Elemental titanium(Ti)and nickel(Ni)powders were consolidated by spark plasma sintering(SPS)to fabricate Ti-51%Ni(mole fraction)shape-memory alloys(SMAs).The objective of this study is to enhance the superelasticity o...Elemental titanium(Ti)and nickel(Ni)powders were consolidated by spark plasma sintering(SPS)to fabricate Ti-51%Ni(mole fraction)shape-memory alloys(SMAs).The objective of this study is to enhance the superelasticity of SPS produced Ti-Ni alloy using free forging as a secondary process.Products from two processes(with and without free forging)were compared in terms of microstructure,transformation temperature and superelasticity.The results showed that,free forging effectively improved the tensile and shape-memory properties.Ductility increased from 6.8%to 9.2%after forging.The maximum strain during superelasticity increased from 5%to 7.5%and the strain recovery rate increased from 72%to 92%.The microstructure of produced Ti-51%Ni SMA consists of the cubic austenite(B2)matrix,monoclinic martensite(B19′),secondary phases(Ti3Ni4,Ti2Ni and TiNi3)and oxides(Ti4Ni2O and Ti3O5).There was a shift towards higher temperatures in the martensitic transformation of free forged specimen(aged at 500°C)due to the decrease in Ni content of B2 matrix.This is related to the presence of Ti3Ni4 precipitates,which were observed using transmission electron microscope(TEM).In conclusion,free forging could improve superelasticity and mechanical properties of Ti-51%Ni SMA.展开更多
The extraction of potassium from a tablet mixture of K-feldspar ore and CaSO4by roasting was studied with a focus on the effects of the decomposition behavior of CaSO4on the potassium extraction process.The roasted sl...The extraction of potassium from a tablet mixture of K-feldspar ore and CaSO4by roasting was studied with a focus on the effects of the decomposition behavior of CaSO4on the potassium extraction process.The roasted slags were characterized by X-ray diffraction（XRD）,scanning electron microscopy（SEM）,energy-dispersive X-ray spectroscopy,and thermogravimetric（TG）analysis.The XRD analysis revealed that hydrosoluble mischcrystal K2Ca2（SO4）3was obtained by ion exchange of Ca^2＋ in CaSO4 and K^＋ in KAlSi3O8.Meanwhile,the intermediate product,SiO2,separated from KAl Si3O8and reacted with CaSO4to decompose CaSO4.The SEM results showed that some blowholes emerged on the surface of the CaSO4particles when they reacted with SiO2at 1200℃,which indicates that SO2and O2gases were released from CaSO4.The TG curves displayed that pure CaSO4could not be decomposed below 1200℃,while the mixture of K-feldspar ore and CaSO4began to lose weight at 1000℃.The extraction rate of potassium and decomposition rate of CaSO4were 62%and 44%,respectively,at a mass ratio of CaSO4to K-feldspar ore of 3：1,temperature of 1200℃,tablet-forming pressure of6 MPa,and roasting time of 2 h.The decomposition of CaSO4reduced the potassium extraction rate;therefore,the required amount of CaSO4was more than the theoretical amount.However,excess CaSO4was also undesirable for the potassium extraction reaction because a massive amount of SO2and O2gas were derived from the decomposition of CaSO4,which provided poor contact between the reactants.The SO2released from CaSO4decomposition can be effectively recycled.展开更多
About five years ago,Liu Chun’er,a Beijingbased office professional,hated her own image in the mirror.＂Fat-laden waist and stocky legs obscured my curve,＂she said.She did not even have the courage to wear skirts.No...About five years ago,Liu Chun’er,a Beijingbased office professional,hated her own image in the mirror.＂Fat-laden waist and stocky legs obscured my curve,＂she said.She did not even have the courage to wear skirts.Now she loves to don skirts,snap pictures of herself and share them with her friends via social media platforms.展开更多
基金the Ministry of Higher Education of Malaysia for the Malaysian International Scholarship and research funding under FRGS vote No. R.J13000.7824.4F810
文摘Elemental titanium(Ti)and nickel(Ni)powders were consolidated by spark plasma sintering(SPS)to fabricate Ti-51%Ni(mole fraction)shape-memory alloys(SMAs).The objective of this study is to enhance the superelasticity of SPS produced Ti-Ni alloy using free forging as a secondary process.Products from two processes(with and without free forging)were compared in terms of microstructure,transformation temperature and superelasticity.The results showed that,free forging effectively improved the tensile and shape-memory properties.Ductility increased from 6.8%to 9.2%after forging.The maximum strain during superelasticity increased from 5%to 7.5%and the strain recovery rate increased from 72%to 92%.The microstructure of produced Ti-51%Ni SMA consists of the cubic austenite(B2)matrix,monoclinic martensite(B19′),secondary phases(Ti3Ni4,Ti2Ni and TiNi3)and oxides(Ti4Ni2O and Ti3O5).There was a shift towards higher temperatures in the martensitic transformation of free forged specimen(aged at 500°C)due to the decrease in Ni content of B2 matrix.This is related to the presence of Ti3Ni4 precipitates,which were observed using transmission electron microscope(TEM).In conclusion,free forging could improve superelasticity and mechanical properties of Ti-51%Ni SMA.
基金Supported by the National Key Research and Development Program(2016YFB0600904)Sichuan Province Science and Technology Project(2017GZ0377)Sichuan University Postdoctoral Research and Development Fund(2017SCU12017)
文摘The extraction of potassium from a tablet mixture of K-feldspar ore and CaSO4by roasting was studied with a focus on the effects of the decomposition behavior of CaSO4on the potassium extraction process.The roasted slags were characterized by X-ray diffraction（XRD）,scanning electron microscopy（SEM）,energy-dispersive X-ray spectroscopy,and thermogravimetric（TG）analysis.The XRD analysis revealed that hydrosoluble mischcrystal K2Ca2（SO4）3was obtained by ion exchange of Ca^2＋ in CaSO4 and K^＋ in KAlSi3O8.Meanwhile,the intermediate product,SiO2,separated from KAl Si3O8and reacted with CaSO4to decompose CaSO4.The SEM results showed that some blowholes emerged on the surface of the CaSO4particles when they reacted with SiO2at 1200℃,which indicates that SO2and O2gases were released from CaSO4.The TG curves displayed that pure CaSO4could not be decomposed below 1200℃,while the mixture of K-feldspar ore and CaSO4began to lose weight at 1000℃.The extraction rate of potassium and decomposition rate of CaSO4were 62%and 44%,respectively,at a mass ratio of CaSO4to K-feldspar ore of 3：1,temperature of 1200℃,tablet-forming pressure of6 MPa,and roasting time of 2 h.The decomposition of CaSO4reduced the potassium extraction rate;therefore,the required amount of CaSO4was more than the theoretical amount.However,excess CaSO4was also undesirable for the potassium extraction reaction because a massive amount of SO2and O2gas were derived from the decomposition of CaSO4,which provided poor contact between the reactants.The SO2released from CaSO4decomposition can be effectively recycled.
文摘About five years ago,Liu Chun’er,a Beijingbased office professional,hated her own image in the mirror.＂Fat-laden waist and stocky legs obscured my curve,＂she said.She did not even have the courage to wear skirts.Now she loves to don skirts,snap pictures of herself and share them with her friends via social media platforms.