锐钛相虫蛀状介孔二氧化钛的表征(英文)

Mesoporous titania with anatase crystal framework was generated directly by ho mogeneous precipitation method using titanium sulfate (Ti(SO4)2) mixed with urea as precursor and octadecylamine (C18H37NH2) as structure-directing agent. The as-synthesized titania has been characterized by XRD, TEM, FT-IR and N2 adsorp tion-desorption isotherm. The results displayed a wormhole-like anatase mesost ructure lacking of long-range order with BET surface area of 35m2·g-1, pore v olume of 0.1cm3·g-1 and broader pore size distribution including microporous a nd mesoporous domain. C18H37NH2 incorporated into the as-synthesized oxide.

云母钛珠光颜料的液相合成技术 Ⅱ云母钛前驱体的热处理过程研究

以ＴＧ－ＥＧＡ等分析检测手段探明了云母铁颜料包膜层的组成，并对其热处理工艺作了系统的研究，得到了较佳的热处理工艺。同时以ＤＴＡ、ＳＥＭ、ＸＲＤ技术研究了膜层ＴｉＯ＿２粒子在煅烧过程中的形态及物相结构变化过程，结果表明，膜层的水合ＴｉＯ＿２粒子在热处理过程中随着温度的升高逐步晶化，并由锐钛相向金红石相转化。实验制得了金红石相含量较高的云母钛珠光颜料，具有闪亮的光泽和鲜明的色调。

pH值对TiO_2相结构的影响

TiO2作为光催化性能最好的半导体材料之一已经引起了广泛的重视。其光催化性能与相结构密切相关,本文深入分析了水解反应过程中pH值对TiO2 晶型形成的影响。研究结果表明,在弱酸性条件下可以得到锐钛相;在强酸性条件下出现了热力学的稳定相金红石相。

用双效晶种法生产金红石型钛白粉的方法

本发明是一种用双效晶种法生产金红石型钛白粉的方法。通过培制双效晶种，在钛液水解步骤时加入培制的双效晶种，该晶种首先做为偏钛酸水解粒子的晶核出现，其后又在煅烧过程中，作为金红石型相变的晶核，以达到在较低的温度下快速相变的目的。晶种中含有SnO2成分，再与Zn^2+、K^+相配合，SnO2占TiO2含量的4％～7％，使TiO2由锐钛相低温快速变成金红石相，解决了硫酸法生产金红石型钛白粉相变难的问题。本发明降低了煅烧温度，降低了成本，提高了产量，可使原有的厂家既能生产锐钛型钛白粉又能生产金红石型钛白粉，有利于老企业的技术改造和提升我国钛白工业的技术水平，增强国际竞争力。

纳米TiO_2的高分子“锚定位”包覆

通过多组分溶液的原位合成方法，成功地制备了ＴｉＯ２／聚苯乙烯－马来酸酐（ＰＳＭＡ）纳米复合材料．红外普图（ＩＲ）分析了这种材料的化学构成，证明纳米ＴｉＯ２与高分子是以共价键的形式存在．随着反应条件的改变，透射电镜（ＴＥＭ）观察到了纳米ＴｉＯ２在复合物中有规律的形貌变化．综合实验结果，提出高分子“锚定位”包覆的作用模型，形象地说明了这种材料以三维网络、纳米晶ＴｉＯ２微相分离的形式存在，同时ＴｉＯ２颗粒的团聚几率在相当大程度上得以降低．结合Ｘ射线衍射，还确定出了复合物中纳米ＴｉＯ２的锐钛矿型结构．

分子自组装制备的掺杂WO_3的TiO_2光催化薄膜的表征(英文)

利用分子自组装技术在载波片上制备了锐钛相TiO2及WO3掺杂的TiO2薄膜。利用原子力显微镜(AFM)和UV-VIS-NIR分光光度计对薄膜进行了表征。利用对罗丹明B的降解评价了所制备薄膜的光催化活性。结果表明:当W/Ti=2at%时,TiO2薄膜的光催化活性得到提高。