Hydroforming process of a Y-shaped stainless steel tube was investigated through numerical simulation and experiments. The forming process and reasons of typical defects were analyzed with three different loading path...Hydroforming process of a Y-shaped stainless steel tube was investigated through numerical simulation and experiments. The forming process and reasons of typical defects were analyzed with three different loading paths. Thickness distribution of formed Y-shaped tube was obtained. It is shown by numerical and experimental results that the transition regions are depressed in the forming condition of low inner pressure and wrinkles occur, while fracture occurs in the forming condition of high inner pressure. After forming, the thickness in left transition fillet region is the largest, that in fight transition fillet region is thinner, and the thinnest thickness is at the top of the protrusion. The original thickness line is below the top of the protrusion. The thinning area occurs above this line, while the thickening area is below this line. The maximum thinning rate is significantly increased as the calibration pressure increases, while the maximum thickening rate remains almost unchanged.展开更多
基金the National Natural Science Foundation of China (Grant No.50525516)
文摘Hydroforming process of a Y-shaped stainless steel tube was investigated through numerical simulation and experiments. The forming process and reasons of typical defects were analyzed with three different loading paths. Thickness distribution of formed Y-shaped tube was obtained. It is shown by numerical and experimental results that the transition regions are depressed in the forming condition of low inner pressure and wrinkles occur, while fracture occurs in the forming condition of high inner pressure. After forming, the thickness in left transition fillet region is the largest, that in fight transition fillet region is thinner, and the thinnest thickness is at the top of the protrusion. The original thickness line is below the top of the protrusion. The thinning area occurs above this line, while the thickening area is below this line. The maximum thinning rate is significantly increased as the calibration pressure increases, while the maximum thickening rate remains almost unchanged.