C hybrid preforms were fabricated in cylindrical shape.The preferred mean particle size of the SiC and B4C powders were 60μm and 55μm respectively.In early experiments,single powder ratio of 85%SiC and 15%B4C was selected to produce the tough preforms.Subsequently,the preforms were placed into the cylindrical shape gypsum bonded block investment moulds and A6063 alloy was infiltrated into the preforms using vacuum assisted（-10 5 Pa）casting machine.Porosity fraction of preforms was determined using Archimedes’test.The fabricated cast specimens were characterized using hardness tests,image analysis and SEM observations and EDX analysis.The result indicates that,by the vacuum assisted block mould investment casting technique,the infiltration of the preforms by molten metal was successfully realized.展开更多
Rice husk ash(RHA) is a potential particulate reinforcement to produce aluminum matrix composites(AMCs)economically.Compocasting method was applied to produce aluminum alloy AA6061 reinforced with various amounts(0,2%...Rice husk ash(RHA) is a potential particulate reinforcement to produce aluminum matrix composites(AMCs)economically.Compocasting method was applied to produce aluminum alloy AA6061 reinforced with various amounts(0,2%,4%,6%and 8%,mass fraction) of RHA particles.The prepared composites were characterized using X-ray diffraction and scanning electron microscopy.X-ray diffraction patterns of AA6061/RHA AMCs revealed the presence of RHA particles without the formation of any other intermetallic compounds.The scanning electron micrographs showed a homogeneous distribution of RHA particles all over the aluminum matrix.Intragranular distribution of RHA particles was observed.Further,RHA particles were bonded well with the aluminum matrix and a clear interface existed.The reinforcement of RHA particles enhanced the microhardness and ultimate tensile strength(UTS) of the AMCs.The tensile behavior is correlated to the microstructure of the AMCs.展开更多
The influences of SiC content on the microstructure, porosity, hardness and wear resistance of A356？SiCp composites processed via two different methods of compocasting and vibrating cooling slope （VCS） were compare...The influences of SiC content on the microstructure, porosity, hardness and wear resistance of A356？SiCp composites processed via two different methods of compocasting and vibrating cooling slope （VCS） were compared with each other. In the as-cast condition, the matrix of VCS and compocast processed composites exhibited globular and dendritric structures, respectively. While a more uniform distribution of SiC particulates in the matrix alloy as well as higher hardness values were obtained for the VCS processed samples, the composites produced via compocasting exhibited less porosity. The increased SiC content （up to 20% in volume fraction） resulted in a more uniform distribution of SiC particles within the matrix alloy and improved wear resistance for both the composite series. However, for the VCS processed composites, the increased SiC content, resulted in the decreased size and shape factor of globules as well as better tribological properties when compared with compocast composites. It was concluded that the improved properties of the VCS processed composites when compared with their compocast counterparts was a consequence of a more uniform distribution of SiC particulates in the matrix alloy as well as the globular microstructure generated during the VCS process.展开更多
文摘Stir casting was used to produce AA6061/15%TiC （mass fraction） aluminum matrix composites （AMCs）. An empirical relationship was developed to predict the effect of stir casting parameters on the ultimate tensile strength （UTS） of AA6061/TiC AMCs. A central composite rotatable design consisting of four factors and five levels was used to minimize the number of experiments, i.e., castings. The factors considered were stirring speed, stirring time, blade angle and casting temperature. The effect of those factors on the UTS of AA6061/TiC AMCs was derived using the developed empirical relationship and elucidated using microstructural characterization. Each factor significantly influenced the UTS. The variation in the UTS was attributed to porosity content, cluster formation, segregation of TiC particles at the grain boundaries and homogenous distribution in the aluminum matrix.
基金Yildiz Technical University and Balkan Center for Advanced Casting Technologies (BCACT) for their financial support
文摘Production of A6063/SiC-B4C hybrid composite using vacuum assisted block mould investment casting was investigated. Firstly,SiC-B4C hybrid preforms were fabricated in cylindrical shape.The preferred mean particle size of the SiC and B4C powders were 60μm and 55μm respectively.In early experiments,single powder ratio of 85%SiC and 15%B4C was selected to produce the tough preforms.Subsequently,the preforms were placed into the cylindrical shape gypsum bonded block investment moulds and A6063 alloy was infiltrated into the preforms using vacuum assisted（-10 5 Pa）casting machine.Porosity fraction of preforms was determined using Archimedes’test.The fabricated cast specimens were characterized using hardness tests,image analysis and SEM observations and EDX analysis.The result indicates that,by the vacuum assisted block mould investment casting technique,the infiltration of the preforms by molten metal was successfully realized.
文摘Rice husk ash(RHA) is a potential particulate reinforcement to produce aluminum matrix composites(AMCs)economically.Compocasting method was applied to produce aluminum alloy AA6061 reinforced with various amounts(0,2%,4%,6%and 8%,mass fraction) of RHA particles.The prepared composites were characterized using X-ray diffraction and scanning electron microscopy.X-ray diffraction patterns of AA6061/RHA AMCs revealed the presence of RHA particles without the formation of any other intermetallic compounds.The scanning electron micrographs showed a homogeneous distribution of RHA particles all over the aluminum matrix.Intragranular distribution of RHA particles was observed.Further,RHA particles were bonded well with the aluminum matrix and a clear interface existed.The reinforcement of RHA particles enhanced the microhardness and ultimate tensile strength(UTS) of the AMCs.The tensile behavior is correlated to the microstructure of the AMCs.
文摘The influences of SiC content on the microstructure, porosity, hardness and wear resistance of A356？SiCp composites processed via two different methods of compocasting and vibrating cooling slope （VCS） were compared with each other. In the as-cast condition, the matrix of VCS and compocast processed composites exhibited globular and dendritric structures, respectively. While a more uniform distribution of SiC particulates in the matrix alloy as well as higher hardness values were obtained for the VCS processed samples, the composites produced via compocasting exhibited less porosity. The increased SiC content （up to 20% in volume fraction） resulted in a more uniform distribution of SiC particles within the matrix alloy and improved wear resistance for both the composite series. However, for the VCS processed composites, the increased SiC content, resulted in the decreased size and shape factor of globules as well as better tribological properties when compared with compocast composites. It was concluded that the improved properties of the VCS processed composites when compared with their compocast counterparts was a consequence of a more uniform distribution of SiC particulates in the matrix alloy as well as the globular microstructure generated during the VCS process.